Pengaruh Komposisi Filler Limbah Polypropylene dan Sekam Padi Terhadap Sifat Fisis dan Mekanik Komposit untuk Aplikasi Papan Semen Partikel

Prakusya, Hanif (2019) Pengaruh Komposisi Filler Limbah Polypropylene dan Sekam Padi Terhadap Sifat Fisis dan Mekanik Komposit untuk Aplikasi Papan Semen Partikel. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 02511540000014_Undergraduate_Thesis.pdf - Submitted Version Restricted to Repository staff only Download (2MB) | Request a copy

Abstract

Papan partikel semen komposit memiliki potensial dalam memproduksi aplikasi pembangunan. Aplikasi yang diproduksi dari papan partikel semen memiliki kekuatan dan ketangguhan lebih dari papan partikel kayu. Selain itu, papan partikel semen juga lebih tahan akan api atau panas dan kedap akan suara. Papan partikel semen biasanya digunakan dalam pembangunan fisik di sektor konstruksi seperti penggunaan pada dinding panel sebagai aplikasi tahan api dan kedap suara. Karena proses pembuatan semen berperan sebagai penyumbang gas karbon dioksida dalam proses produksinya dan salah satu jenis semen adalah semen pre-mix mortar. Salah satu upaya untuk mengurangi dampak negatif terhadap lingkungan dari produksi semen adalah menggunakan material limbah sebagai filler komposit untuk mengurangi penggunaan semen. Material limbah berupa serat alam yang dapat digunakan sebagai penguat pada komposit adalah serat sekam padi. Bahan limbah lain yang bisa digunakan sebagai pengisi adalah polypropylene dan bata ringan. Bata ringan merupakan salah satu bahan utama untuk konstruksi dinding. Penelitian ini dilakukan dengan berbagai variasi komposisi sekam padi, dan polypropylene pada komposit sekam padi/ polypropylene/ bata ringan/ semen untuk aplikasi papan partikel. Pengujian yang dilakukan berupa pengujian fisis (absorbsi air dan densitas), pengujian mekanik (beban lentur dan kuat tekan) serta pengujian mikroskop optik. Hasil penelitian menunjukkan bahwa penambahan sekam padi dan polypropylene dapat memberikan sifat fisis dan mekanis yang lebih baik pada komposisi tertentu. Nilai pengujian sifat fisis dan mekanis papan semen partikel tidak seluruhnya memenuhi standar SNI 03-2105-2006, namun seluruhnya telah memenuhi standar ISO 8335. Nilai kuat lentur dan kuat tekan tertinggi dimiliki oleh komposit dengan variasi komposisi 0,5 phr sekam padi dan 0.5 phr polypropylene dengan nilai masing-masing sebesar 149,29 dan 523 kgf/cm2.
===================================================================================================================================
Composite cement particle board has potential in producing development applications. Applications produced from cement particle boards have more strength and toughness than wood particle boards. In addition, cement particle boards are also more resistant to fire or heat and soundproofing. Cement particle boards are usually used in physical construction in the construction sector such as the use of wall panels as a fire resistant and soundproof application. Because the cement making process acts as a contributor of carbon dioxide gas in the production process and one type of cement is pre-mix mortar cement. One effort to reduce the negative impact on the environment from cement production is to use waste material as a composite filler to reduce the use of cement. Natural fibers that can be used as reinforcement in composites are rice husk fiber. Other waste materials that can be used as fillers are polypropylene waste and lightweight bricks.. This study was conducted with variations in the composition of rice husk and polypropylene on the physical and mechanical properties of rice husk/ polypropylene waste / lightweight brick / cement composite for particle board applications. Tests carried out in the form of physical (water absorption and density), mechanical testing (flexural strength and compression strength), optical microscope of cement bonded particle board composites. Results of the study shows that the addition of rice husk and polypropylene in the composite gave better physical and mechanical properties in spesific composition. The results of physical and mechanical of composite samples on all variations of composition don’t show that all of the values have met SNI standards but all the values have met ISO 8335 standard. The highest flexural strength and compression strength is owned by the composite with variations in the composition of 0,5 phr rice husk and 0.5 phr polypropylene with values of 149,29 dan 523 kgf/cm2 respectively.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Limbah Bata Ringan, Limbah Sekam Padi, Polypropylene, Papan Partikel Semen
Subjects:	T Technology > TA Engineering (General). Civil engineering (General) > TA418.9 Composite materials. Laminated materials. T Technology > TA Engineering (General). Civil engineering (General) > TA681 Concrete construction
Divisions:	Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	Hanif Prakusya
Date Deposited:	22 Jul 2026 06:15
Last Modified:	22 Jul 2026 06:15
URI:	http://repository.its.ac.id/id/eprint/65679

Actions (login required)

View Item