Komparasi Karakteristik Dosimetri Material Bolus Berbahan Dasar Silicone Rubber Dan Bismuth Dengan Bolus Komersial Menggunakan Berkas Foton Berenergi 6 dan 10 MV

Sekartaji, Gandes (2019) Komparasi Karakteristik Dosimetri Material Bolus Berbahan Dasar Silicone Rubber Dan Bismuth Dengan Bolus Komersial Menggunakan Berkas Foton Berenergi 6 dan 10 MV. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 01111540000105-Undergraduate_Theses.pdf Restricted to Repository staff only Download (2MB) | Request a copy

Abstract

Material bolus sering digunakan pada bidang radioterapi untuk meningkatkan dosis permukaan serta mengganti jaringan yang rusak agar mendapatkan distribusi dosis yang sesuai. Bolus biasanya memiliki sifat yang setara dengan jaringan atau air. Pada penelitian ini menggunakan bolus fabrikasi yaitu Silicone Rubber dan Bismuth yang akan dibandingkan dengan bolus komersial seperti paraffin, Play-Doh dan Lilin malam. Tujuan dari penelitian ini adalah meneliti relatif densitas elektron (RED), koefisien atenuasi, faktor transmisi, persentase dosis permukaan (PSD) serta PDD dari masing-masing bolus yang diuji. Bolus dicetak dengan akrilik berukuran 11×11×0.5 cm2. Penelitian ini dilakukan di RS MRCCC Siloam Jakarta. Pengujian relatif densitas elektron, persentase dosis permukaan dan grafik PDD menggunakan CT Scan dan Treatment Planning System (TPS). Selanjutnya untuk uji dosimetri lainnya seperti faktor transmisi dan koefisien atenuasi menggunakan pesawat Linear Accelerator (LINAC) dengan sumber energi foton 6 dan 10 MV. Hasil analisis RED serta densitas membuktikan bahwa bolus tersebut setara dengan densitas jaringan lunak seperti lemak, payudara, paru-paru, serta hati. Hasil karakterisasi menunjukkan Percentage Depth Dose (PDD) dari bolus ketebalan 1,5 cm cocok diterapkan dalam radioterapi dengan spesifikasi pada energi 6 MV sebagai shielding karena dosis permukaannya mencapai 100% sedangkan untuk ketebalan 0.5 dan 1 cm pada foton 6 dan 10 MV digunakan untuk bolus sebagai tissue compensator.
===================================================================================================================================
Bolus material is often used in radiotherapy for increasing surface dose, compensate for surface irregularities and internal heterogeneities. Bolus has properties equivalent to water and soft tissue. In this study, the mixture of Silicone Rubber (SR) and Bismuth was used for bolus fabrication and then compared to commercial boluses such as Paraffin, Play-Doh, and Paraffin Wax. The study aimed to evaluate the comparison of relative electron density (RED), effective mass attenuation coefficient, transmission factor, percentage of surface dose (PSD), and Percentage Depth Dose (PDD) for all boluses. The bolus was made with the size 11 × 11 × 0.5 cm3. Physical density of the synthesized bolus was assessed by computerized tomography (CT) Scanning. The values of RED for all boluses has a similar to water and soft tissue. These results proved that the bolus is equivalent to soft tissue density such as fat, breast, lungs, and liver. Furthermore, for other dosimetry tests such as transmission factors and attenuation coefficients using Linear Accelerator (LINAC) with photon energy sources 6 and 10 MV. The characterization results showed that Percentage Depth Dose (PDD) of 1.5 cm thickness was suitable to be applied in radiotherapy with specifications on 6 MV energy as shielding because the surface dose reached 100% while for 0.5 and 1 cm thickness on photons 6 and 10 MV was used for bolus as a tissue compensator.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Bolus, RED, Faktor Transmisi, Koefisien Atenuasi massa, PSD
Subjects:	Q Science Q Science > QC Physics
Divisions:	Faculty of Natural Science > Physics > 45201-(S1) Undergraduate Thesis
Depositing User:	Gandes Sekartaji
Date Deposited:	20 Jul 2026 03:58
Last Modified:	20 Jul 2026 03:58
URI:	http://repository.its.ac.id/id/eprint/67390

Actions (login required)

View Item