Pengaruh Pemotongan Sejajar Dan Tegak Lurus Arah Roll Plat A 36 Pada Sambungan Las Smaw Dengan Elektroda E7018 Terhadap Kekuatan Tarik, Kekuatan Kekerasan, Dan Mikro Etsa

Aji, Rizza Bagus Setya (2019) Pengaruh Pemotongan Sejajar Dan Tegak Lurus Arah Roll Plat A 36 Pada Sambungan Las Smaw Dengan Elektroda E7018 Terhadap Kekuatan Tarik, Kekuatan Kekerasan, Dan Mikro Etsa. Diploma thesis, INSTITUT TEKNOLOGI SEPULUH NOPEMBER.

Text 102116000000015-Undergraduate_Thesis.pdf Restricted to Repository staff only Download (5MB) | Request a copy

Abstract

Pada penyambungan baja tentu diperlukan suatu proses dan salah satunya pengelasan. Pengelasan sendiri merupakan salah satu proses yang cukup berperan dalam industri manufaktur dengan tujuan untuk proses maintenance maupun proses produksi pada proses pembuatan baja dapat dilakukan proses pengerollan maka dari itu arah pemotongan pada pengerollan dapat mempengaruhi sambungan pengelasan. Dalam tugas akhir ini pengelasan yang digunakan las SMAW. jenis variasi yang digunakan adalah variasi arah pemeotongan pada baja yang telah dilakukan pengerolollan baja yang digunakan adalah ASTM A36. Selanjutnya untuk mengetahui kekuatan sambungan dari kedua bentuk variasi tersebut dengan menggunakan pengujian Tarik, kekerasan, dan mikro etsa. Dari hasil pengujian tarik antara spesimen yang di variasi arah Pengerollan Horizontal memiliki kekuatan tarik lebih besar yaitu 476 N/mm2 sedangkan spesimenn yang sudah di varisai dengan arah Pengerollan Vertikal memiliki kekuatan tarik lebih rendah yaitu 466,33 N/mm2. Daerah patahan terdapat pada Base Metal dan dilihat dari bentuk patahan spesimen, dapat dikatakan bahwa material bersifat ductile. Berdasarkan hasil uji kekerasan. Nilai kekerasan pada spesimen yang di variasi arah pengerollan horizontal lebih besar untuk spesimen yang yang sudah divarisai dengan arah vertikal memiliki nilai lebih rendah.Untuk semua spesimen daerah yang memiliki nilai kekerasan paling tinggi terdapat pada daerah sekitaran Weld Metal dan HAZ sedangkan paling rendah terletak pada daerah Base Metal. Hasil pada hasil mikro yang dapat dilihat adalah struktur mikro dari ferrit dan pearlit.
===========================================================================================================================
connection with steel, of course, a process is needed and one of them is welding. Welding itself is one of the processes that are quite instrumental in the manufacturing industry with the aim of the maintenance process and the production process in the steel making process can be carried out by the pulverizing process so that the cutting direction on the roller can affect the welding connection. In this final project the welding used by SMAW welding. the type of variation used is the variation in the direction of cutting on steel which has been carried out in the rolling steel used is ASTM A36. Furthermore, to determine the connection strength of the two forms of variation using tensile, hardness, and micro etching tests. From the results of tensile testing between specimens in the direction of Pengerollan Horizontal variation has a greater tensile strength of 476 N / mm2 while the specimens that have been varicated with Vertical Grinding direction have a lower tensile strength of 466.33 N / mm2. The fault area is found on the Base Metal and seen from the shape of the fracture of the specimen, it can be said that the material is ductile. .Based on the results of the hardness test. The hardness values in specimens which are varied in direction of horizontal bending are greater for specimens that have been vertically aligned with lower values. For all regional specimens that have the highest hardness values are found in the area around Weld Metal and HAZ while the lowest is in the area Metal Base. The results of the micro results that can be seen are the microstructure of ferrite and pearlite.

Item Type:	Thesis (Diploma)
Uncontrolled Keywords:	Pengelasan, SMAW, ASTM A36, Arah pengerollan baja
Subjects:	T Technology > TS Manufactures > TS227 Welding.
Divisions:	Faculty of Industrial Technology > Mechanical Engineering > 21401-(D3) Diploma 3
Depositing User:	rizza bagus setya aji
Date Deposited:	25 Sep 2024 07:10
Last Modified:	13 Aug 2026 04:06
URI:	http://repository.its.ac.id/id/eprint/70867