Studi eksperimen pengaruh quenching terhadap sifat mekanis dan struktur mikro pada sambungan plat ASTM A36

Donald, - (2014) Studi eksperimen pengaruh quenching terhadap sifat mekanis dan struktur mikro pada sambungan plat ASTM A36. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 4309100070-Undergraduate_Thesis.pdf]
Preview
Text
4309100070-Undergraduate_Thesis.pdf

Download (4MB) | Preview

Abstract

Kebakaran yang terjadi pada struktur bangunan lepas pantai atau kapal dapat
membuat struktur mengalami perubahan struktur mikro dan perubahan kekuatan.
Penelitian ini bertujuan untuk mengetahui perubahan struktur mikro dan kekuatan
tarik akibat proses quenching, dengan variasi suhu, waktu pemanasan, dan media
pendingin, pada sambungan plat ASTM A36 sebagai simulasi kebakaran. Proses
pengujian quenching dilakukan menggunakan kriteria yang ada dalam ASTM A709,
pengujian tarik dilakukan menggunakan kriteria sesuai AWS D.1.1, dan analisa
struktur mikro menggunakan kriteria sesuai. Dari hasil pengujian quenching,
Penurunan kekuatan tarik terbesar adalah sambungan yang dipanaskan pada suhu
950oC dengan waktu 60 menit, dan dengan media air laut, yaitu 326.96 MPa nilai
yield strength dan 420.61 MPa nilai UTS. Penurunan ini masih dalam batas ijin
tensile strength sesuai kriteria ASTM A36. Keuletan pada sambungan plat
berbanding lurus dengan kekuatan tarik sambungan. Jika kekuatan plat menurun,
keuletan sambungan juga menurun. Penurunan kekuatan terkecil pada plat A3
disebabkan karena terbentuknya struktur austenite sisa yang membuat kekuatan
struktur menjadi berkurang. Penurunan kekuatan terbesar pada plat B4 disebabkan
karena terbentuknya struktur austenit sisa, sehingga penurunan kekuatannya lebih
besar dari A3. Hal ini disebabkan karena struktur austenit bersifat lunak namun tidak
ulet.

=======================================================================================================

Fire that occurred on the offshore structure or ship can make structure
changes of micro-structure and the change of power. This research aims to
know the change of microstructure and tensile strength due to quenching
process, with variations in temperature, the time of heating, cooling, and
media on a connection plate ASTM A36 as fire simulation. The testing process
is done using quenching existing criteria in ASTM A709, tensile testing
performed using appropriate criteria AWS D 1.1, and microstructure analysis
using appropriate criteria. Test results of quenching, decreasing the tensile
strength is the biggest connection that is heated at a temperature of 950oC
with a time of 60 minutes, and with the media sea water, 326.96 MPa yield
strength value and 420.61 value MPa UTS. This decline is still within the
bounds of appropriate tensile strength criteria permit ASTM A36. Ductility on
the connection plate is directly proportional to the tensile strength of
connection. If the strength of the ductility decreases, the connection plate is
also declining. The smallest power loss on a plate A3 due to formation of
residual austenite structure that makes the power structure to be reduced. The
biggest power loss on a plate structure formation due to B4 austenit remnants,
so his loss is larger than A3. This caused by structure austenite is malleable
but not tenacious.

Item Type: Thesis (Undergraduate)
Additional Information: RSKe 671.36 Don s
Uncontrolled Keywords: ASTM A36; Keuletan; Struktur mikro; Quenching; Tensile strength
Subjects: T Technology > TN Mining engineering. Metallurgy > TN752.I5 Steel--Heat treatment
Divisions: Faculty of Marine Technology (MARTECH) > Ocean Engineering > 38201-(S1) Undergraduate Thesis
Depositing User: - Taufiq Rahmanu
Date Deposited: 24 Jul 2019 05:33
Last Modified: 24 Jul 2019 05:33
URI: http://repository.its.ac.id/id/eprint/65379

Actions (login required)

View Item View Item