Degradasi Fotokatalitik Ion Cr3+, Ni2+, Dan Zn2+ Menggunakan Katalis Semikonduktor TiO2 Rutil Dengan Bantuan Sinar Uv

Ramadhan, Zein Firdaus (2019) Degradasi Fotokatalitik Ion Cr3+, Ni2+, Dan Zn2+ Menggunakan Katalis Semikonduktor TiO2 Rutil Dengan Bantuan Sinar Uv. Other thesis, Institut Teknologi Sepuluh November.

Text 01211440000022-Undergraduate_Thesis.pdf Restricted to Repository staff only Download (1MB) | Request a copy

Abstract

Pada penelitian ini telah dilakukan degradasi ion Cr3+, Ni2+, dan Zn2+ dengan variasi konsentrasi 25, 50, dan 100 ppm menggunakan katalis semikonduktor TiO2 sebanyak 100 mg di bawah penyinaran lampu UV. Penelitian muncul karena adanya ion Cr3+, Ni2+, dan Zn2+ pada limbah yang ada pada lingkungan. Tujuan dari penelitian ini adalah mengetahui keefektifan katalis semikonduktor TiO2 dengan bantuan sinar UV dalam proses degradasi ion Cr3+, Ni2+, dan Zn2+. Laju degradasi terbesar ion Ni2+ pada konsentrasi 100 ppm dan waktu 120 menit dengan laju degradasi 0,7657 ppm/menit. Laju degradasi terbesar ion Zn2+ pada konsentrasi 100 ppm dengan laju degradasi sebesar 0,7890 ppm/menit. Laju degradasi terbesar ion Cr3+ pada konsentrasi 100 ppm dan waktu 120 menit, dengan laju degradasi sebesar 0,7219 ppm/menit. Terdapat kecenderungan laju degradasi lebih cepat saat konsentrasi lebih tinggi, ketika jumlah molekul lebih banyak. =================================================================================================================================
In this study, 100 mg TiO2 as semiconductor catalyst and UV light were used to reduce nickel, chrome, and zink ion in 3 variations concentration (25 ppm, 50 ppm and 100 ppm). The purpose of this study was to determine the effectiveness of TiO2 semiconductor catalysts with UV light irradiation in the degradation processes of Cr3+, Ni2+, and Zn2+. The highest degradation rate of nickel ions at a concentration of 100 ppm and 120 minutes with a degradation rate of 0,7657 ppm/minute. The highest degradation rate of zinc ions at a concentration of 100 ppm with a degradation rate of 0,7890 ppm/minute. The highest degradation rate of chrome ions at a concentration of 100 ppm and time of 120 minutes, with a degradation rate of 0,7219 ppm / minute. There is a tendency for faster rates of degradation when concentrations are higher, when there are more molecules.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Semikonduktor, TiO2, Sinar UV, Degradasi
Subjects:	Q Science > QD Chemistry > QD716 Photocatalysis.
Divisions:	Faculty of Natural Science > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User:	Zein Firdaus Ramadhan
Date Deposited:	20 Jul 2026 04:21
Last Modified:	20 Jul 2026 04:21
URI:	http://repository.its.ac.id/id/eprint/66164

Actions (login required)

View Item