Komposit ZSM-5-TiO2 termodifikasi karbon telah disintesis dengan metode sol-gel. Prekursor yang digunakan adalah Titanium (IV) Isopropoksida. Variasi pelarut yang digunakan adalah isopropanol, benzena dan toluena. Hasil sintesis dikarakterisasi dengan FTIR, XRD, dan SEM. Hasil karakterisasi XRD menunjukkan puncak karakteristik TiO2 muncul pada 2θ = 5,47o (I-ZTC); 25,13o (B-ZTC) dan 25,17o (T-ZTC). Hasil karakterisasi FTIR menunjukan pita serapan dari I-ZTC, B-ZTC, dan T-ZTC yang serupa dengan pita serapan ZSM-5 di sekitar bilangan gelombang 7,85 cm-1; 8,69 cm-1; 22,97 cm-1; 23,29 cm-1; dan 23,84 cm-1. Hasil FTIR juga menunjukkan pita serapan di sekitar bilangan gelombang 450 cm-1 yang menunjukkan vibrasi ulur Ti-O. Hasil karakterisasi SEM-EDX menunjukkan persebaran Ti lebih merata pada permukaan T-ZTC dibandingkan B-ZTC dan I-ZTC. Hal tersebut menunjukkan kepolaran pelarut mempengaruhi persebaran TiO2. Pelarut yang kepolarannya lebih rendah menunjukkan persebaran TiO2 yang lebih merata dibandingkan persebaran TiO2 pada pelarut yang kepolarannya lebih tinggi. Toluena adalah pelarut yang memiliki persebaran TiO2 paling merata untuk sintesis ZSM-5-TiO2 termodifikasi karbon.
===================================================================================================================================
Carbon-modified ZSM-5-TiO2 composite has been synthesized using the sol-gel method. The precursor used was Titanium (IV) Isopropoxide. Variations of solvents used were isopropanol, benzene, and toluene. The synthesized results were characterized by FTIR, XRD, and SEM. The XRD characterization results showed that the characteristic peaks of TiO2 appeared at 2θ = 5.47o (I-ZTC); 25.13o (B-ZTC) and 25.17o (T-ZTC). FTIR characterization results showed absorption bands of I-ZTC, B-ZTC, and T-ZTC similar to the absorption bands of ZSM-5 around wavenumbers 7.85 cm-1; 8.69 cm-1; 22.97 cm-1; 23.29 cm-1; and 23.84 cm-1. FTIR results also showed an absorption band around wavenumber 450 cm-1 indicating Ti-O stretching vibration. SEM-EDX characterization results showed that the distribution of Ti was more even on the surface of T-ZTC compared to B-ZTC and I-ZTC. This indicates that solvent polarity affects the distribution of TiO2. Solvents with lower polarity show a more even distribution of TiO2 compared to the distribution of TiO2 in solvents with higher polarity. Toluene is the solvent with the most even TiO2 distribution for the synthesis of carbon-modified ZSM-5-TiO2.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	morfologi, komposit, ZSM-5-TiO2, isopropanol, benzena, toluena
Subjects:	Q Science Q Science > QD Chemistry
Divisions:	Faculty of Natural Science > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User:	Ursula Aska Novitasari
Date Deposited:	20 Jul 2026 06:07
Last Modified:	20 Jul 2026 06:07
URI:	http://repository.its.ac.id/id/eprint/69274

Actions (login required)

View Item