Situmorang, Jonathan Arthur Pardamean (2019) Analisa Pengaruh Penambahan PVA Pada Room Temperature Vulcanized Silicone Rubber/ Poly(Vinyl Alcohol) Hydrogel Terhadap Sifat Biokompatibilitas dan Biodegradasi Sebagai Kandidat Material Pengganti Bantalan Tulang Belakang. Other thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
02511540000141-undergraduate_thesis.pdf Download (1MB) | Preview |
Abstract
Silikon Rubber (SR) adalah material elastomer hidrofobik yang bagian utamanya terdiri dari polysiloxane. Material ini mampu memindahkan oksigen melewati strukturnya namun tidak mampu menyerap air ke dalam struktur silikon rubber. Dan sejauh ini penelitian yang dilakukan baru menyimpulkan bahwa SR tidak toksik ke tubuh. Oleh karena itu silikon rubber perlu dicampurkan dengan material yang memiliki biokompatibilitas yang baik dan juga mampu menyerap air dengan baik. Poly(vinyl alcohol) (PVA) merupakan polimer sintetik hidrofilik yang memiliki biokompatibilitaas yang baik dan juga memiliki kemampuan untuk membentuk hidrogel dengan air. Pada penelitian ini telah disinstesis RTV Silicone Rubber/ PVA Hidrogel dan dianalisa pengaruh penambahan PVA sebanyak 10 ,20, 30, 40, dan 45 persen berat terhadap biokompatibilitas dan biodegradasi dari SR RTV/ PVA Hidrogel untuk aplikasi material pengganti bantalan tulang belakang. Pada penelitian ini material telah dikarakterisasi menggunakan SEM-EDS, MTT Assay, Uji Anti Bakteri, dan Uji Degradasi Hidrolisis. Seiringnnya penambahan PVA membuat morfologi dari material semakin berpori. Viabilitas sel material bertambah dimana viabilitas sel tertinggi terdapat pada material SR/PVA-45 sebesar 54% namun membuat kemampuan anti bakteri berkurang dimana zona inhibisi terbesar, sebesar 8.1 mm terdapat pada material SR tanpa penambahan PVA. Laju degradasi hidrolisis semakin cepat seiringnya penambahan PVA. Weight loss tertinggi terdapat pada sampel SR/PVA-45 sebesar 8.08% pada minggu ke 4 pencelupan. Prediksi lifetime dari sampel menggunakan metode regresi linier menunjukkan bahwa lifetime sampel semakin menurun seiringnya penambahan PVA. Dimana sampel SR tanpa penambahan PVA berumur 54 bulan menurun hingga 9 bulan pada sampel SR/PVA-45.
=================================================================================================================================
Silicone Rubber is an elastomeric material with polysiloxane as its main compound. This material capable of transporting oxygen throughout its structure, but unable to absorb water. Thus, silicone rubber needs to be mixed with material with good biocompatibility and also capable of absorbing water. PVA is a hydrophilic syntetic polymer that has good biocompatibility and able to become a hydrogel in water solution. In this research RTV Silicone Rubber/ PVA hydrogel has been synthesized and the effect of PVA addition as much as 10,20,30,40, and 45 percent of total weight has been analyzed for nucleus pulposus replacement. The material has been characterized using SEM-EDS, MTT Assay, Antibacterial Test, and Hydrolytic Degradasion Test. The addition of PVA create a porous structure. In addition, cell viability increased, where as the highest viability, 54%, is in SR/PVA-45 material, but reduce the antibacterial capability. Whereas the SR without PVA addition has the highest inhibition zone diameter 8.1 mm while SR/PVA-45 have no inhibiton zone. The hydrolytic degradation rate also increased with the addition of PVA. The highest weight loss occurred in SR/PVA-45 sampel which is 8.08% after four weeks of immersion. Lifetime prediction using linier regression shown that with additional PVA makes the lifetime of material decline. Where pure SR is 54 months while SR/PVA-45 is 9 months.
| Item Type: | Thesis (Other) |
|---|---|
| Additional Information: | RSMt 620.118 Sit a-1 2019 |
| Uncontrolled Keywords: | Bantalan Tulang Belakang, Silikon Rubber RTV, PVA, Biokompatibilitas, Biodegradasi |
| Subjects: | T Technology > TL Motor vehicles. Aeronautics. Astronautics > TL240.5 Composite materials T Technology > TP Chemical technology > TP1140 Polymers |
| Divisions: | Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis |
| Depositing User: | Jonathan Arthur Pardamean S. |
| Date Deposited: | 29 Nov 2023 02:47 |
| Last Modified: | 29 Nov 2023 02:47 |
| URI: | http://repository.its.ac.id/id/eprint/65139 |
Actions (login required)
 |
View Item |