Ghazy, Ifthar Muhammad (2019) Analisis Pengaruh Luas Permukaan Dan Jenis Katoda Terhadap Efisiensi Anoda Pada Pengujian Imersi Dengan Menggunakan Metode DNV GL Rp-B401. Other thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
02511540000111-Undergraduate_Theses.pdf Download (3MB) | Preview |
Abstract
Korosi adalah proses degradasi sebuah materia akibat reaksi redoks antara suatu senyawa atau logam dengan berbagai zat. Pada dunia industri korosi masih menjadi sorotan khusus, karena kerusakan dan kegagalan yang disebabkan oleh korosi menimbulkan kerugian yang tidak sedikit. Ada beberapa cara untuk mengendalikan proses korosi, salah satunya dengan metode SACP. Pada penelitian kali ini menggunakan metode SACP berdasarkan standar DNV•GL RP-B401. Tujuan dari penelitian ini adalahh untuk mengetahui karakteristik dari anoda korban, yaitu: efisiensi,dan potensial anoda, selain itiu pengaruh jenis katoda dan pengaruh luas permukaan katoda terhadap efisiensi anoda korban aluminum (Al). Pada percobaan ini didapatkan hasil bahwa semakin kecil luas permukaan maka memiliki efisiensi yang lebih tinggi. Sedangkan semakin besar luas permukaan maka arus potensial akan semakin positif. Pada luas permukaan 100cm2 memiliki efisiensi 71% sedangkan pada luas permukaan 550cm2 memiliki efisiensi sebesar 62%. Lain halnya dengan arus potensial, pada luas permukaan 100cm2 memiliki arus potensial -1136,5 mV, dan pada luas permukaan 550cm2 memiliki arus potensial -982,5 mV. Sedangkan jenis katoda mempengaruhi efisiensi sebesar ± 14%, hal tersebut karena adanya perbedaan komposisi paduan pada kedua pipa baja tersebut. Arus potensial yang dihasilkan juga berbeda, dimana API 5L Grade memiliki hasil yang lebih negatif yaitu -1026,5 mV dan pada pipa baja rendah memiliki potensial -980 mV pada saat open circuit potential.
=================================================================================================================================
Corrosion is the process of degradation of a material due to a redox reaction between a compound or metal with various substances. Corrosion still have a special spotlight in the industry, because the damage and failure caused by corrosion causes a significant loss. There are several ways to control the corrosion process, one of them is the SACP method. In this study using the SACP method based on DNV standards • GL RP-B401. The purpose of this study is to determine the characteristics of the sacrificial anode, namely: efficiency, and anode potential, besides the influence of the cathode type and the effect of the cathode surface area on the efficiency of the aluminum sacrifice anode. n this experiment the results showed that the smaller the surface area it has a higher efficiency. While the greater the surface area, the potential current will be more positive. The 100cm2 surface area has an efficiency of 71% while the surface area of 550cm2 has an efficiency of 62%. As with the potential flow, the surface area of 100cm2 has a potential current of -1136.5 mV, and at a surface area of 550cm2 has a potential current of -982.5 mV. While the cathode type affects the efficiency of ± 14%, this is because of the difference in alloy composition in the two steel pipes. The resulting potential currents are also different, where API 5L Grade has a more negative result which is -1026.5 mV and the low steel pipe has a potential of -980 mV when open circuit potential.
| Item Type: | Thesis (Other) |
|---|---|
| Additional Information: | RSMt 620.112 23 Gha a-1 2019 |
| Uncontrolled Keywords: | Korosi, Anoda Korban, SACP, DNV•GL, Aluminum, Efisiensi, Arus Potensial, Jenis Katoda, Luas Permukaan. |
| Subjects: | T Technology > TA Engineering (General). Civil engineering (General) > TA418.75 Corrosion-resistant materials T Technology > TN Mining engineering. Metallurgy > TN879.5 Petroleum pipelines |
| Divisions: | Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis |
| Depositing User: | ifthar muhammad ghazy |
| Date Deposited: | 17 May 2024 10:12 |
| Last Modified: | 17 May 2024 10:12 |
| URI: | http://repository.its.ac.id/id/eprint/65772 |
Actions (login required)
 |
View Item |