Pemanfaatan Silika Microsheet Hasil Ekstraksi Lumpur Sidoarjo sebagai Partikel Penghambur Cahaya pada Fotoanoda untuk Meningkatkan Efisiensi Dye Sensitized Solar Cells (DSSC)

Rachmat, Devita (2019) Pemanfaatan Silika Microsheet Hasil Ekstraksi Lumpur Sidoarjo sebagai Partikel Penghambur Cahaya pada Fotoanoda untuk Meningkatkan Efisiensi Dye Sensitized Solar Cells (DSSC). Masters thesis, Institut Teknologi Sepuluh Nopember.

Text 02311750020001-Master_Theses.pdf Restricted to Repository staff only Download (4MB) | Request a copy

Abstract

Kinerja Dye Sensitized Solar Cell (DSSC) dapat ditingkatkan dengan menambahkan SiO2 sebagai partikel penghambur dan nanopartikel emas (Au) sebagai material plasmonik. Pada penelitian ini telah dilakukan ekstraksi silika dari lumpur Sidoarjo. Silika yang berhasil disintesis mempunyai fasa amorf. Untuk mengubah struktur amorf menjadi kristalin dilakukan proses pemanasan pada suhu 800 – 1150oC. Perubahan fasa dari amorf menjadi triklinik terjadi pada proses pemanasan ini. Hasil XRD dari silika kristalin menunjukkan bahwa struktur kristal silika adalah triklinik. Dibandingkan DSSC dengan penambahan silika amorf pada fotoanoda dasar TiO2, penambahan silika kristalin dapat meningkatkan efisiensi menjadi 0,0774 %. Sedangkan dalam bentuk struktur microsheet, Au-SiO2 struktur kristalin mempunyai efisiensi yang lebih baik yakni sebesar 0,7483 % dibandingkan dengan struktur amorf. Hasil serupa juga diperoleh untuk struktur core shell-microsheet Au@TiO2-SiO2, silika dalam fasa kristalin juga mempunyai efisiensi lebih baik dari pada amorf yaitu sebesar 1,104 %.
=============================================================================================================================
The performance of Dye Sensitized Solar Cell (DSSC) can be improved by adding SiO2 as scattering particles and gold nanoparticles (Au) as plasmonic material. Silica extraction from Sidoarjo mud has been carried out, resulting in an amorphous phase. To change the amorphous phase structure to crystalline, the heating process was carried out at temperature of 800 - 1150oC, in which the amorphous to crystalline phase takes place. XRD spectra exhibited that the crystalline structure of silica is triclinic. Compared to DSSC using addition of amorphous silica into TiO2 photoanode, the addition of crystalline silica can increase the efficiency into 0.0774%. Whereas in the form of microsheet structure, Au-SiO2 crystalline structure has a better efficiency of 0.7483% compared to the amorphous structure. Similar results were also obtained for Au@TiO2-SiO2 core shell-microsheet structure, silica in crystalline phase also has better efficiency than amorphous, i.e. 1.104%.

Item Type:	Thesis (Masters)
Uncontrolled Keywords:	DSSC, lumpur Sidoarjo, microsheet, SiO2 kristalin
Subjects:	Q Science > QC Physics T Technology > TJ Mechanical engineering and machinery > TJ810.5 Solar energy T Technology > TP Chemical technology > TP248 Nanogels. Nanoparticles.
Divisions:	Faculty of Industrial Technology > Physics Engineering > 30101-(S2) Master Thesis
Depositing User:	Devita Rachmat
Date Deposited:	21 Jul 2026 03:51
Last Modified:	21 Jul 2026 04:04
URI:	http://repository.its.ac.id/id/eprint/65297

Actions (login required)

View Item