Pengaruh Temperatur Pemadatan Terhadap Karakteristik Hasil Uji Marshall Untuk Campuran Lataston Lapis Aus (Hrs-Wearing Course) Dengan Penambahan Plastik Tipe Pet (Polyethylene Terephthalate)

Wicaksono, Andiatma Nur Irfan (2019) Pengaruh Temperatur Pemadatan Terhadap Karakteristik Hasil Uji Marshall Untuk Campuran Lataston Lapis Aus (Hrs-Wearing Course) Dengan Penambahan Plastik Tipe Pet (Polyethylene Terephthalate). Diploma thesis, Institute Teknologi Sepuluh Nopember.

Text 10111510000099-Undergraduate_Thesis.pdf Restricted to Repository staff only Download (5MB) | Request a copy

Abstract

Sampah plastik di Indonesia mencapai 65 ton per tahun sehingga diperlukan sebuah inovasi pengolahan limbah plastik untuk menekan jumlah limbah plastik. Salah satu pemanfaatan limbah botol plastik adalah sebagai bahan tambah pada campuran aspal. Keberhasilan pemadatan campuran aspal erat kaitannya dengan suhu pemadatan. Oleh karena itu, perlu adanya suatu penelitian suhu pemadatan dengan variasi suhu pemadatan yang bertujuan untuk mendapatkan suhu optimum pemadatan. Penelitian ini mengunakan lataston lapis aus (HRS-WC). Kadar aspal optimum yang digunakan yakni 8,2% dan kadar limbah botol plastik PET 6% dari total berat aspal. Komposisi proporsi agregat menggunakan data dari Annisa Karismatika (2018) yang mengacu pada spesifikasi umum Bina Marga tahun 2018. Metode yang digunakan pada penelitian ini menggunakan metode basah, dimana PET dicampurkan kedalam aspal panas. Sebelum dilakukan pembuatan benda uji diperlukan adanya uji karakteristik aspal berdasarkan suhu pencampuran aspal dengan plastik PET dan dilanjutkan dengan pembuatan benda uji dengan variasi suhu pemadatan 100°C, 110°C, 120°C, 130°C, 140°C, 150°C, 160°C, 170°C, dan 180°C. Hasil dari penelitian ini adalah seiring bertambahnya suhu pencampuran pada aspal modifikasi, membuat beberapa nilai uji karakteristik aspal yaitu, penetrasi, berat jenis dan daktilitas meningkat. Sedangkan nilai kehilangan berat, titik nyala dan titik lembek menurun. Untuk hasil uji marshall yang didapat seiring bertambahnya suhu pemadatan campuran aspal maka Kepadatan, Stabilitas, VFA dan Marshall Quotient meningkat, sedangkan nilai Void in Mix (VIM), Void in Mineral Agreggate (VMA) dan Flow menurun. Dari hasil penelitian ini didapatkan suhu optimum pemadatan campuran aspal tanpa penambahan PET adalah 150°C berdasarkan spesifikasi Binamarga 2018, sedangkan suhu optimum pemadatan untuk campuran aspal dengan penambahan PET adalah 140°C.
===========================================================================================================================
Plastic waste in Indonesia reaches 65 tons per year so an innovation in plastic waste treatment is needed to reduce the amount of plastic waste. One of the uses of plastic bottle waste is as an ingredient added to the asphalt mixture. The success of the asphalt mixture is closely related to the compaction temperature. Therefore, there needs to be a study of compaction temperature with variations in compaction temperature that aim to obtain the optimum compaction temperature. This study uses worn-layer lataston (HRS-WC). The optimum bitumen content used is 8.2% and the PET plastic waste content is 6% of the total asphalt weight. The composition of aggregate proportions uses data from Annisa Karismatika (2018) which refers to the general specifications of Bina Marga in 2018. The method used in this study uses the wet method, where PET is mixed into hot asphalt. Before making test specimens, it is necessary to test the characteristics of asphalt based on the mixing temperature of asphalt with PET plastic and then proceed with the manufacture of specimens with variations in compaction temperature of 100°C, 110°C, 120°C, 130°C, 140°C, 150°C, 160°C, 170°C, and 180°C. The results of this study are as the mixing temperature increases on modified asphalt, making some characteristics of asphalt test values, namely, penetration, specific gravity and increased ductility. While the value of weight loss, flash point and softening point decreases. For the Marshall test results obtained with increasing asphalt mixture compaction temperature, the Density, Stability, VFA and Marshall Quotient increase, while the value of Void in Mix (VIM), Void in Mineral Agreggate (VMA) and Flow decreases. From the results of this study, the optimum temperature of compaction of asphalt mixture without PET addition was 150°C based on Binamarga 2018 specifications, while the optimum compaction temperature for the asphalt mixture with the addition of PET was 140°C.

Item Type:	Thesis (Diploma)
Additional Information:	RSIS 625.85 Wic p-1 2019
Uncontrolled Keywords:	Kata kunci: PET (Polyethylene Terephthalate), Lataston Lapis Aus (HRS-Wearing Course), Temperatur, Pemadatan, Hasil Uji Marshall
Subjects:	T Technology > TA Engineering (General). Civil engineering (General) > TA443.A7 Asphalt
Divisions:	Faculty of Civil Engineering and Planning > Civil Engineering > 22301-(D4) Diploma 4
Depositing User:	Andiatma Nur Irfan Wicaksono
Date Deposited:	07 Aug 2026 08:07
Last Modified:	07 Aug 2026 08:07
URI:	http://repository.its.ac.id/id/eprint/65796

Actions (login required)

View Item