Pengaruh persen berat poliamida-6 dan temperatur sintering terhadap mikrostruktur dan sifat mekanik proyektil komposit tembaga-poliamida (Cu-PA6)

Dewanto, Hizkia Alpha (2015) Pengaruh persen berat poliamida-6 dan temperatur sintering terhadap mikrostruktur dan sifat mekanik proyektil komposit tembaga-poliamida (Cu-PA6). Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
2711100019-Undergraduate_Thesis.pdf

Download (2MB) | Preview
[img]
Preview
Text
2711100019-Paper-2711100019-paperpdf.pdf

Download (1MB) | Preview
[img]
Preview
Text
2711100019-Presentation-2711100019-presentationpdf.pdf

Download (2MB) | Preview

Abstract

Proyektil untuk senapan dan pistol selama ini terbuat dari logam timbal yang bersifat racun. Selain itu, proyektil normal beresiko mengalami ricochet yang dapat mengakibatkan kerusakan, luka-luka, bahkan korban jiwa. Oleh karena itu, saat ini dikembangkan proyektil yang memiliki dua sifat sekaligus: berbahan baku non timbal dan mampu pecah pada penumbukan (frangible). Penelitian ini meneliti amunisi frangible berbahan baku komposit tembaga dan poliamida-6 dari segi sifat mekanik dan karakterisasi material. Variabel dalam penelitian ini adalah persen massa poliamida-6 dalam proyektil yaitu 0,5, 1, dan 1,5%, serta temperatur sintering proyektil pascakompaksi yaitu 200, 250, dan 300oC. Tahapan pembuatan spesimen proyektil adalah dry mixing dengan magnetic stirrer, kompaksi untuk pemadatan awal spesimen pada tekanan 300 MPa selama 5 menit, dan sintering untuk penguatan ikatan antar partikel dalam spesimen selama 30 menit. Uji mekanik yang dilakukan adalah uji kekerasan dan uji tekan. Uji mekanik dilakukan untuk mendapatkan nilai kekerasan, kekuatan tekan, dan modulus elastisitas proyektil dan membandingkan nilai tersebut dengan proyektil frangible yang sudah ada di pasaran. Uji karakterisasi yang dilakukan adalah pengamatan XRD dan SEM dengan tujuan mengetahui mekanisme ikatan antar partikel proyektil. ===================================================================================================== Majority of projectile for small firearms made of toxic lead and prone to ricochet. Thus, lead-free projectile with ability to break upon contact with hard surface or “frangible” is needed. This research will investigate frangible projectile made of copper and polyamide 6 composite from mechanical properties and characterization side. Variables in this research are polyamide 6 mass percentage, there are 0,5, 1, and 1,5%, and projectile sintering temperature, there are 200, 250, and 300oC. From testing data obtained that variable with most optimal mechanical properties and density for frangible application is polyamide of 0.5% mass percent with average compressive strength of 127.76 MPa, hardness of 21.33 HRB and density of 6.77 gr/cm3, then heating/sintering temperature of 250oC with average compressive strength of 116.73 MPa, hardness of 20.44 HRB and density of 6.66 gr/cm3. By microstructure, the important factor for the mechanical properties of specimen is porosity formed around polyamide particles, diffusion of polyamide towards porosity, and interlocking of copper particles.

Item Type: Thesis (Undergraduate)
Additional Information: RSMt 620.118 Dew p
Uncontrolled Keywords: Metalurgi serbuk, frangible, uji mekanik,karakterisasi
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA418.9 Composite materials. Laminated materials.
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering
Depositing User: - Taufiq Rahmanu
Date Deposited: 18 Dec 2019 02:15
Last Modified: 18 Dec 2019 02:15
URI: http://repository.its.ac.id/id/eprint/72413