Pengaruh Variasi Konsentrasi Ekstrak Daun Jambu Biji sebagai Inhibitor Korosi Terhadap Lama Perendaman dan Temperatur Untuk Menganalisa Laju Korosi pada Baja API 5L Grade B Dalam Media HCl 1M

Pratama, Muhammad Ghifari Pratama (2019) Pengaruh Variasi Konsentrasi Ekstrak Daun Jambu Biji sebagai Inhibitor Korosi Terhadap Lama Perendaman dan Temperatur Untuk Menganalisa Laju Korosi pada Baja API 5L Grade B Dalam Media HCl 1M. Other thesis, Institute Teknologi Sepuluh Nopember.

Text 02511540000007-Ungraduate_Theses.pdf Restricted to Repository staff only Download (3MB) | Request a copy

Abstract

Korosi didefinisikan sebagai hasil kerusakan dari reaksi kimia antara logam dengan lingkungannya. Penggunaan inhibitor merupakan salah satu cara menghambat laju korosi. Inhibitor adalah salah satu komponen yang sangat penting bagi dunia industri. Banyak industri yang lebih memilih menggunakan inhibitor anorganik karena tingkat efisiensinya yang tinggi. Namun penggunaan inhibitor anorganik memiliki sifat yang toksik dan limbahnya tidak ramah lingkungan. Maka dari itu penggunaan inhibitor organik menjadi alternatif baru untuk proteksi korosi karena bersifat biodegradable dan ramah lingkungan. Ekstrak daun jambu biji merupakan salah satu bahan organik yang dapat digunakan sebagai inhibitor. Daun jambu biji memiliki kadar antioksidan yang sangat tinggi. Salah satu antioksidan yang terkandung dalam daun jambu biji adalah tannin yang kaya akan senyawa polifenol yang mampu menghambat proses oksidasi sehingga laju korosi dapat menurun. Studi ini menggunakan specimen baja API 5L Grade B. Sedangkan elektrolit yang digunakan yaitu HCl 1M. Pengujian yang dilakukan pada penelitian ini yaitu Weightloss, EIS dan Polarisasi untuk menganalisa mekanisme laju korosi. Juga gmenggunakan pengujian pendukung seperti FTIR, AAS, dan Mikroskop Stereo. Dari hasil Weightloss diperoleh laju korosi terendah pada konsentrasi 4000ppm dengan efisiensi 90,1284%. Pada variasi temperatur diperoleh laju korosi terendah dengan menggunakan konsentrasi 4000ppm yaitu pada temperatur 27 oC dengan efesiensi sebesar 90,1284%. Pada variasi lama perendaman didapatkan laju korosi terendah dengan menggunakan konsentrasi 4000ppm yaitu pada hari ke-2 dengan efesiensi sebesar 70,4167%. Dari hasil polarisasi didapat bahwa mekanisme inhibitor ini termasuk dalam jenis inhibitor campuran (mixing inhibitor).
==================================================================================================================================
Corrosion is defined as the result of damage from chemical reactions between metals and their environment. The use of inhibitors is one way to inhibit corrosion rates. Inhibitors are one component that is very important for the industrial world. Many industries prefer to use inorganic inhibitors because of their high level of efficiency. However, the use of inorganic inhibitors has toxic properties and the waste is not environmentally friendly. Therefore, the use of organic inhibitors is a new alternative for corrosion protection because it is biodegradable and environmentally friendly. Guava leaf extract is an organic material that can be used as an inhibitor. Guava leaves have very high antioxidant levels. One of the antioxidants contained in guava leaves is tannin which is rich in polyphenol compounds which can inhibit the oxidation process so that the corrosion rate can decrease. This study uses API 5L Grade B steel specimens, while the electrolyte is used 1M HCl. The tests carried out in this study are weight-loss, EIS and polarization to analyze the corrosion rate mechanism. Also use support testing such as FTIR, AAS, and Stereo Microscopes. From the weight loss results obtained the lowest corrosion rate at 4000ppm with an efficiency of 90.1284%. At the temperature variation, the lowest corrosion rate was obtained by using 4000ppm concentration which is at a temperature of 27oC with an efficiency of 90.1284%. In the variation of immersion time the lowest corrosion rate was obtained using 4000ppm concentration on the 2nd day with an efficiency of 70.4167%. From the results of polarization, it was found that the inhibitory mechanism is included in the type of mixture inhibitor (mixing inhibitor).

Item Type:	Thesis (Other)
Additional Information:	RSMt 620.112 23 Pra p-1 2019
Uncontrolled Keywords:	Baja API 5L, Daun jambu biji, HCL, Inhibitor
Subjects:	T Technology > TA Engineering (General). Civil engineering (General) > TA418.74 Corrosion and anti-corrosives
Divisions:	Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	Muhammad Ghifari Pratama
Date Deposited:	22 Jul 2026 06:04
Last Modified:	22 Jul 2026 06:04
URI:	http://repository.its.ac.id/id/eprint/65561

Actions (login required)

View Item