Sintesis Zeolit A Dari Fly Ash Dan NaOH Sebagai Builder Deterjen Dengan Proses Hidrotermal

Fatmawati, Arum Nur and Santoso, Ahmad Da'i Yoga (2019) Sintesis Zeolit A Dari Fly Ash Dan NaOH Sebagai Builder Deterjen Dengan Proses Hidrotermal. Diploma thesis, Institut Teknologi Sepuluh Nopember.

Text 10411600000055_10411600000097_Non Degree.pdf - Accepted Version Restricted to Repository staff only Download (8MB) | Request a copy

Abstract

Deterjen merupakan bahan pencuci yang sering digunakan dalam industri maupun rumah tangga. Banyaknya pemakaian deterjen berdampak pada pencemaran lingkungan karena adanya kandungan fosfat pada builder. Tujuan dari percobaan ini adalah menggantikan builder deterjen yang mengandung fosfat dengan Zeolit A yang lebih ramah lingkungan. Prosedur penelitian ini diawali dengan tahap preparasi fly ash dengan meletakan magnet di atas fly ash dan direaksikan dengan H2SO4 1M pada suhu 60-800C diaduk dengan magnetic stirerr dengan kecepatan 600 rpm selama 2 jam kemudian hasilnya disaring dan dikeringkan di oven, Selanjutnya pembuatan larutan Natrium Silika dari fly ash hasil preparasi dengan NaOH 1M, 2M, 3M, 4M dan 5M diaduk dengan magneic stirerr dengan kecepatan 600 rpm dengan suhu 60-800C selama 1jam, pembuatan larutan Natrium Alumina dari 2,7 gram Al(OH)3 dan NaOH 1M diaduk dengan magnetic stirerr dengan kecepatan 600 rpm dengan suhu 60-800C selama 1jam, kemudian Natirum Silika dicampur dengan Natirum Alumina diaduk dengan magnetic stirerr pada kecepatan 600 rpm selama 30 menit, larutan hasil campuran dimasukkan kedalam botol PP kemudian diamsukkan kedalam oven dengan suhu 1000C selam 12 jam, endapan dipisahkan dengan filtrat kemudian di oven pada suhu 1000C selama 3 jam. Dari hasil penelitian dan analisa zeolit A yang dihasilkan didapatkan kesimpulan bahwa Zeolit A kemurniannya cukup rendah karena masih terdapat kandungan Fe dan Ca. Hasil uji deterjensi Zeolit A terbesar pada variabel Zeolit A 5 M 25,98 % lebih rendah dari STPP (Sodium Tripolyphosphate) sebesar 26,94%. Hasil uji Kapasitas Tukar Kation (KTK) Zeolit A semakin besar dengan bertambahnya konsentrasi NaOH sebesar 99,8 meq/100 gr, 159,68 meq/100 gr dan 159,4 meq/100 gr. Zeolit A bersifat mikropori karena memiliki diameter pori sebesar 1,73 A.
==================================================================================================================================
Detergent is a washing material that is often used in industry and households. The amount of detergent use has an impact on environmental pollution due to the phosphate content of builders. The purpose of this experiment is to replace detergent builders containing phosphate with Zeolite A which are more environmentally friendly. The procedure of this study begins with the preparation stage of fly ash by placing a magnet on the fly ash and stirring, the results of the preparation with a magnet are then dissolved with 1M H2SO4 at 60-800C stirred with magnetic stirerr at 600 rpm for 2 hours then the results are filtered and dried in the oven. Furthermore, making Silica Sodium solution from fly ash prepared by 1M, 2M, 3M, 4M and 5M NaOH stirred with magneic stirerr at a speed of 600 rpm at 60-800C for 1 hour, making Sodium Alumina solution from 2.7 grams of Al (OH) 3 and 1M NaOH are stirred with magnetic stirrer at a speed of 600 rpm with a temperature of 60-800C for 1 hour, then Silica Mixture is mixed with Naughty Alumina stirred with magnetic stirerr at a speed of 600 rpm for 30 minutes, the mixed solution is put into a PP bottle then put into the oven with a temperature of 1000C for 12 hours, the sediment is separated by filtrate and then in the oven at 1000C for 3 hours. From the results of the research and analysis of zeolite A produced the results Zeolite A purity is low because there are still Fe and Ca contents. Zeolite A detergency test on the variable A 5 M Zeolite 25.98 were lower than STPP (Sodium Tripolyphosphate) of 26.94%. Test results of Cation Exchange Capacity (CEC) Zeolite A is greater with increasing NaOH concentration of 99.8 meq / 100 gr, 159.68 meq / 100 gr and 159.4 meq / 100 gr. Zeolite A is micropore because it has a pore diameter of 1.73 A.

Item Type:	Thesis (Diploma)
Additional Information:	RSKI 541.39 Fat s-1 2019
Uncontrolled Keywords:	Fly Ash, Builder, Deterjen, Zeolit A
Subjects:	Q Science > QD Chemistry > QD75.2 Chemistry, Analytic
Divisions:	Faculty of Vocational > 24305-Industrial Chemical Engineering Technology
Depositing User:	Fatmawati Arum Nur
Date Deposited:	13 Aug 2026 02:09
Last Modified:	13 Aug 2026 02:09
URI:	http://repository.its.ac.id/id/eprint/67577