Pengaruh Komposisi Serat Kenaf dan Serbuk CaCO3 Terhadap Karakteristik Material Komposit Hybrid Bermatriks Poliester Tak Jenuh untuk Material Komponen Otomotif

Laksana, Alfian Hudan (2019) Pengaruh Komposisi Serat Kenaf dan Serbuk CaCO3 Terhadap Karakteristik Material Komposit Hybrid Bermatriks Poliester Tak Jenuh untuk Material Komponen Otomotif. Masters thesis, Institut Teknologi Sepuluh Nopember.

Text 02511650012003-Master_Thesis.pdf Restricted to Repository staff only Download (3MB) | Request a copy

Abstract

Komposit hybrid yang diperkuat serat kenaf (Hibiscus Cannabinus L.) banyak dikembangkan sebagai pengganti komposit hybrid berpenguat serat kaca atau serat karbon. Kalsium Karbonat (CaCO3) merupakan pengisi yang dapat digunakan sebagai penguat komposit. CaCO3 yang digunakan pada penelitian ini berasal dari limbah industri. Tujuan dalam penelitian ini adalah menganalisis pengaruh variasi komposisi penambahan serat kenaf dan serbuk CaCO3 sebagai material penguat terhadap sifat mekanik dan fisik komposit hybrid bermatriks poliester tak jenuh. Komposit hybrid poliester tak jenuh/serat kenaf/CaCO3 (PTJ/Serat Kenaf/CaCO3) dibuat dengan metode Hand Layup dalam dua variasi komposisi yang terdiri dari komposit hybrid berkomposisi resin dan serat kenaf terkontrol (80:20) dengan komposisi CaCO3 yang berbeda (2,5, 5, 7,5, 10 dan 20 per hundred rasio) dan komposit hybrid berkomposisi resin terkontrol (80% berat) dengan variasi komposisi CaCO3 (0%, 2,5%, 5%, 10%, dan 20% berat). Hasil penelitian menunjukkan komposit hybrid PTJ/Serat Kenaf/CaCO3 (5%wt) memiliki kekuatan tarik dan sifat kekerasan paling tinggi dengan nilai 43 MPa dan 85,50 Shore D. Nilai Kekuatan impak tertinggi diperoleh komposit PTJ/Serat Kenaf (20%wt) dengan nilai 17,6 kJ/m2. Berdasarkan hasil analisis pemindaian SEM, menunjukkan adanya interaksi antar muka yang baik antara penguat dengan matriks.
==============================================================================================================================
Kenaf fiber (Hibiscus Cannabinus L.)-reinforced hybrid composites have been widely developed as an alternative to glass or carbon fiber-reinforced hybrid composites. Calcium carbonate (CaCO3) is a filler that can be used to reinforce composites. The CaCO3 used in this study came from industrial waste. The purpose of this study was to observe the effect of variations in the composition of kenaf fiber and CaCO3 particulate addition, as reinforcing materials, on the mechanical and physical properties of unsaturated polyester hybrid composites. The calcium carbonate-reinforced kenaf fiber/polyester hybrid composites (PTJ/Serat Kenaf/CaCO3) were made using the hand layup method with two composition variations: a controlled resin and kenaf fiber composition (80:20) hybrid composite with varying CaCO3 additions (2.5, 5, 7.5, 10, and 20 parts per hundred ratio), and a controlled resin (80% wt) hybrid composite with varying CaCO3 loading (0%, 2.5%, 5%, 7.5%, 10%, and 20% by weight). Results showed that the PTJ/Serat Kenaf/CaCO3 (5% wt) hybrid composite had the highest tensile strength and hardness, at 43 MPa and 85.50 Shore D, respectively. The highest impact strength was obtained by the PTJ/Serat Kenaf (20% wt) composite, with a value of 17.6 kJ/m². SEM micrograph results show good interfacial adhesion within the filler/matrix hybrid composites.

Item Type:	Thesis (Masters)
Uncontrolled Keywords:	Komposit Hybrid, Serat Kenaf, Serbuk CaCO3, Poliester Tak Jenuh, Karakteristik
Subjects:	T Technology > TL Motor vehicles. Aeronautics. Astronautics > TL240.5 Composite materials T Technology > TL Motor vehicles. Aeronautics. Astronautics > TL671.6. Materials--Fatigue.
Divisions:	Faculty of Industrial Technology > Material & Metallurgical Engineering > 27101-(S2) Master Thesis
Depositing User:	Alfian hudan laksana
Date Deposited:	22 Jul 2026 04:20
Last Modified:	22 Jul 2026 04:20
URI:	http://repository.its.ac.id/id/eprint/67650

Actions (login required)

View Item