Sintesis K0,5na0,5vo3 Dengan Metode Reaksi Padat, Sifat Dielektrik Dan Potensi Sebagai Cofiring Agent

Sambanyu, Alfian Putra (2016) Sintesis K0,5na0,5vo3 Dengan Metode Reaksi Padat, Sifat Dielektrik Dan Potensi Sebagai Cofiring Agent. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img] Text
1112100002-undergraduate-theses.pdf - Published Version

Download (951kB)
[img] Text
1112100002-paperpdf.pdf - Published Version

Download (272kB)
[img] Text
1112100002-presentationpdf.pdf - Published Version

Download (772kB)

Abstract

Sintesis material K0,5Na0,5VO3 (KNV) telah berhasil dilakukan dengan metode reaksi padat. Penentuan suhu kalsinasi dan suhu sintering material ini didasarkan pada titik leleh vanadium oksida yaitu sekitar 690°C sehingga didapatkan suhu kalsinasi 500°C dan suhu sintering 500°C dan 525°C selama masing-masing 2 jam. Hal ini dibuktikan dengan hasil refinement pengujian XRD material KNV yaitu memiliki fasa tunggal dengan struktur monoklinik dan grup ruang C2/c. Densitas terukur dari KNV 525 adalah 3,03 g/cc, sedangkan untuk KNV 500 adalah 3,25 g/cc. Pelet KNV yang telah disintering kemudian dilakukan pengujian sifat listrik dengan menggunakan Impedance Analyser “Solartron”. Material KNV 525 dan KNV 500 cocok untuk diaplikasikan sebagai material dielektrik pada daerah frekuensi yang tinggi. Material KNV 525 memiliki faktor kualitas yang lebih baik daripada KNV 500. Daerah transisi antara polarisasi muatan ruang dengan polarisasi dipol untuk KNV 525 berada pada frekuensi 20 kHz, sedangkan untuk KNV 500 berada pada frekuensi 1,2 MHz. Material KNV dapat digunakan sebagai co-firing agent pada bahan dielektrik keramik. =========================================================== Materials K0.5Na0.5VO3 has been successfully synthesized by solid state reaction. The calcine and sintering temperature is based on the melting point of vanadium oxide which is about 690°C, so that we get suitable calcine temperature is 500°C and sintering temperature is 500°C and 525°C with 2 hours holding time. It has been proved with the refinement of XRD result that KNV material has single phase crystal with a monoclinic structure and C2/c space group. The measuring density for KNV 525 and KNV 500 sequentially is 3.03 gr/cc and 3.25 gr/cc. To measure dielectric properties of KNV pellets disc was using Impedance Analyser “Solartron”. The KNV 500 and KNV 525 is suitable for high-frequency dielectric material applications. KNV 525 has better quality factor than KNV 500. The transition area between space charge polarization and dipole polarization for KNV 525 is at 20 kHz and 1.2 MHz for KNV 500. The KNV materials can be use as co-firing agent of dielectric ceramics materials.

Item Type: Thesis (Undergraduate)
Additional Information: RSFi 620.195 Sam s
Uncontrolled Keywords: co-firing agent, dielektrik, reaksi padat, vanadium oksida
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA418.9 Composite materials
Divisions: Faculty of Science > Physics > (S1) Undergraduate Theses
Depositing User: EKO BUDI RAHARJO
Date Deposited: 16 Oct 2019 02:12
Last Modified: 16 Oct 2019 02:12
URI: http://repository.its.ac.id/id/eprint/71200