Natrium bikarbonat (NaHCO3) dari waterglass dengan proses karbonasi

Diorana, Bunga Citra and Ariqoh, Rizky (2019) Natrium bikarbonat (NaHCO3) dari waterglass dengan proses karbonasi. Other thesis, Institut Teknologi Sepuluh Nopember.

Preview	Text Thesis Baru.pdf Download (2MB) | Preview
	Text 02211746000021_02211746000029-Undergrduate_Thesis.pdf Download (2MB)

Abstract

Proses karbonasi dipilih karena bahan baku water glass murah dan dapat menghasilkan produk samping silika yang bernilai jual tinggi. Proses ini mereaksikan Sodium sillicate (water glass) dengan gas CO2 menjadi Sodium Carbonate (soda ash) dilanjutkan dengan mereaksikan kembali Sodium Carbonate dengan gas CO2 agar menjadi Sodium Bicarbonate. Bahan baku utama dalam proses pembuatan yaitu Sodium Silicate yang memiliki komposisi SiO2 sebesar 27,7% dan NaO sebesar 6,8% dengan modulus 3,3. Dari proses ini dapat menghasilkan NaHCO3 dengan kemurnian >99%. Pabrik ini akan didirikan dan siap beroperasi pada tahun 2023, dengan pembelian peralatan pada tahun 2020 dan masa konstruksi selama 2 tahun (2021-2022). Lokasi pabrik direncanakan akan didirikan di Kawasan Industri Sentul, Bogor Jawa Barat. Kapasitas produksi Sodium Bicarbonate direncanakan sebesar 20.000 ton/tahun. Dalam pemenuhan kapasitas tahunan, pabrik akan beroperasi kontinyu 24 jam per hari selama 300 hari. Untuk memproduksi Sodium Bicarbonate sebesar 20.000 ton/tahun diperlukan bahan baku Sodium Silicate sebesar 18.158,75 ton/tahun, gas CO2 sebesar 15.104,44 ton/tahun, dan CaCO3 sebesar 0,9635 ton/tahun. Perhitungan Analisa ekonomi didasarkan pada discounted cash flow. Dari perhitungan analisa ekonomi, dengan harga jual Sodium Bicarbonate sebesar $234,88 per ton dan harga jual silika sebesar $782,91 per ton, diperoleh Internal Rate Return (IRR) sebesar 32% dengan suku bunga 12,5% dan waktu pengembalian modal (pay out period) 3,05 tahun. Modal untuk pendirian pabrik menggunakan rasio 40% modal sendiri dan 60% modal pinjaman. Modal total yang dibutuhkan untuk mendirikan pabrik adalah sebesar Rp. 79,222,804,713. Sedangkan Break Event Point (BEP) yang diperoleh adalah sebesar 32,56%.
==================================================================================================================================
The carbonation process was chosen because water glass is cheap and can produce high-value silica byproducts. This process reacts Sodium sillicate (water glass) with CO2 gas to become Sodium Carbonate (soda ash) followed by reacting Sodium Carbonate again with CO2 gas to become Sodium Bicarbonate. The main raw materials in the manufacturing process are Sodium Silicate which has a SiO2 composition of 27.7% and NaO of 6.8% with a modulus of 3.3. From this process can produce NaHCO3 with purity> 99%. This plant will be established and ready to operate in 2023, with the purchase of equipment in 2020 and a construction period of 2 years (2021-2022). The location of the plant is planned to be erected in Sentul Industrial Estate, Bogor, West Java. Sodium Bicarbonate production capacity is planned at 20,000 tons / year. In meeting its annual capacity, the plant will operate continuously 24 hours per day for 300 days. To produce Sodium Bicarbonate at 20,000 tons / year, Sodium Silicate raw material is needed at 18,158.75 tons / year, CO2 gas at 15,104.44 tons / year, and CaCO3 at 0.9635 tons / year. Calculation Economic analysis is based on discounted cash flow. From the calculation of economic analysis, with Sodium Bicarbonate selling price of $ 234.88 per ton and silica selling price of $ 782.91 per ton, an Internal Rate of Return (IRR) of 32% is obtained with an interest rate of 12.5% and payback period (pay) out period) 3.05 years. Capital for the construction of factories uses a ratio of 40% own capital and 60% loan capital. The total capital needed to set up a factory is Rp. 79,222,804,713. While the Break Event Point (BEP) obtained is 32.56%.

Item Type:	Thesis (Other)
Additional Information:	RSK 660.284 25 Dio s-1 2020
Uncontrolled Keywords:	Sodium Bicarbonate, Silika, Sodium Carbonate, Karbonasi
Subjects:	T Technology > TP Chemical technology > TP248 Nanogels. Nanoparticles.
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Chemical Engineering > 24201-(S1) Undergraduate Thesis
Depositing User:	Rizky Ariqoh
Date Deposited:	14 May 2024 05:19
Last Modified:	14 May 2024 05:19
URI:	http://repository.its.ac.id/id/eprint/73843

Actions (login required)

View Item