Pengaruh pH dalam sintesis TiO2 anatase dengan metode chemical bath deposition terhadap karakteristik sensor gas volatile organic compound (methanol)

Kusumaningtyas, Shita Agustin (2016) Pengaruh pH dalam sintesis TiO2 anatase dengan metode chemical bath deposition terhadap karakteristik sensor gas volatile organic compound (methanol). Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
2414105035-undergradyate thesis.pdf

Download (1MB) | Preview
[img]
Preview
Text
2414105035-presentationpdf.pdf

Download (2MB) | Preview

Abstract

Telah dilakukan sintesis lapisan tipis TiO2 anatase dari prekursor TiCl3 pada substrat FTO dan Al2O3 menggunakan metode chemical bath deposition dengan variasi pH 3,5, pH 5,5, pH 7, pH 8,5 dan pH 9,5. Lapisan tipis TiO2 yang terbentuk diuji dengan XRD, AFM dan BET. Dari hasil pengujian didapatkan bahwa semakin tinggi pH, fase yang terbentuk cenderung anatase dan didapatkan pula bahwa penambahan pH berpengaruh terhadap kontur TiO2. Penggunaan substrat sebagai media penumbuhan TiO2 mempengaruhi fase serta ukuran kristal TiO2. Pada substrat FTO dengan pH 9,5 didapatkan fase anatase dengan ukuran kristal 16,25 nm sedangkan pada serbuk TiO2 memiliki ukuran kristal 60,85 nm. Sintesis TiO2 dengan pH 3,5 memiliki luas permukaan paling besar yaitu 88,8 m2/g. Hasil uji sensor gas menunjukkan bahwa TiO2 pada substrat FTO tidak cocok jika diaplikasikan sebagai sensor gas karena FTO memiliki sifat konduktif. ============================================================================================================ Synthesis of thin layer TiO2 anatase from TiCl3 precursor has been successfully grown on FTO and Al2O3 substrates by using chemical bath deposition. The pH of synthesis was varied i.e 3.5, 5.5, 7, 8.5, and 9.5. Several characterization methods were applied to check whether the film has been formed by means of XRD, AFM and BET. The result indicate that the higher the pH used, the more fraction of anatase was observed and influence of pH addition had an effect on TiO2 peak. Our result also reveqal that the use of FTO led to difference in the phase formation and crystallite size of TiO2, i.e.16.25 nm using FTO and 60,85 nm for powder. Synthesis TiO2 from pH 3.5 has a greatest surface area with value of 88.8 m2/g. Gas sensor test result indicate that TiO2 substrate on the FTO is not suitable when applied as gas sensors because of its conductive proprerties.

Item Type: Thesis (Undergraduate)
Additional Information: RSF 661.806 Kus p
Uncontrolled Keywords: chemical bath deposition, sensor gas, pH, TiO2 anatase, volatile organic compound
Subjects: T Technology > TP Chemical technology > TP350 Natural gas--Drying.
Divisions: Faculty of Industrial Technology > Physics Engineering > 30201-(S1) Undergraduate Thesis
Depositing User: - Taufiq Rahmanu
Date Deposited: 02 Dec 2019 06:22
Last Modified: 02 Dec 2019 06:22
URI: http://repository.its.ac.id/id/eprint/72146

Actions (login required)

View Item View Item