Studi Pengaruh Rasio Si/Al Terhadap Sifat Fisik-Mekanik Semen Geopolimer Berbasis Terak Feronikel

Mustofa, . (2016) Studi Pengaruh Rasio Si/Al Terhadap Sifat Fisik-Mekanik Semen Geopolimer Berbasis Terak Feronikel. Masters thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
2714201008-master-theses.pdf - Published Version

Download (2MB) | Preview

Abstract

Geopolimer merupakan material aluminosilikat padat dan stabil yang dibentuk oleh hidroksida alkali atau aktivasi silikat alkali dari prekursor yang biasanya diberikan sebagai serbuk padat melalui proses geopolimerisasi. Sumber utama bahan geopolimer merupakan bahan-bahan yang memiliki komponen silika dan alumina, salah satunya adalah terak feronikel. Proses geopolimerisasi secara substansial melibatkan reaksi kimia yang cepat dalam kondisi basa pada mineral Si-Al yang menghasilkan tiga dimensi rantai polimer dan struktur cincin yang terdiri dari obligasi Si-O-Al-O. Pada penelitian ini, proses pembuatan semen geopolimer terbagi dalam empat proses. Pertama, mencampurkan serbuk terak feronikel dengan aluminium hidroksida untuk memenuhi rasio Si/Al yang ditentukan. Kedua, mencampurkannya dengan larutan aktivator dengan rasio S/L adalah 5,4 gr/mL untuk membentuk pasta. Ketiga, pasta dicetak dalam cetakan kubus dengan dimensi 5x5x5 cm3 dan dipanaskan dalam oven pada suhu 80 oC selama 24 jam. Akhirnya, spesimen dibiarkan pada suhu ruang untuk pengerasan lebih lanjut. Hasil penelitian menunjukkan bahwa terdapat kecenderungan menurunnya penyerapan air dan meningkatnya kuat tekan dengan meningkatnya rasio Si/Al. Hal ini karena meningkatnya rasio Si/Al mengarah pada pembentukan geopolimer yang lebih homogen. Kondisi optimum dicapai ketika semen geopolimer memiliki kuat tekan tinggi dan penyerapan air rendah yaitu pada rasio Si/Al = 3,5, dimana kuat tekan dan penyerapan air (setelah 24 jam perendaman) masing-masing adalah 12,6 MPa dan 81,7 gr/100 cm2. ======================================================== Geopolymer is a solid and stable aluminosilicate material formed by alkali hydroxide or alkali silicate activation of the precursors is normally given as a solid powder through geopolymerization reaction. The main sources of geopolymer material are materials that have a component of silica and alumina, one of which is the ferronickel slag. Geopolymerization reaction substantially involves the rapid chemical reaction in alkaline conditions of mineral Si-Al that produces three-dimensional polymer chain and ring structure consisting of a bond Si-O-Al-O. In this study, manufacturing process of geopolymer cement consists in four stages. First, ferronickel slag powder mixed with aluminum hydroxide with specified Si/Al ratio. Second, mixed it with the activator solution with the S/L ratio is 5,4 g/mL to form the paste. Third, pasta molded in the cube mold with dimensions of 5x5x5 cm3 and cured in an oven at a temperature of 80 °C for 24 hours. Finally, the specimens were left at room temperature for further hardening. The results showed that there was a tendency to decrease water absorption and increase compressive strength with increasing Si/Al ratio. This is due to the increased of Si/Al ratio leads to the formation of a more homogeneous geopolymer. The optimum condition is achieved when the geopolymer cement has a high compressive strength and low water absorption is at a ratio of Si/Al = 3.5, where the compressive strength and water absorption (after 24 hours of immersion) was 12.6 MPa and 81.7 g/100 cm2, respectively.

Item Type: Thesis (Masters)
Additional Information: RTMt 620.118 Mus s
Uncontrolled Keywords: sifat fisik-mekanik, semen geopolimer, terak feronikel
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA418.9 Composite materials. Laminated materials.
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 27101-(S2) Master Thesis
Depositing User: EKO BUDI RAHARJO
Date Deposited: 13 Nov 2019 07:27
Last Modified: 13 Nov 2019 07:27
URI: http://repository.its.ac.id/id/eprint/71756

Actions (login required)

View Item View Item