Pengaruh Bentuk V Groove Dan Bevel Groove Metode Multilayer Pengelasan Gtaw Dengan Filler Er-70s 6 Pada Material Sa 36 Terhadap Kekuatan Tarik, Kekerasan Dan Lebar Haz

PUTRA, ANNEDY EGA DIPHASYAH (2019) Pengaruh Bentuk V Groove Dan Bevel Groove Metode Multilayer Pengelasan Gtaw Dengan Filler Er-70s 6 Pada Material Sa 36 Terhadap Kekuatan Tarik, Kekerasan Dan Lebar Haz. Diploma thesis, Institut Teknologi Sepuluh Nopember.

Text 10211600000114-Undergraduate_Thesis.pdf Restricted to Repository staff only Download (6MB) | Request a copy

Abstract

Di zaman modern ini kemajuan teknologi sekarang sangatlah maju. Perkembangan teknologi yang pesat inilah harus diimbangi oleh sumber daya manusia yang ada. perkembangan teknologi pengelasan merupakan suatu jenis teknologi yang sering digunakan dalam proses manufaktur. Dalam hal ini dasarnya adalah efisiensi yang tinggi, biaya yang murah, penghematan tenaga, dan penghematan energi. Mutu dari hasil pengelasan tergantung dari pengerjaan lasnya sendiri dan juga sangat tergantung dari persiapan sebelum pelaksanaan pengelasan. Salah satu factor yang mempengaruhi adalah pemilihan jenis groove yang tepat. Dalam tugas akhir ini pengelasan yang digunakan las GTAW. Salah satu jenis sambungan las yang perlu dikaji lebih lanjut adalah sambungan las dengan bentuk V groove dan Bevel groove dengan metode multilayer menggunakan elektroda ER-70S 6 pada material plat SA 36. Selanjutnya untuk mengetahui hasil pengelasan dari kedua bentuk groove tersebut dengan mengamati hasil uji makro etsa, uji kekerasan dan uji tarik. Dari pengujian yang telah dilakukan pengelasan V groove dan Bevel groove dengan metode multilayer pada pengelasan GTAW menggunakan elektroda ER-70S 6 menghasilkan lebar HAZ dari uji makro etsa pada pengelasan V groove lebih besar dibandingkan Bevel groove. Untuk hasil pengujian kekerasan, spesimen Bevel groove memiliki nilai kekerasan lebih tinggi dibandingkan spesimen V groove yaitu dengan nilai 90 HRB pada weld metal dan 87 HRB pada HAZ. Dan pada hasil pengujian tarik antara spesimen V groove dengan Bevel groove dengan metode multilayer semua spesimen patah pada lokasi base metal.
====================================================================================================================================
At this time welding technique has been used very frequent for attaching or connecting on construction steel for instance on maintenance or production processes. In this case the underlying are high efficiency, low cost, and energy savings. The quality of the welding result determined by the welding processes and also on welding preliminaries prior to welding process. Either of the factors that affects is to correctly specify the groove. On this thesis GTAW weld will be utilized. One of the joint types that needed further studied are weld joint with V groove and Bevel groove with multilayer method using ER70S 6 electrode on SA 36 plate material. Furthermore, to quantify the welding product on either groove types are by analyzing macro etching result, hardness test and tensile test. From the test that has been conducted on weld joint either V groove and Bevel groove with multilayer method on GTAW weld using ER-70S6 electrode achieving HAZ width form macro etching test on which V groove has bigger with than Bevel groove. From hardness test Bevel groove specimen has higher hardness value than V groove specimen with 90 HRB on weld metal, and 87 HRB on HAZ. Next on tensile test between V groove specimen and Bevel groove specimen using multilayer method both of the specimen fail on base metal location.

Item Type:	Thesis (Diploma)
Uncontrolled Keywords:	Pengelasan GTAW, Multi Layer, V groove, Bevel groove, lebar HAZ, Uji Kekerasan, Uji Tarik.
Subjects:	T Technology > TS Manufactures T Technology > TS Manufactures > TS227 Welding.
Divisions:	Faculty of Vocational > Mechanical Industrial Engineering (D4)
Depositing User:	Annedy Ega Diphasyah Putra
Date Deposited:	13 Aug 2026 06:33
Last Modified:	13 Aug 2026 06:33
URI:	http://repository.its.ac.id/id/eprint/70371