Analisis Pengaruh Variasi Gas Pelindung dengan Variasi Debit Gas Pelindung Pada Weld Joint Baja A36 Terhadap Sifat-Sifat Mekanik

Farhan, Hanif (2020) Analisis Pengaruh Variasi Gas Pelindung dengan Variasi Debit Gas Pelindung Pada Weld Joint Baja A36 Terhadap Sifat-Sifat Mekanik. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 04311540000139-Undergraduate_Theses.pdf Restricted to Repository staff only Download (9MB) | Request a copy

Abstract

Baja ASTM A36 merupakan baja karbon rendah dengan kandungan karbon 0,25% dan digunakan untuk konstruksi bangunan lepas pantai. Tujuan penelitian ini untuk mengetahui pengaruh variasi gas pelindung dengan variasi debit gas pelindung terhadap kekuatan tarik, kekerasan dan pengamatan struktur makro-mikro pada pengelasan baja ASTM A36 dengan metode GMAW. Variasi gas pelindung yang digunakan adalah Ar+CO2 (0+100%, 70%+30%, 100%+0%). Variasi debit gas pelindung yang digunakan adalah 12l/m, 15l/m, 18l/m. Elektroda yang digunakan adalah ER70S-G. Hasil uji kekuatan tarik menunjukkan bahwa pengelasan dengan CO2 100% dengan debit gas pelindung 18 l/m mempunyai nilai kekuatan tarik terbesar, yaitu dengan yield 278 MPa dan Ultimate strength 353 MPa. Hasil uji kekerasan menunjukkan bahwa pengelasan dengan CO2 100% mempunyai nilai kekerasan terbesar di weld metal, yaitu 226,1 VHN. Pada hasil pengamatan struktur mikro, pengelasan dengan CO2 dengan debit gas pelindung 18 l/m mempunyai fase pearlite paling tinggi pada bagian weld metal, yaitu sebesar 38%.================================================================= ASTM A36 steel is low carbon with carbon content 0,25 % and used for offshore construction. The purpose of this study was knowing the effect variation shield gas with variation shield gas flow rate to tensile strength, hardness and macro-micro structures observations. Shield gas variation used is Ar+CO2 (0%+100%, 70%+30%, 100%+0%). Shield gas flow rate variation using ER70S-G. Tensile test result show that welding with CO2 100% with shield gas flow rate 18 l/m has the highest tensile strength value on yield strength 278 MPa and ultimate strength 353 MPa. Hardness test results show that with CO2 100% and shield gas flow rate has the highest value in the weld metal that 226,1 VHN. Observation of macro photos show that welding CO2 100% with gas flow rate has widest HAZ width of 18 mm. Observation micro structure welding with CO2 with shield gas flow rate 18 l/m has pearlite phase is highest in the weld metal, that is 38%

Item Type:	Thesis (Other)
Additional Information:	RSKe 671.52 Far a-1
Uncontrolled Keywords:	GMAW,Gas Pelindung, dan Debit Gas Pelindung
Subjects:	T Technology > TN Mining engineering. Metallurgy > TN879.6 Welding
Divisions:	Faculty of Marine Technology (MARTECH) > Ocean Engineering > 38201-(S1) Undergraduate Thesis
Depositing User:	Hanif Farhan
Date Deposited:	20 Jun 2024 09:08
Last Modified:	14 Apr 2026 03:37
URI:	http://repository.its.ac.id/id/eprint/73856