Modifikasi Karbon Aktif Dari Tandan Kosong Kelapa Sawit (Elaeis Jacq) Dengan Metode Double Step Untuk Adsorpsi Karbon Dioksida

Setiawan, Aziz (2019) Modifikasi Karbon Aktif Dari Tandan Kosong Kelapa Sawit (Elaeis Jacq) Dengan Metode Double Step Untuk Adsorpsi Karbon Dioksida. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 01211540000067-Undergraduate_Thesis.pdf Restricted to Repository staff only Download (2MB) | Request a copy

Abstract

Modifikasi karbon aktif dari tandan kosong kelapa sawit (Elaeis Jacq) dengan metode double-step telah menunjukkan peningkatan kapasitas adsorpsi karbon dioksida dari 3,300 mmol/g menjadi 4,441 mmol/g. Kinetika adsorpsi karbon dioksida adalah orde dua semu dengan mengikuti korelasi R2 yaitu kapasitas adsorpsi selalu proporsional dengan banyaknya sisi aktif. Peningkatan kapasitas tersebut terjadi sebagai hasil dari perubahan sifat menjadi CO2-filik dengan pengaruh penambahan nitrogen. Karbon kemudian dikarakterisasi dengan instrumen XRD, FTIR, SEM, dan Adsorpsi-desorpsi nitrogen. Hasil XRD menunjukkan bahwa karbon aktif termodifikasi nitrogen memiliki fasa amorf dan berstruktur grafit dan hasil SEM menunjukkan adanya pori berongga yang terbentuk pada karbon. Spektra FTIR memberikan hasil vibrasi ulur gugus C=C pada 1650 cm-1, gugus C-C pada 1057 cm-1, gugus C=O aldehida pada 1753 cm-1, vibrasi ulur C-N pada 1437 cm-1 dan vibrasi ulur C=N pada 1540 cm-1. Hasil adsorpsi-desorpsi nitrogen menunjukkan bahwa terjadi penurunan luas permukaan pada sampel karbon aktif dari 1178 m2/g menjadi 891,8 m2/g dengan adanya penambahan nitrogen.
===================================================================================================================================
**English Version (without paragraphs):**

Modification of activated carbon derived from empty fruit bunches (*Elaeis* spp.) using a double-step method successfully increased the carbon dioxide adsorption capacity from 3.300 mmol/g to 4.441 mmol/g. The CO₂ adsorption kinetics followed a pseudo-second-order model with a high correlation coefficient (R²), indicating that the adsorption capacity was proportional to the number of active sites. This enhancement in adsorption capacity was attributed to the transformation of the carbon surface into a more CO₂-philic material through nitrogen incorporation. The synthesized carbon was characterized using X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), and nitrogen adsorption-desorption analysis. XRD results showed that the nitrogen-modified activated carbon exhibited an amorphous phase with a graphite structure, while SEM observations revealed the presence of well-developed hollow pores on the carbon surface. FTIR spectra identified characteristic stretching vibrations of C=C at 1650 cm⁻¹, C–C at 1057 cm⁻¹, aldehyde C=O at 1753 cm⁻¹, C–N at 1437 cm⁻¹, and C=N at 1540 cm⁻¹. Nitrogen adsorption-desorption analysis indicated a decrease in the specific surface area from 1178 m²/g for the activated carbon to 891.8 m²/g after nitrogen modification, despite the improved CO₂ adsorption performance.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Adsorpsi, Karbon, Karbon dioksida, Modifikasi, Nitrogen, Tandan Kosong
Subjects:	Q Science Q Science > QD Chemistry > QD502 Chemical kinetics Q Science > QD Chemistry > QD547 Flocculation, precipitation, adsorption, etc.
Divisions:	Faculty of Natural Science > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User:	Aziz Setiawan
Date Deposited:	20 Jul 2026 05:51
Last Modified:	20 Jul 2026 05:51
URI:	http://repository.its.ac.id/id/eprint/67257

Actions (login required)

View Item