Pembentukan Komposit ZSM5(Hirarki)-Tio-C: Pengaruh Laju Pemanasan Terhadap Celah Pita

Lestari, Devi (2020) Pembentukan Komposit ZSM5(Hirarki)-Tio-C: Pengaruh Laju Pemanasan Terhadap Celah Pita. Masters thesis, Institut Teknologi Sepuluh Nopember.

Text 01221750012009-Master_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (3MB) | Request a copy

Abstract

Laju pemanasan pada pembuatan komposit ZSM-5(Hirarki)-TiO
2-C dari campuran gel TTIP-isopropanol-ZSM-5 dapat menekan penguapan pelarut dan terjadi pirolisis. Proses tersebut akan menaikan kadar karbon dalam komposit dan menurunkan celah pita. Pembuatan komposit dilakukan dengen metode sol-gel menggunakan pelarut isopropanol dengan precursor TTIP pada media ZSM-5 pada atmosferik nitrogen. Gel yang didapat dikalsinasi pada 550°C dalam atmosfer nitrogen dengan laju pemanasan 50, 100 dan 250 °C/menitdiperoleh ZSM-5-TiO2-C. Padatan hasil pembuatan dikarakterisasi menggunakan analisis XRD, FTIR, SEM-EDX, TGA, DRS dan Fisisorpsi N2 serta uji katalis fotokatalis pada pewarna reactive yellow. Hasil karakterisasi menunjukan bahwa komposit memiliki kandungan TiO2 12% dan karbon 10% pada laju pemanasan 250. TiO2 dan karbon tampak terlapis pada ZSM-5. Komposit dengan laju pemanasan 50 didapat celah pita 3,25 eV, komposit dengan laju penasan 100 didapat celah pita 3,12 eV dan komposit dengan laju pemanasan 250 didapat celah pita 2,55 eV. Uji fotokatalis dengan aktivitas fotokatalitik pada reactive yellow dengan penghilangannya sebesar 72,23% pada ZTC-250.
====================================================================================================================================
The making of a mixture of ZSM-5 (Hierarchy) -TiO2-C from a mixture of TTIP-isopropanol-ZSM-5 gel aims to reduce the evaporation of isopropanol and TTIP is further hydrolyzed. This process will increase the carbon content in the composite and reduce the band gap. Composites were made using a sol-gel method using isopropanol solvent with TTIP precursors on ZSM-5 media on atmospheric nitrogen. The obtained gel was calcined at 550 °C in atmospheric nitrogen with increased gains of 50, 100 and 250 °C/min obtained by ZSM-5-TiO2-C. The resulting solids were characterized using XRD, FTIR, SEM-EDX, TGA, DRS and N2 analysis as well as photocatalyst catalyst tests on yellow reactive dyes. The characterization results show that the composition has 12% TiO2 content and 10% carbon at 250 heating speeds. TiO2 and carbon appear to be coated on ZSM-5. Composites with an increase rate of 50 obtained a band gap of 3.25 eV, composites with an increase rate of 100 obtained a band gap of 3.12 eV and composites with an increase rate of 250 obtained a band gap of 2.55 eV. Photocatalyst test with photocatalytic activity on yellow reactive with 72.23% removal on ZTC-250.

Item Type:	Thesis (Masters)
Additional Information:	RTKi 620.118 Les p-1 2020
Uncontrolled Keywords:	Komposit ZSM-5-TiO2-C; Laju Pemanasan; Pegeseran Celah Pita
Subjects:	Q Science > QD Chemistry > QD501 Catalysis. Catalysts.
Divisions:	Faculty of Mathematics and Science > Chemistry > 47101-(S2) Master Thesis
Depositing User:	Devi Lestari
Date Deposited:	11 Dec 2025 08:10
Last Modified:	12 Dec 2025 06:49
URI:	http://repository.its.ac.id/id/eprint/74541

Actions (login required)

View Item