Analisa Pengaruh Variasi Heat Input Dan Temperatur PWHT Terhadap Struktur Mikro Dan Sifat Mekanik Pada Baja Paduan Rendah Dengan Proses Pengelasan SMAW

Ismail, Andhanu Surya (2015) Analisa Pengaruh Variasi Heat Input Dan Temperatur PWHT Terhadap Struktur Mikro Dan Sifat Mekanik Pada Baja Paduan Rendah Dengan Proses Pengelasan SMAW. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
2711100137-Undergraduate_Thesis.pdf - Accepted Version

Download (3MB) | Preview

Abstract

SA 516 Grade 70 adalah material yang digunakan dalam industri bolier (baja bertekanan). Dalam pengelasan SA 516 Grade 70 diperlukan perhatian yang khusus agar hasil pengelasan sesuai dengan yang diinginkan dan tidak terjadi cacat dalam pengelasan. Penelitian kali ini telah dilakukan pengelasan dengan variasi heat input dan temperatur PWHT untuk mengetahui pengaruhnya terhadap strukturmikro dan sifat mekanik. Besar heat input dalam penelitian ini dilakukan dengan penggunaan besar arus 80A dan 140A. Sedangkan temperatur PWHT yang digunakan adalah 450oC dan 600oC. Metode yang digunakan dalam penelitian ini adalah sample telah dilas dengan variasi heat input 80A dan 140A, setelah itu dilanjutkan dengan perlakuan postheat dengan tempertur 450oC dan 600oC. Selanjutnya telah dilakukan pengujian struktur mikro, uji tarik dan kekerasan untuk mengetahui kualitas sambungan. Pada hasil pengamatan strukturmikro terbentuk struktur accicular ferit pada HAZ sample A.1. Acciculr ferit terbentuk dari fasa austenit yang mengalami pendinginan cepat sehingga membentuk ferit dengan bentuk yang tajam. Sample B.1 viii mengalami degradasi struktur accicular ferit diakibatkan karena waktu pendinginan yang sedikit melambat didaerah HAZ. Selanjutnya dari hasil uji kekerasan sample yang tidak diberi perlakuan pwht memiliki nilai kekerasan paling rendah karena struktur accicular ferit mengakibatkan nilai kekerasn didaerah HAZ sample menurun. Dan dari hasil uji tarik diketahui bahwa sample yang tidak diberi perlakuan pwht memiliki nilai kekuatan tarik dan yield paling besar. Besar kekuatan tarik dan yield adalah 563 Mpa dan 387 Mp untuk sample yang dilas dengan heat input 80A sedangkan 541 Mpa dan 375 Mpa untuk sample yang dilas dengan heat input 140A. ================================================================================================ SA 516 Grade 70 is material that is used in the bolier industry (pressure vessel). In the welding process of SA 516 Grade 70 is required particular attention to get the result that is accordance with the desired and to avoid defects in welding process. In this study, the welding process has done. This welding used heat input variation and PWHT temperature to recognize its impact to structuremicro and mechanical properties. The amount of heat input in this study used the current of 80A and 140A. Whereas the PHWT temperature that is used are 450oC and 600oC. The method that is used in this study is samples have been welded with the variation of heat input 80A and 140A, after that followed with the postheat treatment with the temperatures of 450oC and 600oC. Afterwards the testing of microstructure, tensile and hardness testing have done. These testings are used to discover the connection quality. In the result of microstructure observation, there formed accicular ferrite structure on HAZ sample A.1. Accicular ferrite is formed by austenite which is undergoing a process x of rapid cooling, thus this process is forming ferrite with a sharp shape. Sample B.1 accicular ferrite degradation structure is occured. This is happened because of the cooling time is a little slow in the area of HAZ. Subsequently from the hardness testing, sample A.1 and B.1 have the lowest hardness value, it is because accicular ferrite structure makes the hardness value in the area of HAZ sample is declining. And from the tensile testing, is known that the sample which is not get pwht have the biggest tensile strength values and the biggest yield. The values of tensile strength and yield are 563 Mpa and 387 Mpa for sample in 80A heat, while 541 Mpa and 375 Mpa for sample in 140 heat.

Item Type: Thesis (Undergraduate)
Additional Information: RSMt 671.521 2 Ism a
Uncontrolled Keywords: SMAW, SA 516 Grade 70, Input Panas, Temperatur pwht, Accicular ferit
Subjects: T Technology > TN Mining engineering. Metallurgy > TN879.6 Welding
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis