Dewanti, Laras Refsita (2020) Analisis Pengaruh Temperatur Thermal Shock terhadap Struktur Graphene Hasil Sintesis dengan Metode Microwave-Assisted Solvothermal untuk Aplikasi Superkapasitor. Other thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
02511640000050-Undergraduate_Thesis.pdf Download (3MB) | Preview |
Preview |
Text
02511640000050-Undergraduate_Thesis.pdf Download (3MB) | Preview |
Abstract
Superkapasitor merupakan terobosan yang menarik dibidang energi karena memiliki kapasitas penyimpanan yang jauh lebih besar dari kapasitor biasa. graphene merupakan salah satu bahan superkapasitor yang banyak digunakan karena memiliki luas spesifik permukaan yang tinggi. Tujuan dari penelitian ini sendiri antara lain menganalisa pengaruh temperatur terhadap struktur material graphene dan sifat kapasitif material graphene sebagai elektroda superkapasitor dengan metode microwave-assisted solvothermal dengan menggunakan grafit, asam Tartarat, dan Metanol sebagai bahan utamanya. Variasi temperatur thermal shock di dalam furnace yang digunakan dalam proses sintesa yaitu 600, 700, 800 oC. Material hasil proses sintesis dilakukan karakterisasi menggunakan pengujian XRD, FTIR, dan SEM. Untuk performa superkapasitor, dilakukan pengujian CV. Didapatkan bahwa dengan semakin tinggi temperatur thermal shock yang diberikan, semakin banyak energi yang diberikan untuk memperlebar jarak antar layer pada grafit sehingga dihasilkan graphene yang bersifat amorfus, dengan morfologi yang tipis dan gugus fungsi oksigen yang rendah. Nilai kapasitansi dari yang tertinggi berturut-turut adalah saat dilakukan thermal shock dengan temperatur 800oC (141,659 F/g), 700oC (124,848 F/g) dan 600oC (111,240 F/g).
=================================================================================================================================
Supercapacitor is an interesting breakthrough in the field of energy because it has a storage capacity that greater than ordinary capacitors. graphene is one of the most widely used supercapacitor materials because it has a high surface specific area. The purpose of this research is to analyze the effect of temperature on the structure of graphene material and the capacitive properties of graphene material as a supercapacitor electrode by the microwave-assisted solvothermal method using graphite, Tartaric acid, and Methanol as its main ingredients. The temperature variation of thermal shock in the furnace used in the synthesis process is 600, 700, 800 oC. Material produced from the synthesis process was characterized using XRD, FTIR, and SEM tests. For supercapacitor performance, CV testing is carried out. It was found that the higher the temperature of the thermal shock applied, the more energy was given to widen the distance between the layers in the graphite to produce amorphous graphene, with a thin morphology and a low oxygen function group. the highest capacitance value is the usage of thermal shock temperature at 800oC (141,659 F/g), 700oC (124,848 F/g) dan 600oC (111,240 F/g) respectively.
| Item Type: | Thesis (Other) |
|---|---|
| Additional Information: | RSMt 620.198 Dew a-1 2020 |
| Uncontrolled Keywords: | Microwave-assisted, Graphene, Solvothermal, Temperatur Thermal-Shock, Superkapasitor. |
| Subjects: | T Technology > TA Engineering (General). Civil engineering (General) > TA455.G65 Graphene |
| Divisions: | Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis |
| Depositing User: | Laras Refsita Dewanti |
| Date Deposited: | 19 Dec 2023 08:17 |
| Last Modified: | 19 Dec 2023 08:17 |
| URI: | http://repository.its.ac.id/id/eprint/73222 |