Pengaruh Variasi Volume Air Terhadap NIlai Kekerasan, Makro Dan Mikro Etsa pada SUS 304 Dengan Metode Pengelasan SMAW Menggunakan Elektroda 308L

Izziddin, Muhammad Hafizh (2019) Pengaruh Variasi Volume Air Terhadap NIlai Kekerasan, Makro Dan Mikro Etsa pada SUS 304 Dengan Metode Pengelasan SMAW Menggunakan Elektroda 308L. Diploma thesis, Institut Teknologi Sepuluh Nopember.

Text 10211600000099_Undergraduate_Thesis.pdf Restricted to Repository staff only Download (5MB) | Request a copy

Abstract

Pembangunan konstruksi dengan menggunakan logam pada masa sekarang ini banyak melibatkan unsur pengelasan khususnya bidang rancang bangun karena sambungan las merupakan salah satu pembuatan sambungan yang secara teknis memerlukan keterampilan yang tinggi bagi pengelas, agar di peroleh sambungan dengan kualitas baik. Pada penelitian ini akan menganalisa mengenai variasi volume air 18L, 36L dan 54L pada laju pendinginan setelah dilakukan pengelasan SMAW menggunakan NSN-308L berdiameter 3,2. Dalam penelitian ini dilakukan pengujian kekerasan untuk mengetahui nilai kekerasan pada titik pasti batas antara Base Metal, HAZ dan Weld Metal. Dan Pengujian Metalography (Mikro dan Makro) untuk mengetahui lebar HAZ. Hasil penelitian yang di dapatkan pada pengujian kekerasan, di dapat nilai paling besar pada spesimen dengan variasi volume 54L di daerah HAZ yaitu 99.5 HRB. Karena semakin banyak volume air maka nilai kekerasan akan semakin tinggi . Untuk pengujian hasil makro, HAZ terlebar didapat pada spesimen tanpa laju pendinginan air dengan lebar 4.8 mm, Untuk mikro etsa terdapat Carbida Chrome tertinggi terdapat pada specimen tanpa laju pendinginan air yaitu sebesar 4.982%.
=================================================================================================================================
Nowadays building construction using metal involves a lot of welding elements, especially in the design, because the weld joint is one of the connections that technically require high skill for the welder in order to get the good quality of the connection. In this research, the volume variation of 18L, 36L, and 54L will be analyzed at the cooling rate after SMAW welding using NSN-308L with a diameter of 3.2. The hardness test was also conducted to find the hardness point at the exact point of the boundary between Base Metal, HAZ, and Weld Metal, also Metallography Test (both Micro and Macro) to find the width of HAZ. The results obtained in the hardness test, obtained the greatest value in the specimen with a variation of 54L volume in the HAZ area of 99.5 HRB. Because the more volume of water the higher the value of violence. For testing macro results, the widest HAZ was obtained in specimens without a water-cooling rate of 4.8 mm in width, for micro etching there was the highest Chrome Carbide found in specimens without a water-cooling rate of 4,982%.

Item Type:	Thesis (Diploma)
Uncontrolled Keywords:	Cooling rate, hardness test, macro and micro-etching Metallography Test.
Subjects:	T Technology > TS Manufactures
Divisions:	Faculty of Vocational > Mechanical Industrial Engineering (D4)
Depositing User:	Izziddin Muhammad Hafizh
Date Deposited:	13 Aug 2026 07:23
Last Modified:	13 Aug 2026 07:23
URI:	http://repository.its.ac.id/id/eprint/70309

Actions (login required)

View Item