Pengaruh Variasi Tekanan Dan Temperatur Warm Compaction Terhadap Sifat Mekanik Komposit Cu-10%Sn Dengan 0,7% Zinc Stearate Sebagai Material Peluru Frangible.

Putra, Arief Handi (2016) Pengaruh Variasi Tekanan Dan Temperatur Warm Compaction Terhadap Sifat Mekanik Komposit Cu-10%Sn Dengan 0,7% Zinc Stearate Sebagai Material Peluru Frangible. Undergraduate thesis, Institut Technology Sepuluh Nopember.

[thumbnail of 2712100051- Undergraduate-Thesis.pdf]
Preview
Text
2712100051- Undergraduate-Thesis.pdf - Accepted Version

Download (4MB) | Preview

Abstract

Peluru frangible adalah peluru latih yang didesain untuk
hancur ketika mengenai benda keras. Peluru frangible banyak
diproduksi menggunakan metode cold compaction. Penelitian ini
mengembangkan warm compaction untuk mempersingkat waktu
produksi dibanding metode cold compaction. Proses warm
compaction telah dilakukan dengan variasi tekanan 300, 400, 500
dan 600 MPa serta variasi temperatur kompaksi 100oC dan 200oC.
Dari hasil penelitian diperoleh bahwa proses pembuatan komposit
dengan metalurgi serbuk pada kedua temperatur menghasilkan
nilai densitas yang tertinggi pada tekanan 600 MPa dengan nilai
berturut – turut 8,26 g/cm3 dan 8,74 g/cm3. Dari hasil pengujian
sifat mekanik didapatkan nilai kekerasan maksimum pada tekanan
600 MPa temperatur 200oC yaitu 100,88 HV dan kekuatan tekan
didapatkan nilai maksimum 469,47 MPa pada tekanan 600 MPa
temperatur 200oC. Hasil karakterisasi menggunakan XRD dan
SEM menunjukan bahwa metode yang digunakan dalam
pembuatan komposit Cu-10%Sn ini mampu menghasilkan
senyawa Cu3Sn dan Cu6Sn5.
===========================================================================================================
Frangible projectile is a projectile designed to shattered as stroke
a hard target. Frangible projectile fabricated using cold
compaction method. This study observe warm compaction method
to reduce production time compared from cold compaction
method. Synthesis of material Cu-10%Sn composite by warm
compaction has been observed with the variation of pressure
(300, 400, 500 and 600 MPa) and temperature (100 and 200 oC).
Form the result of experiment we found that Both of the
temperature produce the density value, with the highest at 600
MPa, there are 8,26 g/cm3 and 8,74 g/cm3. From the mechanical
testing of the composite, the maximum hardness is 100,88 HV at
600 MPa, 200 oC, and the maximum compressive strength is
469,47 MPa at 600 MPa, 200 oC. From the characterization by
XRD and SEM, show that the method which used in syntesis of
Cu-10%Sn composite can produce Cu3Sn dan Cu6Sn5
intermetallic compound

Item Type: Thesis (Undergraduate)
Additional Information: RSMt 671.37 Put p
Uncontrolled Keywords: frangible, metalurgi serbuk, Cu-Sn, temperatur kompaksi
Subjects: T Technology > TS Manufactures > TS699 Powder coating of metals
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: Mr. Tondo Indra Nyata
Date Deposited: 17 Feb 2020 06:37
Last Modified: 17 Feb 2020 06:37
URI: http://repository.its.ac.id/id/eprint/74982

Actions (login required)

View Item View Item