Studi Pengaruh Penambahan Sio2 Terhadap Morfologi, Sifat Fisik Dan Sifat Mekanik Komposit Fotopolimer Pmma/Sio2 Sebagai Kandidat Bahan Dental Filler

Rojimba, Rico Adrianto (2016) Studi Pengaruh Penambahan Sio2 Terhadap Morfologi, Sifat Fisik Dan Sifat Mekanik Komposit Fotopolimer Pmma/Sio2 Sebagai Kandidat Bahan Dental Filler. Undergraduate thesis, Institut Teknologi Sepuluh Nopember Surabaya.

[img]
Preview
Text
2712100110-undergraduated-theses-.pdf - Published Version

Download (2MB) | Preview

Abstract

Polimetil metakrilat (PMMA) merupakan material yang banyak digunakan untuk aplikasi bahan tambal gigi, namun memiliki beberapa kekurangan yaitu daya serap air yang tinggi dan tingkat kekerasan yang rendah. SiO2 biasa digunakan sebagai partikel pengisi suatu komposit. SiO2 memiliki sifat hidrofobik, jika dikompositkan mampu meningkatkan sifat mekanik polimer. Penelitian ini bertujuan untuk meningkatkan sifat fisik dan mekanik PMMA dengan cara membentuk komposit PMMA/SiO2 menggunakan metode fotopolimerisasi. variasi yang digunakan pada penelitian ini adalah penambahan SiO2 sebesar 5%, 10%, 15%, 20%, dan 25% berat. Metode fotopolimeriasi menggunakan fotoinisiator Irgacure 784. Cahaya tampak berwarna biru dengan range panjang gelombang 440-480 nm digunakan untuk mensintesis komposit PMMA/SiO2. Pengujian kekerasan dan daya serap air dilakukan untuk mengetahui respon terhadap penambahan SiO2. Hasil penelitian menunjukan bentuk morfologi awal dari PMMA adalah flake berpori setelah adanya penambahan SiO2 terdapat partikel putih diantara pori tersebut. nilai kekerasan komposit PMMA/SiO2 paling besar didapat pada komposisi SiO2 25% dengan nilai 84,8 HD. Kemampuan serap pada komposisi adalah yang paling kecil, sebesar 0,65%. =========================================================== Polymethyl methacrylate (PMMA), a material that is widely used for the application of dental filling material, but has some limitations, such as a high water absorption and low levels of hardness. SiO2 is used as filler particles of a composite. SiO2 has hydrophobic properties, if the composite is able to improve the mechanical properties of the polymer. This study aims to improve the physical and mechanical properties of PMMA by forming a PMMA / SiO2 composite using photopolymerization method. variations used in this study is the addition of SiO2 by 5%, 10%, 15%, 20%, and 25% by weight. Photopolymerization method using the photoinitiator Irgacure 784. Visible light blue with a wavelength range 440-480 nm is used to synthesize the composite PMMA / SiO2. Testing of hardness and water absorption was conducted to determine a response to the addition of SiO2. The results showed the initial morphology of PMMA is a porous flake after the addition of SiO2 contained white particles among the pores. Hardness value of PMMA/SiO2 composites most obtained on the composition SiO2 25% by value of 84.8 HD. Absorptive capability in the composition is the smallest, at 0.65%

Item Type: Thesis (Undergraduate)
Additional Information: RSMt 620.118 Roj s
Uncontrolled Keywords: Komposit PMMA/SiO2, Fotopolimerisasi, Irgacure 784
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA418.9 Composite materials. Laminated materials.
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis