Kombinasi Ekstrak Daun Eceng Gondok Dengan Ekstrak Daun Jambu Biji Sebagai Inhibitor Organik Pada Baja API 5L Grade B Dalam Larutan HCl 1M Dengan Menggunakan Varian Temperatur Dan Variasi Konsentrasi

Wicaksono, Adhi (2019) Kombinasi Ekstrak Daun Eceng Gondok Dengan Ekstrak Daun Jambu Biji Sebagai Inhibitor Organik Pada Baja API 5L Grade B Dalam Larutan HCl 1M Dengan Menggunakan Varian Temperatur Dan Variasi Konsentrasi. Diploma thesis, Institut Teknologi Sepuluh Nopember.

Text 10211500000130-Undergraduate_Thesis.pdf Restricted to Repository staff only Download (3MB) | Request a copy

Abstract

Baja merupakan salah satu material yang tidak bisa dipisahkan dari dunia industri. Jenis baja yang sering digunakan dalam dunia industri yaitu baja karbon. Baja karbon sering digunakan karena memiliki kekerasan yang tinggi dan kekuatan material yang baik. Pipa baja pada industri sering terkena kontak langsung dengan air, udara, serta zat-zat yang mengalir di dalamnya, sehingga korosi pada baja sangat sulit untuk dihindari. Penelitian yang dilakukan terdiri dari dua jenis, yaitu pengujian pengaruh variasi temperatur pada green inhibitor dan mekanisme inhibisi pada green inhibitor daun tumbuhan eceng gondok. Pada penelitian ini dilakukan dengan beberapa variasi temperatur, yaitu 30°C, 40°C, dan 50°C, serta kombinasi inhibitor di antaranya ekstrak daun eceng gondok dengan daun jambu biji yang digunakan dengan perbandingan 30 ml : 70 ml; 50 ml : 50 ml; dan 70 ml : 30 ml, dengan menggunakan media korosi HCl 1M. Untuk mengetahui pengaruh konsentrasi inhibitor pada material baja, dilakukan pengujian EIS (Electrochemical Impedance Spectroscopy) dan PDP (Potentiodynamic Polarization), sedangkan untuk mengetahui laju korosi dilakukan dengan metode pengujian Weight Loss. Efisiensi tertinggi pada pengujian polarisasi potensiodinamik pada temperatur 50°C terletak pada kombinasi konsentrasi eceng gondok 50 ml dan daun jambu biji 50 ml, yaitu sebesar 95,48%. Efisiensi tertinggi pada pengujian EIS pada temperatur 50°C terletak pada kombinasi konsentrasi eceng gondok 30 ml : daun jambu biji 70 ml. Pada pengujian weight loss, efisiensi tertinggi yaitu sebesar 77,235%, terletak pada perendaman 4 jam dengan kombinasi konsentrasi inhibitor eceng gondok 50 ml dan daun jambu biji 50 ml. Mekanisme inhibisi dari kombinasi inhibitor ini yang terjadi bersifat lebih dominan anodik.
==============================================================================================================================
Steel is one of the materials that cannot be separated from the industrial world. The type of steel that is often used in the industrial world is carbon steel. Carbon steel is often used because it has high hardness and good material strength. Steel pipes in industry are often exposed to direct contact with water, air, and substances flowing through them, so that corrosion in steel is very difficult to avoid. The research conducted consisted of two types, namely testing the effect of temperature variations on green inhibitors and examining the inhibition mechanism of green inhibitors derived from water hyacinth plant leaves. In this study, several temperature variations were used, namely 30°C, 40°C, and 50°C, along with a combination of inhibitors consisting of water hyacinth leaf extract and guava leaf extract used in ratios of 30 ml : 70 ml; 50 ml : 50 ml; and 70 ml : 30 ml, using 1M HCl as the corrosion medium. To determine the effect of inhibitor concentration on the steel material, EIS (Electrochemical Impedance Spectroscopy) and PDP (Potentiodynamic Polarization) testing were conducted, while the corrosion rate was determined using the Weight Loss testing method. The highest efficiency in potentiodynamic polarization testing at 50°C was found in the combination of 50 ml water hyacinth concentration and 50 ml guava leaf concentration, at 95.48%. The highest efficiency in EIS testing at 50°C was found in the combination of 30 ml water hyacinth concentration and 70 ml guava leaf concentration. In the weight loss testing, the highest efficiency was 77.235%, obtained at 4-hour immersion with a combination of 50 ml water hyacinth inhibitor concentration and 50 ml guava leaf concentration. The inhibition mechanism of this inhibitor combination was found to be predominantly anodic.

Item Type:	Thesis (Diploma)
Uncontrolled Keywords:	baja api 5L grade B, Potensiodinamic, EIS, Weighloss
Subjects:	Q Science Q Science > QD Chemistry
Divisions:	Faculty of Industrial Technology > Mechanical Engineering > 21401-(D3) Diploma 3
Depositing User:	Adhi Wicaksono
Date Deposited:	12 Aug 2026 08:20
Last Modified:	12 Aug 2026 08:20
URI:	http://repository.its.ac.id/id/eprint/71446

Actions (login required)

View Item