Analisis Fasa, Sifat Magnetik, Dan Penyerapan Gelombang Mikro Bahan Serbuk Magnetit (Fe3o4)-Semen Portland Tipe I

Oktafiana, Tri (2016) Analisis Fasa, Sifat Magnetik, Dan Penyerapan Gelombang Mikro Bahan Serbuk Magnetit (Fe3o4)-Semen Portland Tipe I. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 1112100068-undergraduate-theses.pdf]
Preview
Text
1112100068-undergraduate-theses.pdf - Published Version

Download (1MB) | Preview

Abstract

Penelitian ini menggunakan serbuk magnetit (Fe3O4) dan
semen Portland tipe 1 sebagai bahan pelapis permukaan
bangunan yang dapat menyerap gelombang mikro. Campuran
kedua bahan dikarakterisasi menggunakan X-ray Diffractometer
(XRD), X-ray Fluorescence (XRF), Vibrating Sample
Magnetometer (VSM) dan Vector Network Analyzer (VNA)
dengan variasi perbandingan konsentrasi antara serbuk magnetit
(Fe3O4) dan semen Portland tipe 1 yaitu 5:1, 3:1, 1:1, 1:3, dan
1:5. Dari hasil karakterisasi diperoleh sifat magnetik yang besar
yaitu dengan nilai saturasi magnetik dan remanensi magnetik
masing-masing sebesar 38,74 emu/gr dan 16,24 emu/gr untuk
perbandingan 5:1 dengan jumlah serbuk magnetit (Fe3O4) yang
lebih banyak, sedangkan penyerapan gelombang mikro paling
besar adalah pada perbandingan 3:1 dengan nilai reflection loss
sebesar -19,15 dB pada frekuensi 8,24 GHz. Sebagai bahan
pelapis bangunan, perbandingan konsentrasi serbuk magnetit
(Fe3O4) dan semen Portland tipe 1 yang paling efektif untuk
menyerap gelombang mikro adalah 3:1 karena merupakan
perbandingan paling baik untuk pelapis permukaan bangunan.
==========================================================
This research using magnetite (Fe3O4) powder and type I
Portland cement as building surface coating material that can
absorb microwave. A mixture of two materials was characterized
by X-ray Diffractometer (XRD), X-ray Fluorescence (XRF),
Vibrating Sample Magnetometer (VSM) and Vector Network
Analyzer (VNA) with variation of the ratio concentration of
magnetite (Fe3O4) powder and type I Portland cement that is 5:1,
3:1, 1:1, 1:3, and 1:5. Characterization result show that the
highest magnetic properties with value of magnetic saturation and
magnetic remanence of each 38,74 emu/gr and 16,24 emu/gr for
ratio 5:1 with concentration of magnetite powder more than
Portland cement, while the highest absorption of microwave is in
ratio 3:1 with reflection loss value -19,15 dB at frequency 8,24
GHz. As a coating material of building, magnetite powder and
Portland cement ratio is 3:1 because it is the best ratio for
coating the building surface.

Item Type: Thesis (Undergraduate)
Additional Information: RSFi 620.118 Tri a
Uncontrolled Keywords: Gelombang mikro, magnetit, pelapis bangunan, semen portland, sifat magnetik.
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA462 Metal Corrosion and protection against corrosion
Divisions: Faculty of Mathematics and Science > Physics > 45201-(S1) Undergraduate Thesis
Depositing User: EKO BUDI RAHARJO
Date Deposited: 21 Oct 2019 07:25
Last Modified: 21 Oct 2019 07:25
URI: http://repository.its.ac.id/id/eprint/71301

Actions (login required)

View Item View Item