Perbandingan Laju Korosi Substrat Baja Karbon ST41 Dengan Pelapis Bahan Nikel dan Krom Dengan SS 316L Untuk Bahan Implan Tulang

Dasaad, Muhammad Dimitrie Arsenna (2019) Perbandingan Laju Korosi Substrat Baja Karbon ST41 Dengan Pelapis Bahan Nikel dan Krom Dengan SS 316L Untuk Bahan Implan Tulang. Diploma thesis, Institut Teknologi Sepuluh Nopember.

Text 10211600000059-Non_Degree.pdf Restricted to Repository staff only Download (7MB) | Request a copy

Abstract

Salah satu jenis bahan yang biasa digunakan dalam pembuatan alat-alat implan tulang adalah SS 316L. Dalam penerapannya SS 316L terbilang mahal. Untuk mendapatkan harga yang lebih terjangkau maka pada bahan dasar pembuatannya dilakukan pergantian, dengan resiko ketahanan yang berbeda. Untuk mengetahui ketahanan korosi dengan bahan yang berbeda maka dilakukan penelitian ini. Dalam penelitian ini material yang digunakan adalah baja ST41 yang dilapisi oleh nikel dan krom dalam larutan Simulated Body Fluid sebagai media korosif dan dilakukan perbandingan laju korosi nya dengan SS 316L. Jenis pengujian yang dilakukan pada penelitian kali ini adalah Polarisasi potensiodinamik dengan metode tafel dan weight loss. Hasil pengujian menunjukkan adanya penurunan laju korosi yang signifikan pada baja ST41 yang dilapisi dengan nickel chrome (NiCr) dalam larutan Simulated Body Fluid (SBF) ketika telah dilakukan proses perendaman selama 7 hari. Pada pengujian Polarisasi Potensiodinamik laju korosi pada hari ke 7 adalah 4,7329x10-4 mm/year dengan pelapis NiCr dan 5,2665x10-3 mm/year untuk SS 316L. Maka laju korosi ST41 pelapis NiCr setelah melewati 7 hari perendaman lebih rendah dibandingkan SS 316L.
===================================================================================================================================
One type of material commonly used in making bone implant devices is SS 316L. In its applications SS 316L is quite expensive. In order to get a more affordable price, the basic materials are changed but with different resistance. To find out the corrosion resistance with different materials, this study was conducted. In this study the material used was ST41 coated with nickel and chrome in a Simulated Body Fluid solution as a corrosive medium and do a comparison of the corrosion rate with SS 316L. The type of test in this study was potentiodynamic polarization with the tafel method and weight loss. The test results showed a significant reduction of corrosion rate in ST41 coated with Nickel Chrome in SBF solution when the immersion process was carried out for 7 days. In the Potentiodynamic Polarization test the corrosion rate on day 7 was 4.7329x10-4 mm/year for NiCr coatings and 5.2665x10-3 mm/year for SS 316L. So the corrosion rate of ST41 with NiCr coating after passing 7 days of immersion is lower than SS 316L.

Item Type:	Thesis (Diploma)
Uncontrolled Keywords:	ST 41 Steel, SS 316L, Corrosion Rate, SBF, Nickel Chrome, Potentiodynamic Polarization, Weight loss
Subjects:	T Technology > TA Engineering (General). Civil engineering (General) > TA418.74 Corrosion and anti-corrosives
Divisions:	Faculty of Vocational > Mechanical Industrial Engineering (D4)
Depositing User:	Dasaad Muhammad Dimitrie Arsenna
Date Deposited:	13 Aug 2026 04:07
Last Modified:	13 Aug 2026 04:07
URI:	http://repository.its.ac.id/id/eprint/68740

Actions (login required)

View Item