Pengaruh Partikel Al2o3 atau Hcl dalam Proses Presipitasi Aluminium Hidroksida terhadap Kualitas Produk Al2o3

Hendrawan, Andreas Ryan (2019) Pengaruh Partikel Al2o3 atau Hcl dalam Proses Presipitasi Aluminium Hidroksida terhadap Kualitas Produk Al2o3. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 02111440000074-Undergraduate_Theses.pdf Restricted to Repository staff only Download (3MB) | Request a copy

Abstract

Alumina memiliki banyak manfaat, salah satunya adalah sebagai bahan baku pembuatan aluminium. Aluminium dari alumina yang memiliki spesifikasi metalurgi yang dihasilkan melalui proses bayer, terhadap bahan baku bauksit. Banyak faktor yang mempengaruhi proses bayer terhadap kandungan dan kualitas dari alumina yang dihasilkan. Ada dua jenis alumina yang dihasilkan melalui proses bayer, yaitu jenis alumina untuk peleburan (smelter grade alumina, SGA), sebagai bahan baku untuk membuat logam aluminium dan jenis untuk bahan kimia (chemical grade alumina, CGA) sebagai bahan baku untuk pembuatan berbagai bahan kimia dan bahan lainnya berbasis aluminium. Dalam penelitian ini meneliti pengaruh dari HCl dan partikel Al2O3 terhadap kandungan alumina yang dihasilkan agar alumina yang dihasilkan dapat memenuhi standar bahan pembuatan aluminium. Alumina yang dihasilkan dari bauksit menggunakan proses bayer. Proses bayer terdiri dari tiga tahap yaitu digestion (pelarutan), presipitasi (pengendapan), dan kalsinasi (pemanasan). Pada proses digestion dilakukan pencampuran bauksit yang sudah digerus dan diayak dengan larutan natrium hidroksida (NaOH) ke dalam steel vial, dipanaskan pada suhu 150oC selama 3 jam. Proses digestion menghasilkan larutan sodium aluminat dan red mud. Selanjutnya larutan sodium aluminat yang dihasilkan digunakan untuk proses presipitasi. Pada proses presipitasi yang dilakukan menggunakan 2 metode untuk mengendapkan aluminium hidrat (Al(OH)3) yaitu dengan menggunakan asam klorida (HCl) dan partikel alumina (Al2O3). Variasi dilakukan pasa saat proses presipitasi yaitu penggunaan 6,8,10,12, dan 14 ml HCl dan 0.2,0.3,0.4,0.5,0.6 gram partikel alumina. Lalu tahap selanjutnya adalah dengan mengkalsinasi endapan aluminium hidrat yang telah dihasilkan pada suhu 200oC selama 3 jam. Berdasarkan penelitian larutan natrium aluminat diperoleh dari pencampuran bauksit dengan larutan NaOH. Larutan natrium aluminat yang diperoleh selanjutnya melalui proses presipitasi menggunakan serbuk alumina atau HCl. Pada proses presipitasi dengan menggunakan serbuk alumina didapatkan hasil bahwa semakin meningkatnya jumlah serbuk alumina yang digunakan, maka semakin banyak endapan Al(OH)3 yang dihasilkan. Persen Al2O3 terbaik diperoleh pada 0.2 gram serbuk alumina yang digunakan yaitu sebesar 90.9%. Pada proses presipitasi dengan menggunakan HCl didapatkan hasil bahwa semakin banyak jumlah HCl yang digunakan, maka semakin banyak endapan Al(OH)3 yang dihasilkan. Persen Al2O3 yang diperoleh dengan menggunakan HCl bersifat fluktuatif. Kadar Al2O3 terbaik diperoleh pada 12 ml HCl terjadi pada pH 10 dengan perolehan persentase alumina sebesar 89.7%.
==================================================================================================================================
Alumina has many benefits, one of which is as a raw material for making aluminum. Aluminum from alumina which has metallurgical specifications produced through the bayer process, on bauxite feedstock. Many factors influence the bayer process on the content and quality of alumina produced. There are two types of alumina produced through the bayer process, namely the type of alumina for smelting (smelter grade alumina, SGA), as a raw material for making aluminum metals and types for chemicals (chemical grade alumina, CGA) as raw material for manufacturing various chemicals and other aluminum-based materials. In this study examined the effect of HCl and Al2O3 particles on the alumina content produced so that the resulting alumina can meet the standards of aluminum-making materials. Alumina produced from bauxite uses the bayer process. The bayer process consists of three stages, namely digestion, precipitation, and calcination. In the digestion process mixing bauxite has been done and sieved with sodium hydroxide (NaOH) solution into a steel vial, heated at 150oC for 3 hours. The digestion process produces sodium aluminate solution and red mud. Furthermore, the resulting sodium aluminate solution is used for the precipitation process. In the precipitation process carried out using 2 methods to precipitate aluminum hydrate (Al (OH)3) by using hydrochloric acid (HCl) and alumina particles (Al2O3). Variations were carried out during the precipitation process using 6,8,10,12 and 14 ml HCl and 0.2,0.3,0,4,0,5,0,6 gram alumina particles. Then the next step is to calcify aluminum hydrate deposits that have been produced at 200oC for 3 hours. Based on the research sodium aluminate solution was obtained from mixing bauxite with NaOH solution. The sodium aluminate solution obtained is then through the precipitation process using alumina powder or HCl. In the process of precipitation using alumina powder, it was found that the higher the amount of alumina powder used, the more Al(OH)3 deposits were produced. The best Al2O3 percentage is obtained at 0.2 grams of alumina powder used, which is 89.7%. In the process of precipitation using HCl, the results show that the more amount of HCl is used, the more Al(OH)3 deposits are produced. Al2O3 percent obtained by using HCl is volatile. The best Al2O3 content obtained at 12 ml HCl occurred at pH 10 with the percentage of alumina obtained at 89.7%.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Alumina, Bauxite, Bayer Process, Chloride Acid, Sodium Hydroxide.
Subjects:	Q Science > QD Chemistry > QD63 Extraction T Technology > TP Chemical technology > TP156 Crystallization. Extraction (Chemistry). Fermentation. Distillation. Emulsions.
Divisions:	Faculty of Industrial Technology > Mechanical Engineering > 21201-(S1) Undergraduate Thesis
Depositing User:	Hendrawan Andreas Ryan
Date Deposited:	21 Jul 2026 06:12
Last Modified:	21 Jul 2026 06:12
URI:	http://repository.its.ac.id/id/eprint/67722

Actions (login required)

View Item