Sintesis Nanopartikel Tembaga dengan Ekstrak Daun Sentalo (Chromolaena odorata (L.)) sebagai Agen Penstabil

Handoyo, Cantika Alda Hafshah (2019) Sintesis Nanopartikel Tembaga dengan Ekstrak Daun Sentalo (Chromolaena odorata (L.)) sebagai Agen Penstabil. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 01211540000047-Undergraduate_Theses.pdf - Accepted Version Restricted to Repository staff only Download (2MB) | Request a copy

Abstract

Sintesis nanopartikel tembaga (CuNPs) dengan metode reduksi kimia telah banyak dilakukan. Pada penelitian ini, sintesis nanopartikel tembaga menggunakan agen penstabil ekstrak daun sentalo (Chromolaena odorata (L.)), dan agen pereduksi natrium sitrat telah berhasil dilakukan. Proses ekstraksi daun sentalo dilakukan dengan pelarut aqua demineralisasi pada suhu 60°C dan diaduk selama 45 menit. Variasi campuran larutan untuk sintesis nanopartikel tembaga dilakukan pada konsentrasi CuSO4 (0,05 M; 0,1 M; dan 0,15 M), konsentrasi natrium sitrat (0,15 M; 0,2 M; dan 0,25 M), dan ekstrak sentalo (10%, 20%, dan 30%). Nanopartikel tembaga yang disintesis berupa serbuk berwarna hijau kecoklatan. Nanopartikel yang telah dihasilkan selanjutnya dikarakterisasi dengan menggunakan spektroskopi FTIR, XRD, PSA, dan TEM. Pola difraktogram XRD yang diperoleh terdapat puncak pada 2θ = 43,15°; 49,75°; dan 73,91° dengan intensitas yang kecil. Nanopartikel tembaga yang terbentuk memiliki bentuk batang dengan ukuran diameter rata-rata 30 nm. Optimasi yang dilakukan menggunakan metode respon permukaan dengan desain Box-Behnken diperoleh kondisi optimum pada puncak 300 nm dengan konsentrasi CuSO4 0,12 M hingga 0,15 M, konsentrasi natrium sitrat 0,22 M hingga 0,25 M, dan persen ekstrak 22,5% hingga 30%. Pada puncak 800 nm dengan konsentrasi CuSO4 0,05 M hingga 0,06 M, konsentrasi natrium sitrat 0,15 M hingga 0,25 M, dan persen ekstrak 10% hingga 22,5%.
===================================================================================================================================
The synthesis of copper nanoparticles (CuNPs) by chemical reduction had been carried out. In this study, the synthesis of copper nanoparticles was carried out with Sentalo leaf extract (Chromolaena odorata (L.)) as stabilizing agent and sodium citrate as reducing agent. The extraction of Sentalo leaves was done using aqua demineralization as solvent. The extraction was carried out at 60 °C and stirred for 45 minutes. The CuSO4 concentrations (0.05 M; 0.1 M; and 0.15 M), sodium citrate concentrations (0.15 M; 0.2 M; and 0.25 M), and Sentalo extract (10%, 20%, and 30%) were optimized. The copper nanoparticles that synthesized were in the form of brownish green powder. The nanoparticles were characterized using FTIR, XRD, PSA, and TEM. The XRD diffractogram shows peaks at 2θ = 43.15°; 49.75°; and 73.91° with a small intensity. Copper nanoparticles that formed have stem shapes with an average diameter of 30 nm. Optimization by using the surface response method with the Box-Behnken design obtained optimal conditions at a peak of 300 nm with CuSO4 concentrations of 0.12 M to 0.15 M, sodium citrate concentrations of 0.22 M to 0.25 M, and percent extract 22, 5% to 30%. At the peak of 800 nm with a concentration of 0.05 M CuSO4 to 0.06 M, the concentration of sodium citrate was 0.15 M to 0.25 M, and the percent extract was 10% to 22.5%.

Item Type:	Thesis (Other)
Additional Information:	RSKi 620.5 Han s-1 2019 3100019081359
Uncontrolled Keywords:	Nanopartikel Tembaga, Ekstrak Daun Sentalo, Metode Respon Permukaan, Desain Box-Behnken
Subjects:	Q Science > QD Chemistry > QD75.2 Chemistry, Analytic T Technology > TP Chemical technology > TP248 Nanogels. Nanoparticles.
Divisions:	Faculty of Natural Science > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User:	Cantika Alda Hafshah Handoyo
Date Deposited:	22 Dec 2025 01:57
Last Modified:	22 Dec 2025 01:57
URI:	http://repository.its.ac.id/id/eprint/65496

Actions (login required)

View Item