Pengaruh Suhu Pemanasan pada Sifat Fisis Senyawa Karbon dari Gula Siwalan

Sari, Novita (2019) Pengaruh Suhu Pemanasan pada Sifat Fisis Senyawa Karbon dari Gula Siwalan. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 01111540000085-Undergraduate_Thesis.pdf Restricted to Repository staff only Download (2MB) | Request a copy

Abstract

Senyawa karbon telah berhasil didapatkan menggunakan metode pemanasan. Bahan dasar yang digunakan adalah gula siwalan dari Pacitan, Lamongan, Jawa Timur. Serbuk karbon dasar diperoleh pada suhu pemanasan 2500 C selama 2 jam, kemudian sampel dasar tersebut dipanaskan lagi pada temperatur 4000 C, 5000 C, 6000 C dan 7000 C selama 5 jam. Kemudian serbuk karbon di cuci dengan akuades, serbuk masing-masing sampel di ukur densitasnya menggunakan piknometer. Sintesis larutan karbon dilakukan dengan melarutkan 1 gram serbuk karbon kedalam 10 ml larutan aquades dan larutan DMSO. Ultrasonic cleaner digunakan selama 2 jam pada setiap larutan supaya serbuk karbon terdispersi dalam larutan kemudian dilakukan sentrifugasi selama 30 menit dengan kecepatan 4.000 rpm. Larutan karbon yang diperoleh di karakterisasi dengan menggunakan Particle Size Analyser (PSA) dan UV-Vis. Sedangkan sebagian lagi digunakan untuk dideposisi diatas substrat kaca ITO dengan menggunakan teknik spin coating dan dihasilkan lapisan tipis karbon yang kemudian dikarakteisasi dengan four point probe (FPP). Serbuk karbon yang dihasilkan dari pemanasan gula siwalan densitas serbuk yang semakin meningkat dengan adanya peningkatan temperatur pemanasan, nilai densitas yang diperoleh yaitu 0,71 gr/cm3 sampai 1,40 gr/cm3. Penambahan temperatur pemanasan karbon mengakibatkan ukuran partikel karbon tersebut semakin homogen, hal ini ditunjukkan oleh pengujian PSA. Nilai ukuran partikelnya dari suhu pemanasan T250 sampai T700 rata-rata adalah 225,26 nm sampai 182 nm. Absorbansi senyawa karbon semakin besar seiring dengan meningkatnya suhu pemanasan. Serapan absorbansi maksimum senyawa karbon terdapat pada rentang panjang gelombang Ultraviolet dan Visible sehingga dapat diaplikasikan pada material semikonduktor. Konduktivitas listrik senyawa karbon yang dihasilkan dengan pengujian FPP yang yaitu sebesar 2,06–6,53 S/m, sedangkan energi gap diperoleh pada senyawa karbon yaitu 0,40 eV – 1,30 eV sehingga dapat dikategorikan sebagai material semikonduktor.
===================================================================================================================================
Carbon compounds has successfully been synthesized using the heating method. The starting material used was Palmyra sugar from Paciran, Lamongan, East Java. The basic carbon powder was obtained at a heating temperature of at 2500 C for 2 hours, then it was heated again at temperatures of 4000 C, 5000 C, 6000 C dan 7000 C for 5 hours. Then the carbon powder was washed with distilled water. The sample density was measured using a piknometer. Carbon solution was prepared by dissolving 1 gram of carbon powder into 10 ml of distilled water and DMSO. The ultrasonic cleaner was used for 2 hours for each solution so that the carbon powder was dispersed in the solution then centrifuged for 30 minutes at 4000 rpm. Carbon solutions were characterized using particle size analyzers (PSA) and UV-Vis. While some of it was used to be deposited on the ITO glass substrate using spin coating technique and produced a thin layer of carbon which was then characterized by a four-point probe (FPP). The density of carbon powder increases with the increase in heating temperature, the density obtained was 0,71-1,40 gr/cm3. An addition of carbon heating temperature results in smaller carbon particle size, which was indicated by PSA testing. The particle size value of the heating temperature T250 to T700 on average is 225 nm to 182 nm. The absorbance increases with increasing heating temperature. Maximum absorbance of carbon compounds was found in the ultraviolet and visible wavelenght range, so that it can be applied to semiconductor materials. The value of electrical conductivity on carbon compounds measured by four point probe is 2,06–6,53 S/m, the energy gap is 0.40 eV - 1.30 eV. Carbon compounds can be categorized as a semiconductor materials according to these result.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Karbon, konduktivitas listrik, semokonduktor
Subjects:	Q Science > QC Physics > QC610.3 Electric conductivity Q Science > QC Physics > QC 611.97.T46 Temperature effects. Including transition temperature
Divisions:	Faculty of Natural Science > Physics > 45201-(S1) Undergraduate Thesis
Depositing User:	Novita Sari
Date Deposited:	20 Jul 2026 03:25
Last Modified:	20 Jul 2026 03:25
URI:	http://repository.its.ac.id/id/eprint/66175

Actions (login required)

View Item