Laku Panas Pada Baja ST 42 Dengan Variasi Media Pendingin Air dan Oli Kemudian di Tempering Terhadap Nilai Kekerasan dan Struktur Mikro

Yonedy, Alisjahbana (2019) Laku Panas Pada Baja ST 42 Dengan Variasi Media Pendingin Air dan Oli Kemudian di Tempering Terhadap Nilai Kekerasan dan Struktur Mikro. Diploma thesis, Institut Teknologi Sepuluh Nopember.

Text 10211500000048-Undergraduate_Thesis.pdf Restricted to Repository staff only Download (1MB) | Request a copy

Abstract

Baja karbon rendah telah banyak diketahui memiliki nilai ketangguhan dan keuletan akan tetapi memiliki sifat kekerasan dan ketahanan aus yang rendah dikarenakan memiliki kandungan unsur karbon dalam struktur baja kurang dari 0,3%, selain itu baja ini memiliki mampu mesin dan mampu las dengan baik dan sifat nya relatif lunak. Oleh karena sifat-sifat tersebut, baja karbon rendah ST 42 banyak digunakan sebagai bahan baku untuk pembuatan komponen struktur bangunan, pipa gedung, jembatan, dan body pada mobil. Pada penelitian ini akan dilakukan pengamatan terhadap perubahan sifat kekerasan dan struktur mikro yang terjadi pada baja karbon rendah ST 42 jika diberikan perlakuan panas hardening dan tempering dengan memberikan variasi media pendingin air dan oli. Perlakuan panas hardening ini diawali dengan melakukan pemanasan carburizing terhadap baja karbon rendah ST 42 dengan suhu 9000C dan dilakukan penahanan selama 4 jam, kemudian didinginkan dengan cepat menggunakan media pendingin berupa air. Selanjutnya diberi perlakuan panas hardening 1 kembali dengan variasi temperatur yaitu 900°C, dan proses tempering temperatur 400°C dengan media pendingin air. Selanjutnya baja karbon rendah ST 42 diberi perlakuan panas hardening 2 dengan variasi temperatur 900°C, dan proses tempering temperatur 400°C dengan media pendingin oli, maka dilakukan observasi terhadap sifat kekerasan dan struktur mikro. Pada penelitian ini didapatkan penurunan pada nilai kekerasan pada baja karbon rendah ST 42 yang diberi perlakuan panas hardening dengan media pendingin air dan juga mengalami penurunan pada baja karbon rendah ST 42 dengan media pendingin oli dengan perubahan temperatur. Benda uji yang diberikan perlakuan tempering dengan diberikan variasi temperatur 900°C dengan media pendingin air memiliki nilai kekerasan yang paling tinggi.
=====================================================================================================================================
Low carbon steels have been known to have toughness and tenacity values but have low hardness and wear resistance because they have a carbon element content in steel structures of less than 0.3%, besides this steel has engine capable and is well welded and has properties it's relatively soft. Because of these characteristics, low carbon steel ST 42 is widely used as a raw material for the manufacture of building structural components, building pipes, bridges, and bodies on cars. In this study, observations will be made on changes in hardness and microstructure which occur in ST 42 low carbon steel if given hardening and tempering heat treatment by giving variations of water cooling media and oil. The hardening heat treatment begins with heating carburizing against ST 42 low carbon steel with a temperature of 9000C and holding for 4 hours, then cooled quickly using a cooling medium in the form of water. Then the hardening 1 heat treatment was returned with a temperature variation of 900 ° C, and a temperature tempering process of 400 ° C with water cooling media. Furthermore, ST 42 low carbon steel was given hardening 2 heat treatment with a temperature variation of 900 ° C, and a temperature tempering process of 400 ° C with oil cooling media, it is observed the hardness and microstructure. In this research we found an decrease in the hardness value of ST 42 low carbon steel hardening treated with water cooling media and also experienced an decrease in ST 42 low carbon steel with oil cooling media with temperature changes. The specimens given tempering treatment were given a temperature variation of 900 ° C with oil cooling media having the highest hardness value

Item Type:	Thesis (Diploma)
Uncontrolled Keywords:	Baja Karbon Rendah ST 42, Carburizing, Hardening, Tempering, Variasi Pendingin, Sifat Kekerasan, Struktur mikro
Subjects:	T Technology > TS Manufactures > TS176 Manufacturing engineering. Process engineering (Including manufacturing planning, production planning)
Divisions:	Faculty of Vocational > Mechanical Industrial Engineering (D4)
Depositing User:	Yonedy Alisjahbana
Date Deposited:	11 Aug 2026 07:34
Last Modified:	11 Aug 2026 07:34
URI:	http://repository.its.ac.id/id/eprint/72196

Actions (login required)

View Item