Fauzi, Azharuddin (2019) Studi Pengaruh Variasi Komposisi Filler Polypropylene (PP) yang Diperkuat Oleh Woven Fiberglass Terhadap Sifat Fisis dan Sifat Mekanik Komposit Untuk Aplikasi Papan Partikel Semen. Other thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
02511540000107_Undergraduate_Theses.pdf Download (2MB) | Preview |
Abstract
Sampah plastik merupakan permasalahan yang cukup serius karena memiliki sifat non-biodegradable yang apabila menumpuk dapat menyebabkan kerusakan lingkungan. Sampah plastik menimbulkan masalah karena sanat sulit diuraikan oleh mikroorganisme yang menyebabkan mineral di dalam tanah semakin berkurang. Jenis sampah plastik yang cukup banyak dipakai adalah PP (Polypropylene) yang banyak dipakai sebagai bungkus makanan, bungkus pakaian, barang-barang elektronik dan masih banyak lagi. Limbah lainnya seperti bata ringan. Bata ringan memiliki unsur kalsium yang memiliki kemampuan mempercepat proses pengikatan apabila ditambahkan air. Solusi untuk mengurangi limbah sampah yang menumpuk adalah dengan membuat papan partikel semen yang diperkuat oleh plastik PP (Polypropylene). Melimpahnya limbah plastik PP dan bata ringan dapat dimanfaatkan untuk dijadikan produk yang memiliki nilai ekonomi. Penelitian ini bertujuan untuk menganalisis pengaruh variasi komposisi limbah plastik PP yang diperkuat oleh woven fiberglass terhadap sifat mekanik dan sifat fisis, yang diharapkan dapat diaplikasikan sebagai papan partikel semen. Pengujian yang dilakukan adalah Pengujian yang akan dilakukan meliputi Mikroskop optik. Untuk pengujian kuat beban lentur menggunakan standar ASTM C293. Pengujian kompresi dengan menggunakan standar yang digunakan adalah ASTM C270. Pengujian penyerapan air dengan standar ASTM C1403, dan pengujian densitas dengan standar C642. Hasil pengujian diketahui bahwa Penambahan PP dan woven fiberglass memberikan sifat mekanik dan sifat fisis yang baik. Komposit dengan penambahan 0,75 phr PP dan 0,28 phr woven fiberglass memiliki kekuatan sebesar 98,302 kg/cm2 dan kuat tekan sebesar 20,667 Mpa Hasil pengujian mekanik telah memenuhi standar ISO 8335 1987
================================================================================================================================
Plastic waste is quite serious problems because of the nature of non-biodegradable which accumulates can cause damage to the environment. Plastic waste pose a problem because the sanat difficult outlined by the microorganisms that cause the minerals in the soil on the wane. Types of plastic waste which is quite widely used are PP (Polypropylene) are widely used as food wrap, wrap your clothes, electronic goods and much more . Other wastes such as lightweight bricks. Light bricks have elements of calcium binding process has the ability when added to water. Solutions to reduce waste that builds up is to make particle board of cement reinforced by plastic PP (Polypropylene). The abundance of waste plastic PP and lightweight brick can be used for products that have economic value. This research aims to analyze the effect of variations in the composition of the plastic waste PP reinforced by fiberglass woven against the mechanical properties and physical properties, which is expected to be applied as a cement particle board. Testing done is Testing to be performed include the Optical Microscope. Flextural strength for testing using standard ASTM C293. Testing compression by using the standard used is ASTM C270. Water absorption test with standard , and testing the density with the standard C1403 . The test results were known that the addition of PP and woven fiberglass give the mechanical properties and physical properties. Composites with addition of 0.75 phr and 0.28 phr PP woven fiberglass has the strength of 98.302 kg/cm2 and a compressive test results of 20.667 MPa meets ISO 8335 1987 standards
| Item Type: | Thesis (Other) |
|---|---|
| Additional Information: | RSMt 620.119 Fau s-1 2019 |
| Uncontrolled Keywords: | Sampah Plastik, Polypropylene, Woven Fiberglass, Komposit, Papan Partikel |
| Subjects: | T Technology > TL Motor vehicles. Aeronautics. Astronautics > TL240.5 Composite materials T Technology > TP Chemical technology > TP884.L5 Lightweight concrete |
| Divisions: | Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis |
| Depositing User: | Azharuddin Fauzi |
| Date Deposited: | 16 Jun 2023 01:55 |
| Last Modified: | 16 Jun 2023 01:55 |
| URI: | http://repository.its.ac.id/id/eprint/65527 |
Actions (login required)
 |
View Item |