Abstract

Karbondioksida (CO2) merupakan salah satu gas yang diketahui sebagai sumber utama dari efek pemanasan global. Pada penelitian ini karbondioksida telah berhasil disintesis menjadisenyawa lain yang memiliki nilai tambah yaitu Diethyl carbonate (DEC) dan Dimethyl carbonate (DMC). Senyawa DEC dan DMC pada penelitian ini disintesis dari CO2, etanol maupun metanol dengan reaksi langsung menggunakan reaktor yang dilengkapi dengan pemanas pada bagian luarnya. Reaksi ini berlangsung dengan menggunakan katalis homogen ataupun heterogen. Kondisi operasi yang digunakan dalam penelitian ini adalah tekanan awal 35 bar dan suhu reaksi 170oC. Pada penelitian ini pengaruh jenis agen pendehidrasi (epoksida) yaitu propilen oksida dan butilen oksida juga diinvestigasi. Produk dari sintesis ini kemudian dianalisa dengan Gas Chromatography serta Gas Chromatography – Mass Spectrometry. Dari hasil penelitian ini didapatkan yield maksimum DEC sebesar 31,77% pada penggunaan propilen oksida sebagai agen pendehidrasi dan katalis KI-Zeolite dalam waktu 2 jam dan yield DMC sebesar 46,88% pada penggunaan butilen oksida sebagai agen pendehidrasi serta katalis KI-Zeolite.
=====================================================================================================================================
Carbon dioxide (CO₂) is one of the gases known as a major contributor to global warming. In this study, carbon dioxide was successfully converted into higher-value compounds, namely diethyl carbonate (DEC) and dimethyl carbonate (DMC). The DEC and DMC compounds were synthesized from CO₂, ethanol, and methanol through a direct reaction using a reactor equipped with an external electric heater. The reaction was carried out using either homogeneous or heterogeneous catalysts. The operating conditions used in this study were an initial pressure of 35 bar and a reaction temperature of 170°C. The effects of different types of dehydration agents (epoxides), namely propylene oxide and butylene oxide, were also investigated. The products obtained from the synthesis were analyzed using Gas Chromatography (GC) and Gas Chromatography–Mass Spectrometry (GC-MS). The results showed that the maximum DEC yield was 31.77% when propylene oxide was used as the dehydration agent with a KI/zeolite catalyst for 2 hours, while the maximum DMC yield was 46.88% when butylene oxide was used as the dehydration agent with a KI/zeolite catalyst.

Item Type:	Thesis (Masters)
Uncontrolled Keywords:	Karbondioksida, bahan bakar, epoksida, katalis homogen, katalis heterogen, dialkyl carbonate
Subjects:	Q Science > QD Chemistry > QD501 Catalysis. Catalysts. T Technology > TP Chemical technology > TP339 Ethanol as fuel. Biomass energy.
Divisions:	Faculty of Industrial Technology > Chemical Engineering > 24101-(S2) Master Thesis
Depositing User:	Anggerta Lintang Alivia
Date Deposited:	22 Jul 2026 01:59
Last Modified:	22 Jul 2026 01:59
URI:	http://repository.its.ac.id/id/eprint/69173

Actions (login required)

View Item