Analisis Pengaruh Penambahan Limbah Kantong Plastik Low Density Polyethylene (LDPE) Pada Campuran Lataston Lapis Pondasi (HRS-Base) Terhadap Parameter Marshall

Ariyanti, Adi (2019) Analisis Pengaruh Penambahan Limbah Kantong Plastik Low Density Polyethylene (LDPE) Pada Campuran Lataston Lapis Pondasi (HRS-Base) Terhadap Parameter Marshall. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 10111815000022-Undergraduate_Theses.pdf Restricted to Repository staff only Download (4MB) | Request a copy

Abstract

Peningkatan jumlah sampah plastik di Indonesia mencapai 64 juta ton per tahun berdasarkan data dari Asosiasi Industri Plastik Indonesia dan Badan Pusat Statistik. Dengan mengetahui permasalahan pekerjaan perkerasan jalan saat ini dihadapkan dengan tantangan untuk meningkatkan kualitas dan kuantitas secara optimal dengan memanfaatkan sumber daya yang ada maka, hal tersebut membuat banyak penelitian yang dilakukan untuk peningkatan kualitas pada perkerasan jalan salah satunya dengan memodifikasi sifat dari aspal tersebut dengan bahan campuran plastik. Dalam penelitian ini digunakan limbah plastik jenis LDPE (Low Density Polyethylene). Lapisan aspal yang digunakan merupakan Lataston Lapis Pondasi (HRS-Base). Kadar limbah kantong plastik yang digunakan adalah 0%; 2%; 4% dan 6% dari total berat aspal.
Tahapan dalam penelitian ini meliputi uji fisik material, pengecekan spesifikasi HRS-Base yang mengacu pada spesifikasi umum PU Bina Marga Tahun 2018, pengujian KAO (Kadar Aspal Optimal), pengujian penambahan LDPE, dan analisa hasil pengujian marshall serta parameternya. Metode yang digunakan dalam penelitian ini merupakan metode kering.
Hasil dari penelitian ini menunjukkan bahwa nilai Kadar Aspal Optimum sebesar 6,5%. Dari pengujian Marshall yang telah dilakukan, didapatkan nilai stabilitas campuran aspal yang ditambahkan LDPE mengalami peningkatan yang signifikan dibandingkan campuran aspal normal. Selain nilai stabilitas, penambahan LDPE pada campuran aspal membuat nilai VIM, VMA, Density, VFA, flow dan Marshall Quotient meningkat. Berdasarkan penelitian yang telah dilakukan, campuran aspal pada Lataston Lapis Pondasi (HRS-Base) yang memenuhi sebagian besar parameter Marshall berdasarkan spesifikasi Umum PU Bina Marga Tahun 2018 merupakan campuran aspal dengan kadar aspal optimum 6,5% dan kadar LDPE sebesar 2% dari total berat aspal. Campuran aspal Lataston Lapis Pondasi (HRS-Base) dengan penambahan LDPE dapat mengurangi jumlah harga bahan sebesar Rp 2.688 / m3 dibandingkan campuran aspal normal.
====================================================================================================================================
An increasing in plastic waste in Indonesia has reached 64 millions tons based on Plastic Industry Association and Central Buereau of Statistics Republic of Indonesia. By knowing this road pavement problem is now facing defiance to increase quality and quantity using available resources optimally so, that problem brings up many researches to increase the quality of road pavement by modifies the nature of asphalt with plastic waste mixture. This research using a LDPE (Low Density Polyethylene) kind of plastic waste. The used asphalt layer in this research is Hot Rolled Sheet-Base (HRS-Base). The amount of plastic waste used is 0%; 2%; 4% and 6% from asphalt total weight. Steps in this research including physical material tests, checking on HRS-Base specification that refers to the general specification of PU Bina Marga Year 2018, optimum asphalt content (KAO) tests, LDPE adding tests and analyze marshall tests results along with the parameter. The method used in this research is dry method. The results of this research shows that the value of Optimum Asphlat Content is 6,5%. From the Marshall tests that have been done, the stability value of the asphalt mixture that added with LDPE experienced a significant increased compared to the normal asphalt mixture. Besides stability values, an addition of LDPE in asphalt mixture made the value of VIM, VMA, Density, VFA. flow and Marshall Quotient increased. Based on researches that have been done, most of the Marshall parameterse filled with mixture of HRS-Base that based on General Specification of PU Bina Marga Year 2018 is an asphalt mixture with optimum asphalt content value 6,5% and LDPE content value is up to 2% from asphalt total weight. The added of HRS-Base mixture could detract material price cost by Rp 2.688 /m³ compared to the normal asphalt mixture.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	LDPE (Low Density Polyethylene), Hot Rolled Sheet, Marshall Parameters
Subjects:	T Technology > TE Highway engineering. Roads and pavements T Technology > TE Highway engineering. Roads and pavements > TE7 Transportation--Planning
Divisions:	Faculty of Vocational > 22401-Civil Infrastructure Engineering (D3)
Depositing User:	Adi Ariyanti
Date Deposited:	11 Aug 2026 01:13
Last Modified:	11 Aug 2026 01:13
URI:	http://repository.its.ac.id/id/eprint/65965

Actions (login required)

View Item