Augustino, Immanuel Freddy (2015) Pengaruh Lama Waktu Tunggu Pada Proses PWHT Terhadap Sifat Mekanik, Struktur Mikro Dan Tegangan Sisa Pada Pengelasan Baja AAR M201 Gr.B+. Masters thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
2713201012-Master_Thesis.pdf Download (4MB) | Preview |
Abstract
PWHT adalah proses perlakuan panas yang biasanya diberikan pada material setelah mengalami proses pengelasan, PWHT bertujuan untuk mengurangi tegangan sisa, menyeragamkan butir dan membuat material lebih tangguh.
Dalam penelitian ini material yang digunakan adalah AAR M201 Gr.B+ dengan ketebalan 20mm. Proses las menggunakan SMAW dengan elektroda E8018-B2, polaritas DCEP. PWHT diberikan pada temperatur 600oC dengan waktu tunggu selama 1 jam, 2 jam, 3 jam dan 4 jam didalam furnace lalu didinginkan di udara.
Berdasarkan hasil pengujian struktur mikro, semakin lama waktu tunggu, maka struktur butir menjadi lebih seragam, dan butir menjadi lebih besar. Hal ini dikarenakan panas yang masuk merupakan energi bagi struktur butir sehingga membuat butir membesar dan lebih seragam. Berdasarkan hasil pengujian kekerasan pada daerah base metal, HAZ, dan weld metal, didapatkan nilai kekerasan menurun akibat PWHT, hal ini dikarenakan tegangan sisa menurun akibat proses PWHT sehingga nilai kekerasan ikut turun. Didapatkan nilai kekerasan yang masuk dalam range yaitu pada material yang diberi perlakuan panas selama 4 jam. Berdasarkan hasil pengujian impak pada daerah weld metal, FL+1, FL+5, didapatkan daerah weld metal memiliki nilai impak paling rendah, hal ini karena pada daerah weld metal kekerasannya tinggi sehingga ketangguhannya rendah. Semua daerah menunjukkan tren yang sama, dari material tanpa diberi PWHT hingga yang diberi PWHT dengan waktu tunggu 4 jam. Berdasarkan hasil pengujian XRD pada daerah base metal, HAZ, dan weld metal, didapatkan hasil yang berbeda-beda, namun dari keseluruhan daerah menunjukkan bahwa tegangan sisa menurun pada material yang diberi PWHT 4 jam sehingga mengakibatkan nilai kekerasan menurun dan ketangguhan meningkat. Nilai tegangan sisa mencapai nilai yang hampir sama pada pemberian PWHT 2 jam.
===============================================================================================
PWHT is a heat treatment process that usually given to materials after welding. PWHT is supposed to reduce the residual stress, to uniform the grain and to make material much tougher.
On this experiment, material used is AAR M201 Gr.B+ with 20mm thick. Welding process using SMAW with electrode E8018-B2, polarity DCEP. PWHT is given in temperature of 600oC, held for 1 hour, 2 hours, 3 hours and 4 hours in the furnace and then cooled in air.
Based on the result of microstructure test, the longer Holding time is given, the more uniform and the bigger the grain becomes. This is because the heat which given into material is energy to the grain to make himself much bigger and more uniform. Based on the result of hardness test in areas of base metal, HAZ, and weld metal, obtained the value of hardness decreased because of PWHT, this may happen because the residual stress decreased after PWHT, so the value of hardness is decreased as well. Obtained the hardness value that is still in range is in the material given PWHT with Holding time for 4 hours. Based on the result of impact test in areas of weld metal, FL+1, FL+5, obtained the impact value in area of weld metal has the lowest value, for the hardness in weld metal is high and the toughness is low. All areas show the same trend from the material without PWHT to material given PWHT for 4 hours. Based on the result of XRD test in areas of base metal, HAZ, and weld metal, obtained different result each, yet the entire areas show that the residual stress decreased on material given PWHT for 4 hours, so it causes the hardness value decreased and the toughness increased. The residual stress achieves almost the same value on material given PWHT for 2 hours.
| Item Type: | Thesis (Masters) |
|---|---|
| Additional Information: | RTMt 671.52 Aug p |
| Uncontrolled Keywords: | PWHT, Temperatur, Waktu tunggu, Struktur mikro, Kekerasan, impak, XRD |
| Subjects: | T Technology > TS Manufactures > TS227 Welding. |
| Divisions: | Faculty of Industrial Technology > Material & Metallurgical Engineering > 27101-(S2) Master Thesis |
| Depositing User: | Mr. Marsudiyana - |
| Date Deposited: | 21 Jan 2020 06:52 |
| Last Modified: | 21 Jan 2020 06:52 |
| URI: | http://repository.its.ac.id/id/eprint/72823 |