Studi Pengaruh Modifikasi Karbon Aktif Dengan Penambahan Hno3 Pada Elektroda Karbon Dalam Sistem Capacitive Deionization

Blegur, Ernes Josias (2016) Studi Pengaruh Modifikasi Karbon Aktif Dengan Penambahan Hno3 Pada Elektroda Karbon Dalam Sistem Capacitive Deionization. Masters thesis, Institut Teknologi Sepuluh Nopember Surabaya.

[img]
Preview
Text
1114201017-Master_Thesis.pdf - Published Version

Download (2MB) | Preview

Abstract

Elektroda karbon dibuat dengan metode crosslink untuk tujuan desalinasi telah disintesis dan dikarakterisasi. Elektroda karbon yang digunakan pada studi ini disintesis dengan menggunakan karbon aktif dengan dan atau tanpa karbon aktif modifikasi, polyvinyl alcohol sebagai binder, dan glutaritc acid sebagai agent crosslink dengan temperature crosslink 120° C. Modifikasi karbon aktif dibuat dengan penambahan HNO3 dengan variasi 8, 9 dan 10 M. Berdasrkan hasil UJI FTIR terjadi penambahan gugus-gugus fungsi yang mengandung oksigen pada karbon aktif modifikasi. Sifat fisik elektroda karbon diamati dengan SEM-EDX, dan hasil uji menunjukan bahwa elektroda karbon yang dibuat dengan ACM 10 M memiliki struktur pori yang lebih baik dibandingkan elektroda lainnya. Sementara itu, nilai kapasitansi spesifik elektroda karbon dianalisis dan dihitung dengan Cyclic Voltametry (CV) pada sweep rate 10 mV/s. Hasil menunujukan bahwa elektroda karbon yang dibuat dengan karbon aktif modifikasi menggunakan 10M HNO3 nilai tertinggi dibandingkan yang lainnya. Selanjutnya, persentase penurunan kadar garam sistim CDI baik dengan atau tanpa elektroda karbon yang dimodifikasi menunjukan bahwa nilai tertinggi dapat dicapai dengan CDI yang dibuat dengan karbon aktif modifikasi menggunakan HNO3 dengan persentase penurunan kadar garam yang diperoleh 35.09%. Hasil ini menunjukan bahwa karbon aktif modifikasi menggunakan HNO3 dapat meningkatkan efisiensi CDI ======================================================================= Carbon electrodes prepared with crosslink method for desalination purpose has been synthesized and characterized. The carbon electrodes used in this study synthesized using activated carbon with and/or without modified active carbon, polyvinyl alcohol (PVA) as a binder, and glutaric acid as a crosslink agent with crosslink temperature at 120°C. Modification of active carbon prepared with the addition of HNO3 with varies at 8, 9 and 10 M. Based on the results of FTIR test showed that the addition of functional groups containing oxygen occurred in the modified activated carbon. The physical properties of carbon electrodes were observed by SEM-EDX, and the results showed that the carbon electrodes prepared with modified activated carbon using 10 M HNO3 has a pore structure is better than the other electrodes. Meanwhile, specific capacitance values for the carbon electrodes were analyzed and calculated by Cyclic Voltammetry (CV) at a sweep rate of 10 mV/s. The results showed that the carbon electrodes prepared with the modified active carbon using 10M HNO3 has the highest value compared to the other one. Furthermore, the salt-removal percentage of the CDI systems either with or without modified carbon electrodes showed that the highest values could be achieved by CDI prepared with modified active carbon using 10M HNO3 with the salt-removal percentage obtained at 35.09%. This result indicates that modified active carbon using HNO3 could enhance the efficiency of CDI

Item Type: Thesis (Masters)
Additional Information: RTFi 541.372 4 Ble s
Uncontrolled Keywords: Crosslink, Polyvinyl alcohol (PVA), capasitive deionization (CDI), konduktivitas
Subjects: Q Science > QC Physics > QC610.3 Electric conductivity
Q Science > QD Chemistry > QD553 Electrochemistry. Electrolysis
Divisions: Faculty of Mathematics and Science > Physics > 45101-(S2) Master Thesis
Depositing User: EKO BUDI RAHARJO
Date Deposited: 20 Jan 2020 02:15
Last Modified: 20 Jan 2020 02:15
URI: http://repository.its.ac.id/id/eprint/72735

Actions (login required)

View Item View Item