Analisa Penyebab Dan Pencegahan Keausan Guide Vane Coal Mill Pabrik Tuban 4 (Studi Kasus PT. Semen Gresik Tuban, Jawa Timur)

Anhar, Muhammad Irvan (2015) Analisa Penyebab Dan Pencegahan Keausan Guide Vane Coal Mill Pabrik Tuban 4 (Studi Kasus PT. Semen Gresik Tuban, Jawa Timur). Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
2110100029-Undergraduate_Thesis.pdf - Accepted Version

Download (5MB) | Preview

Abstract

Coal mill merupakan salah satu equipment pada pabrik semen yang digunakan untuk menghaluskan batubara hingga berbentuk powder sebagai bahan bakar rotary kiln untuk menghasilkan clinker. Salah satu komponen yang menyusun coal mill adalah guide vane yang merupakan dynamic classifier dan selalu mengalami keausan sebelum dilakukan overhaul. Keausan pada guide vane coal mill ini dapat mengganggu kerja rotary kiln sehingga mengganggu kinerja produksi. Dalam penelitian tugas akhir ini telah dianalisa penyebab keausan dengan metode Root Cause Failure Analysis (RCFA) yang digunakan untuk mencari penyebab terjadinya kerusakan, sehingga solusi untuk pencegahannya dapat dilakukan. Dilakukan pengujian komposisi kimia (Optical Emission Spectroscopy) dan pengujian struktur mikro (Metalography Test) terhadap material guide vane untuk mengetahui jenis material, sedangkan pengujian kekerasan dan pengujian impact dilakukan untuk mengetahui sifat mekanik material guide vane. Dari hasil analisa-analisa tersebut didapatkan jenis material guide vane tergolong material Fe-Cr-C overlay sebagai layer hardfacing dan mild steel AISI 1023 sebagai base plate. Material Fe-Cr-C overlay memiliki sifat mekanik dengan kekerasan yang tinggi, ketangguhan yang rendah, dan sangat getas dibandingkan mild steel AISI 1023 yang memiliki sifat mekanik dengan kekerasan rendah namun ketangguhannya tinggi dan ulet. Berdasarkan hal tersebut material guide vane tidak cukup tangguh untuk menerima beban berulang yang disebabkan oleh tumbukkan butiran batubara, sehingga terjadi fatigue wear. ================================================================================================== Coal mill is the equipment to be used to grind coal into powder as fuel of rotary kiln burner in order to produce clinker in cement factory. Guide vane is components of dynamic classifier inside coal mill that always wear rapidly before overhaul period. These failure might affect and disrupt the production performance of rotary kiln. This research has analyzed the cause of the wear using Root Cause Failure Analysis (RCFA) method to find the cause of failure so that the solution could be proposed to prevent it. Guide vane material was tested using chemical composition test (Optical Emission Spectroscopy) and microstructure test (Metallography Test) to determine the type of material, while the hardness test and impact test was conducted to determine the mechanical properties of the material. Test result reveals that the guide vane consists of a layer hard material classified as Fe-Cr-C overlay and mild steel AISI 1023 as the base plate. Fe-Cr-C overlay material has mechanical properties of high hardness, low toughness, and very brittle. Based on this, guide vane’s material is not tough enough to receive cyclic loads occur from coal granulates impact that lead to fatigue wear.

Item Type: Thesis (Undergraduate)
Additional Information: RSM 620.004 6 Anh a
Uncontrolled Keywords: Coal Mill, Guide Vane, Keausan
Subjects: T Technology > TH Building construction > TH3351 Maintenance and repair
Divisions: Faculty of Industrial Technology > Mechanical Engineering > 21201-(S1) Undergraduate Thesis
Depositing User: Yeni Anita Gonti
Date Deposited: 02 Mar 2020 02:50
Last Modified: 02 Mar 2020 02:50
URI: http://repository.its.ac.id/id/eprint/75249

Actions (login required)

View Item View Item