Pengaruh Air Hujan Terhadap Karakteristik Dan Laju Korosi Pada Baja Aisi 1045 Dan Stainless Steel (SS) 304 Di Lingkungan Sungai

Widharesta, Haci (2012) Pengaruh Air Hujan Terhadap Karakteristik Dan Laju Korosi Pada Baja Aisi 1045 Dan Stainless Steel (SS) 304 Di Lingkungan Sungai. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
2708100058-Undergraduate_Thesis.pdf - Accepted Version

Download (2MB) | Preview

Abstract

Baja dalam penggunaannya berada pada lingkungan terbuka dan tidak terhindar dari kontak dengan air di sekitarnya, misalnya air hujan dan air sungai. Air hujan dan air sungai mengandung unsur-unsur kimia yang bersifat korosif sehingga dapat mengkorosikan logam. Kandungan korosif yang terdapat pada kedua air tersebut merupakan akibat dari polutan yang berasal dari limbah industri, limbah rumah tangga, juga gas hasil bungan industri maupun kendaraan bermotor yang terbawa udara. Dalam penelitian ini baja AISI 1045 dan Stainless Steel 304 diuji dengan metode weight loss dan metode elektrokimia potensiostat. Pengujiann korosi dengan metode weight loss dilaksanakan di lapangan dengan medium air hujan selama 90 hari. Sedangkan metode elektrokimia potensiostat dilaksanakan di laboratorium dengan medium campuran air hujan dan air sungai. Berdasarkan pengujian korosi dengan metode weight loss, diperoleh hasil laju korosi untuk spesimen AISI 1045 sebesar 9,821 mpy dan untuk spesimen stainless steel 304 sebesar 0,034 mpy. Sedangkan hasil pengujian elektrokimia potensiostat, pada spesimen AISI 1045 diperoleh laju korosi terbesar pada konsentrasi 75% air hujan terhadap air sungai, yaitu sebesar 2,948 mpy. Dan pada spesimen stainless steel 304, laju korosi terbesar pada konsentrasi 25% air hujan terhadap air sungai, yaitu sebesar 1,734 mpy. Berdasarkan pengujian elektrokimia potensiostat dengan berbagai konsentrasi, air sungai bersifat lebih korosif dibanding dengan air hujan. Setelah dilakukan pengujian SEM dan XRD pada spesimen yang mengalami uji imersi selama 90 hari, pada spesimen AISI 1045 terdapat produk korosi berupa Fe3O4 dengan morfologi berpori. Sedangkan pada stainless steel 304 tidak tampak adanya produk korosi karena nilai laju korosi yang dialami stainless steel sangat kecil. ======================================================================================================================== Steel is used on open environment and not spared of water contact around, such as rain and river water. They contain of corrosive chemical substance so can corrode metal. Corrosive content on them is a result of industrial, household waste pollutant and either industrial flue gas or motor vehicles. In this study AISI 1045 steel and stainless steel 304 were examined by weight loss method and potensiostat electrochemical method. Weight loss has done on rain water medium for 90 days. Potensiostat electrochemical method done at laboratory with rain and river water medium. Based on corrosion examination with weight loss method, corrosion rate for AISI 1045 was 9.821 mpy and for stainless steel 304 was 0.34 mpy. While the highest corrotion rate of potensiostat electrochemical examination result for AISI 1045 is 75% rain to river water, 2.948 mpy. And for stainless steel 304, the highest corrotion rate happened on 25% rain to river water, 1.734 mpy. Hence based on potensiostat electrochemical with various concentration, river water is more corrosive than rain water. After SEM and XRD examination on immersion test AISI 1045 for 90 days, it was found that corrosion product Fe3O4 with porous. While on 304 stainless steel wasn’t found corrotion product because corrosion rate for stainless steel was very low.

Item Type: Thesis (Undergraduate)
Additional Information: RSMt 620.112 23 Wid p
Uncontrolled Keywords: Air hujan, Korosi, Weight loss, Potensiostat
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA418.74 Corrosion and anti-corrosives
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis