Pengaruh Temperatur Pemadatan Terhadap Karakteristik Hasil Uji Marshall Untuk Campuran Lataston Lapis Pondasi (HRS-BASE) Dengan Penambahan Sampah Plastik Tipe Polyethylene Terephthalate (PET)

Perdhana, Anggardha Yanotama Wahyu (2019) Pengaruh Temperatur Pemadatan Terhadap Karakteristik Hasil Uji Marshall Untuk Campuran Lataston Lapis Pondasi (HRS-BASE) Dengan Penambahan Sampah Plastik Tipe Polyethylene Terephthalate (PET). Diploma thesis, Institut Teknologi Sepuluh Nopember.

Text 10111510000102-Undergraduate_Thesis.pdf Restricted to Repository staff only Download (6MB) | Request a copy

Abstract

Indonesia menempati posisi keempat sebagai negara dengan penggunaan botol plastik terbanyak di dunia. Memanfaatkan sampah botol plastik sebagai bahan tambahan campuran aspal merupakan salah satu solusi permasalahan sampah botol plastik. Spesifikasi campuran aspal yang digunakan merupakan Lataston Lapis Pondasi (HRS-Base). Kadar aspal yang digunakan yakni 7,3%. Kadar sampah botol plastik yang digunakan yakni 5% dari total berat aspal. Suhu pemadatan yang digunakan yakni 100°C, 110°C, 120°C, 130°C, 140°C, 150°C, 160°C, 170°C, dan 180°C. Penelitian ini menggunakan komposisi agregat dari penelitian Farah Aisah (2018) yang mengacu pada spesifikasi umum 2018. Metode yang digunakan dalam penelitian ini merupakan metode basah, dimana PET dicampurkan ke dalam aspal panas. Hasilnya, nilai penetrasi, berat jenis, dan daktilitas meningkat seiring meningkatnya suhu pencampuran, sedangkan kehilangan berat, titik nyala, dan titik lembek menurun. Aspal dengan penambahan plastik PET nilai penetrasi, kehilangan berat, dan daktilitas lebih rendah dibanding aspal tanpa penambahan plastik PET, sedangkan untuk nilai berat jenis, titik nyala, dan titik lembek lebih tinggi. Baik pada campuran aspal tanpa dan dengan penambahan plastik PET nilai density, VFA, stabilitas, dan MQ semakin meningkat seiring dengan meningkatnya suhu pemadatan, sedangkan nilai VIM, VMA, dan flow menurun seiring dengan meningkatnya suhu pemadatan. Campuran aspal tanpa penambahan plastik PET memiliki nilai density, VFA, dan flow yang lebih tinggi dibanding campuran aspal dengan penambahan plastik PET, sedangkan untuk nilai VIM, VMA, dan stabilitas lebih rendah.
==================================================================================================================================
Indonesia is the fourth place by using the most plastic bottles in the world. Using plastic bottles waste as a mixture of additives is one solution to reduce plastic bottles waste. This research used Hot Rolled Sheet-Base (HRS-Base)’s specification. The optimum asphalt content is 7,3%. The percentage of waste plastic bottles used is 5% of total asphalt weight. The compaction temperature used are 100°C, 110°C, 120°C, 130°C, 140°C, 150°C, 160°C, 170°C, and 180°C. This research use the aggregate composition of Farah Aisah (2018) based on general specification of PU Bina Marga 2018. The method used in this research is wet method, where PET is mixed into hot asphalt. The results are, penetration, density, and ductility values increase with increasing mixing temperature, while weight loss, flash point, and softening point decrease. Asphalt with the addition of PET plastics have lower penetration, weight loss, and ductility value than asphalt without the addition of PET plastic, while for spesific gravity, flash point, and softening point values they are lower. Both on the asphalt mixture without and with the addition of PET plastics the values of density, VFA, stability, and MQ increases with increasing compaction temperature, while the values of VIM, VMA, and flow decrease with increasing compaction temperature. Asphalt mixture without the addition of PET plastics have higher density, VFA, and flow values than asphalt mixture with the addition of PET plastics, while for VIM, VMA and stability values they are lower.

Item Type:	Thesis (Diploma)
Uncontrolled Keywords:	Polyethylene Terephthalate (PET), Lataston Lapis Pondasi, Parameter Marshall, Temperatur, Pemadatan
Subjects:	T Technology > TA Engineering (General). Civil engineering (General) > TA443.A7 Asphalt
Divisions:	Faculty of Vocational > Civil Infrastructure Engineering (D3)
Depositing User:	Anggardha Yanotama Wahyu Perdhana
Date Deposited:	17 Oct 2025 08:58
Last Modified:	17 Oct 2025 08:58
URI:	http://repository.its.ac.id/id/eprint/65729

Actions (login required)

View Item