Pengaruh Serat Kaca Kontinu Terhadap Kekuatan Tarik Dan Sifat Thermal Komposit Polyester/Serat Kaca

Syamsu, Lingga Nur (2015) Pengaruh Serat Kaca Kontinu Terhadap Kekuatan Tarik Dan Sifat Thermal Komposit Polyester/Serat Kaca. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
270910007-Undergraduate_Thesis.pdf - Accepted Version

Download (3MB) | Preview

Abstract

Unsaturated Polyester Resin merupakan termoset polimer yang banyak digunakan. Poliester memiliki ketahanan kimia, ketahanan korosi dan sifat mekanik yang tinggi. Komposit adalah gabungan dari dua material atau lebih yang memiliki ikatan secara mekanik dengan tujuan untuk membentuk material sesuai dengan yang diinginkan serta harganya yang rendah. Dalam material komposit serat, fungsi utama serat adalah sebagai penopang kekuatan dari komposit sehingga tinggi rendahnya kekuatan komposit sangat tergantung dari serat yang digunakan. Serat kaca adalah bahan yang ringan, kuat, dan sering digunakan dalam berbagai industri karena sifat mereka yang sangat baik. Dalam penelitian ini, dilakukan proses pembuatan komposit polyester/serat kaca kontinu dengan variasi fraksi berat serat kaca 0, 10, 20, 30, dan 40 wt %. Serat kaca yang digunakan memiliki diameter rata-rata ~11 μm dan jenis yang digunakan continuous roving. Metode pencampuran komposit poliester/serat kaca dilakukan dengan hand lay-up. Hasil uji FTIR menunjukkan adanya ikatan kimia antara polyester, katalis, dan serat kaca. Hasil pengujian tarik tertinggi pada terdapat pada komposisi 40% serat kaca sebesar 159,32 MPa. Penambahan serat kaca pada komposit dapat meningkatkan stabilitas thermal komposit. ================================================================================================== Unsaturated Polyester Resin is a thermosetting polymer that is widely used. Polyesters are having chemical resistance, corrosion resistance and high mechanical properties. Composite is a combination of two or more materials that have a mechanical bond with the aim to establish in accordance with the desired material and the price is low. In the fiber composite material, the main function is as a pillar of strength fiber composite so that the level of the composite strength is highly dependent on the fiber used. Glass fibers are a material that is light, strong, and are often used in various industries because of their excellent properties. In this study, the process of making a composite polyester / continuous glass fiber with a variation of the weight fraction of glass fibers 0, 10 ,20, 30, and 40 wt%. Glass fibers used have an average diameter of ~11 μm and the type used continuous roving. A method of mixing the composite polyester / glass fiber made by hand lay-up. The FTIR test result indicates a chemical bond between the polyester, catalyst, and glass fiber. The highest tensile test results on the composition contained 40% glass fibers at 159.32 MPa. The addition of the glass fibers in the composite can enhance the thermal stability of the composite.

Item Type: Thesis (Undergraduate)
Additional Information: RSMt 620.118 Sya p
Uncontrolled Keywords: polyester, serat kaca kontinu, hand lay-up, kekuatan tarik, sifat thermal
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA418.9 Composite materials. Laminated materials.
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: Yeni Anita Gonti
Date Deposited: 13 Feb 2020 06:35
Last Modified: 13 Feb 2020 06:35
URI: http://repository.its.ac.id/id/eprint/74881