Pengaruh Fraksi Massa Polianilin Dan Barium M Hexaferit Sebagai Material Penyerap Radar Pada Pelapisan Single Layer Baja AH36

Assyahidah, Ainul Millah (2015) Pengaruh Fraksi Massa Polianilin Dan Barium M Hexaferit Sebagai Material Penyerap Radar Pada Pelapisan Single Layer Baja AH36. Undergraduate thesis, Institut Teknology Sepuluh Nopember.

[img] Text
1111100002-Undergraduate Thesis.pdf - Published Version

Download (3MB)

Abstract

Material anti radar atau yang sering dikenal sebagai Radar Absorbing Material (RAM) pada dasarnya merupakan material yang mempunyai sifat bahan magnetik, dielektrik dan konduktif. Dimana sifat tersebut mampu untuk mereduksi gelombang elektromagnetik melalui mekanisme polarisasi dipol magnet, secara gelombang melalui mekanisme superposisi yang bersifat destruktif. Pemanfaat bahan baku yang digunakan dari sumber daya alam (SDA) sebagai material magnetik yang berasal dari batuan besi Tanah Laut Kalimantan Selatan, yang direkayasa secara ionik melalui mekanisme kopresipitasi dengan doping ion Zn dan BaCO3 untuk membentuk struktur Barium M Heksaferit. Selanjutnya dilakukan kalsinasi (pemanasan) pada temperature 1000 oC dengan waktu penahan (holding time) selama 5 jam. Sedangkan pembuatan PANi disintesis dari bahan dasar monomer anilin dengan menggunakan metode polimerisasi. Material partikel Barium M-Heksaferit yang dikombinasikan dengan partikel PANi (polimer konduktif) dan diikat oleh resin (cat) untuk dijadikan material komposit isotropik sebagai penyerapan gelombang radar pada daerah X-Band. Pada penelitian ini proses pelapisan RAM menggunakan metode Dallenbach layer pada pelapisan single layer dengan komposisi PAni (polianilin) dan BaM (Barium M Heksaferit)1 : 1, 1:2, 1:3 dan 2 : 1. Dari hasil pengujian VNA didapatkan penyerapan yang paling baik pada material dengan perbandingan 2 : 1, sedangkan v pada pengujian Scanning Electron Microscope (SEM) didapatkan ukuran partikel 0.4 μm – 0.5 μm. ====================================================================================================== Radar Absorbing Material (RAM) is basically a material whose characteristics are magnetic, dielectric and conductive. All those characteristics are able to reduce electromagnetic wave through a magnetic-dipole-polarization mechanism, through super-position mechanism whose characteristic is destructive. A usage of a raw material of natural resources, as magnetic material, which is taken from ironic stone from Tanah Laut, South Borneo, are changed using an ionic process which through coprecipitation mechanism using Zn and BaCO3 ion doping in shaping Barium structure M-Hexaferrite. After that, calcinations (heating) is done on 1000 0C with a holding time for 5 hours long. Meanwhile, PANi is synthesized from a basic substance of monomer aniline using polymerisation method. Barium M-Hexaferrite particle material which is combined with PANi (conductive Polymer) are tied by resin (paint) and used as isotopic composite material for absorbing radar on X-Band area. On this research, RAM’s coating process using Dallenbach layer method. On single layer coating, the composition of PAni (polianilin) and Bam (Barium M-Hexaferrite) 1 : 1, 1:2, 1:3 and 2 : 1. From VNA test’s result we know that the best absorption is got from a material whose ratio is 2 : 1. Meanwhile, the result of Scanning Electron Microscope (SEM) shows that particle’s size is 0.4 μm – 0.5 μm

Item Type: Thesis (Undergraduate)
Additional Information: RSFi 537.015 1 Ass p
Uncontrolled Keywords: Polianilin (PANi), Barium M Heksaferit (BaM), Radar Absorbing Material (RAM), pelapisan Dallenbach layer
Subjects: Q Science > QC Physics > QC448 Fiber optics.
Divisions: Faculty of Mathematics and Science > Physics > (S1) Undergraduate Theses
Depositing User: Mr. Tondo Indra Nyata
Date Deposited: 08 Nov 2019 02:34
Last Modified: 08 Nov 2019 02:34
URI: http://repository.its.ac.id/id/eprint/71657

Actions (login required)

View Item View Item