Pengaruh Penambahan Kitosan Terhadap Sifat Mekanik Komposit Kitosan / Hidroksiapatit Yang Didoping Seng Sebagai Kandidat Material Bone Subtitute

Purnomo, Agus (2016) Pengaruh Penambahan Kitosan Terhadap Sifat Mekanik Komposit Kitosan / Hidroksiapatit Yang Didoping Seng Sebagai Kandidat Material Bone Subtitute. Undergraduate thesis, Institut Teknologi Sepuluh Nopember Surabaya.

[img]
Preview
Text
2712100076-Undergraduate_Thesis.pdf - Published Version

Download (4MB) | Preview

Abstract

Komposit Kitosan/HA-Zn telah berhasil dibuat dengan metode pencampuran basah. Kitosan dengan derajat deasetilasi 84% dilarutkan dalam asam asetat 3% selama 1 jam pada temperatur 700 C. Kemudian ditambahkan serbuk HA-Zn dengan konsentrasi ion dopingan sebesar 15 % mol yang dibuat menggunakan metode sol gel pada temperatur kalsinasi sebesar 9000 C selama 3 jam. Perbandingan komposisi campuran komposit yakni 10%, 15% dan 20% Kitosan. Hasil serbuk komposit kemudian diuji dengan FTIR, XRD SEM dan uji densitas untuk karakterisasi sifat fisik. Uji tekan dan hardness dilakukan untuk mengetahui sifat mekanik. Dari hasil uji, penambahan Kitosan meningkatkan distribusi ikatan antara komponen matriks dan filler pada komposit. Penambahan Kitosan diketahui dapat meningkatkan nilai kekuatan tekan dan nilai modulus elastisitas serbuk HA-Zn yang dikompositkan. Sedangkan untuk nilai densitas dan kekerasan permukaan menurun seiring meningkatnya jumlah Kitosan yang ditambahkan. Sampel 10%K/HA-Zn denan nilai kuat tekan dan modulus elastisitas masing-masing 57,035 MP dan 0.152 GPa memiliki sifat fisik dan mekanik yang memenuhi standar sebagai kandidat material pengganti tulang cancellous ======================================================================= Composite Zinc doped in Chitosan / Hydroxyapatite have been made with the wet mixing method. Chitosan with degree of deacetylation of 84% dissolved in 3% acetic acid fisrt for 1 hour at a temperature of 700 C. Then powder HA-Zn (15% mol Zn) which created using sol-gel method at calcination temperature of 9000 C for 3 hours was added. Composition of Chitosan in composite was 10%, 15% and 20%. In this study, characterization of composite powders has done by FTIR, XRD and SEM. Then test density, compressive and hardness of compact composite is done to determine the mechanical properties. In the result, Chitosan improve the distribution bond between matrix and filler components of composite. Chitosan increase compressive strength and modulus elasticity of composite. Furthermore, the density and surface hardness of composite decreased with increasing the amount of chitosan. 10%K/HA-Zn with 57,035 MPa of compressive strength and 0,152 GPa of modulus elasticity, have the physical and mechanical properties that meet the standards as cancellous bone substitute material

Item Type: Thesis (Undergraduate)
Additional Information: RSMt 620.118 Pur p
Uncontrolled Keywords: komposisi, komposit Kitosan/HA-Zn, sifat mekanik, bone subtitute.
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA418.9 Composite materials. Laminated materials.
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis