Analisis Pengaruh Variasi Heat Input dan Debit Gas Pelindung Pengelasan FCAW pada Sambungan Baja BKI Grade A Terhadap Sifat Mekanik

Yuniarto, M. Ichsan Rosidin (2019) Analisis Pengaruh Variasi Heat Input dan Debit Gas Pelindung Pengelasan FCAW pada Sambungan Baja BKI Grade A Terhadap Sifat Mekanik. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

Text 04311540000014-Undergraduate_Thesis.pdf Restricted to Repository staff only Download (7MB) | Request a copy

Abstract

Kegiatan eksplorasi minyak dan gas di laut membutuhkan fasilitas anjungan lepas pantai khususnya berupa struktur terapung, karena dapat berpindah tempat sesuai kebutuhan. Salah satu rangkaian pekerjaan untuk memproduksi struktur lepas pantai tersebut adalah proses pengelasan. FCAW merupakan proses pengelasan yang cocok untuk kegiatan fabrikasi karena memiliki tingkat produktivitas yang tinggi. Tujuan penelitian ini adalah untuk mengetahui pengaruh variasi heat input dan debit gas pelindung terhadap kekuatan tarik dan pengamatan struktur makro-mikro pada pengelasan baja BKI Grade A dengan metode pengelasan FCAW. Variasi heat input yang digunakan pada penelitian ini adalah 1,19 KJ/mm, 1,32 KJ/mm, dan 1,46 KJ/mm, serta variasi debit gas pelindung yang digunakan adalah 18 l/min, 20 l/min, dan 22 l/min. Pada hasil pengujian kekuatan tarik, pengelasan yang dilakukan dengan menggunakan heat input 1,46 Kj/mm dan debit gas pelindung 22 l/min memiliki nilai kekuatan tarik terbesar yaitu ultimate strength 468,14 MPa dan yield strength 349,96 MPa. Hasil pengamatan struktur makro menunjukkan bahwa pengelasan dengan heat input 1,46 KJ/mm dan debit gas pelindung 18 l/min memiliki lebar daerah HAZ terlebar yaitu sebesar 20 mm. Pada hasil pengamatan struktur mikro, spesimen pengelasan dengan nilai heat input 1,46 KJ/mm dan debit gas pelindung 22 l/min memiliki presentase fase ferrite terkecil pada bagian weld metal nya yaitu sebesar 54,4% kemudian pearlite sebesar 45,6%.
============================================================================ Oil and gas exploration activities in the sea require offshore platform facilities especially in the form of floating structure, because it can move as needed. One of the series of works to produce floating offshore structure is welding process. FCAW is a welding process that is suitable for fabrication activities because it had a high level of productivity. The purpose of this study was to determine the influence of variation in heat and flow rate of shielding gas on tensile strength and macro-microstructure observation at weldjoint of BKI grade A steel using FCAW welding process. The variation of heat input used in this study are 1.19 KJ/mm, 1.32 KJ/mm, and 1.46 KJ/mm, and flow rate of shielding gas variation are 18 l/min, 20 l/min, and 22 l/min. On the tensile strength test result, weldjoint using 1.46 KJ/mm heat input and 22 l/min shielding gas flow rate had the highest tensile strength value that were 468.14 MPa on ultimate strength and 349.96 MPa on yield strength. The result of macrostructure observation showed weldjoint with 1.46 KJ/mm heat input and 18 l/min shielding gas flow rate had the widest HAZ area of 20 mm. On the microstructure observation result, welding specimen that used 1.46 KJ/mm heat input and 22 l/min flow rate of shielding gas had the smallest percentage of ferrite phase in the weld metal area, that was 54.4% then 45.6% pearlite.

Item Type:	Thesis (Undergraduate)
Uncontrolled Keywords:	Baja BKI grade A, Flux Cored Arc Welding, Heat Input, Debit Gas Pelindung, Kekuatan Tarik, Struktur Makro-Mikro
Subjects:	T Technology > TC Hydraulic engineering. Ocean engineering > TC1665 Offshore structures--Materials.
Divisions:	Faculty of Marine Technology (MARTECH) > Ocean Engineering > 38201-(S1) Undergraduate Thesis
Depositing User:	M. Ichsan Rosidin Yuniarto
Date Deposited:	04 Jun 2026 02:36
Last Modified:	04 Jun 2026 02:37
URI:	http://repository.its.ac.id/id/eprint/68296