Sintesis Zeolit Y dari Metakaolin dengan Perlakuan Asam Sulfat dan Aplikasinya sebagai Katalis pada Reaksi Esterifikasi

SAFITRI, LELI ENDAH (2019) Sintesis Zeolit Y dari Metakaolin dengan Perlakuan Asam Sulfat dan Aplikasinya sebagai Katalis pada Reaksi Esterifikasi. Masters thesis, Institut Teknologi Sepuluh Nopember.

Text 01211750010017_Master_Thesis.pdf Restricted to Repository staff only Download (3MB) | Request a copy

Abstract

Penelitian ini telah dilakukan sintesis zeolit Y dari kaolin yang dikalsinasi menjadi metakaolin dan aplikasi zeolit Y sebagai katalis pada reaksi esterifikasi. Sintesis zeolit Y terdiri atas proses metakaolinisasi, perlakuan metakaolin dengan asam sulfat dengan variasi konsentrasi 3, 6, 9, 12, dan 15 M, pemeraman dan hidrotermal selama 24 jam pada suhu 100 °C. Padatan hasil sintesis dikarakterisasi dengan difraksi sinar-X (XRD) dan spektroskopi inframerah (FTIR) menunjukkan terbentuknya zeolit NaY. Karakterisasi dengan Scanning Electron Microscopy-Energy Dispersive X-ray (SEM-EDX) menunjukkan bahwa morfologi permukaan zeolit NaY berbentuk oktahedral. Hasil uji keasaman katalis dengan FTIR-piridin menunjukkan jumlah asam tertinggi adalah sampel HY-9 yaitu sebesar 0,26 mmol/g dan adsorpsi-desorpsi N2 dari sampel HY-9 mempunyai luas permukaan 372,28 m2/g. Selain itu, dilakukan pertukaran kation pada NaY sehingga menjadi HY. Uji aktivitas katalitik dari zeolit HY dilakukan dengan reaksi esterifikasi asam asetat dan benzil alkohol dengan perbandingan molar 1:4, waktu reaksi selama 8 jam dan jumlah katalis sebanyak 2,5% berat asam asetat. Hasil konversi asam asetat tertinggi didapatkan pada kondisi reaksi 200 °C dengan katalis HY-9 yaitu sebesar 94,06% dengan metode titrasi.
======================================================================================================================================
This research has carried out the synthesize zeolite Y from kaolin calcined into metakaolin and application of zeolite Y as a catalyst in the esterification reaction. The synthesis of zeolite Y consists of the metakaolinization process, treatment of metakaolin with sulfuric acid using variations of concentrations of 3, 6, 9, 12, and 15 M, aging, and hydrothermal for 24 hours at 100 °C. Solids synthesized which are characterized by X-ray diffraction (XRD) and infrared spectroscopy (FTIR) show the formation of NaY zeolite. Characterization with Scanning Electron Microscopy-Energy Dispersive X-ray (SEM-EDX) showed that the surface morphology of NaY zeolite was octahedral. The acidity test results of the catalyst with FTIR-pyridine showed the highest amount of acid was the HY-9 sample of 0.26 mmol/g and N2 adsorption-desorption from the HY-9 sample had a surface area of 372.28 m2/g. In addition, a cation exchange was carried out on NaY to become HY. Catalytic activity of zeolite HY was carried out by esterification reaction of acetic acid and benzyl alcohol with 1: 4 molar ratio, reaction time for 8 hours and catalyst amount of 2.5% by weight of acetic acid. The highest conversion of acetic acid (94,06%) were obtained at the reaction conditions of 200 °C using a HY-9 catalyst by titration method.

Item Type:	Thesis (Masters)
Uncontrolled Keywords:	Kaolin, Metakaolin, Zeolit Y, Katalis HY, Reaksi Esterifikasi
Subjects:	Q Science Q Science > QD Chemistry Q Science > QD Chemistry > QD501 Catalysis. Catalysts.
Divisions:	Faculty of Natural Science > Chemistry > 47101-(S2) Master Thesis
Depositing User:	Safitri Leli Endah
Date Deposited:	20 Jul 2026 07:04
Last Modified:	20 Jul 2026 07:04
URI:	http://repository.its.ac.id/id/eprint/68282

Actions (login required)

View Item