Pemilihan Parameter Untuk Meningkatkan Kekuatan Spesimen Tarik Dan Impact Pada Proses Injeksi Plastik Dengan Metode Taguchi

Prihananto, Dhian (2015) Pemilihan Parameter Untuk Meningkatkan Kekuatan Spesimen Tarik Dan Impact Pada Proses Injeksi Plastik Dengan Metode Taguchi. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 2110100093-Undergraduate_Thesis.pdf]
Preview
Text
2110100093-Undergraduate_Thesis.pdf - Accepted Version

Download (4MB) | Preview

Abstract

Kebutuhan dan ketergantungan manusia akan plastik
dewasa ini sangat besar dan bahan ini menjadi tidak tergantikan
oleh material lain. Hal ini dikarenakan produk plastik mudah
didapat, mudah dibawa kemana-mana dan mudah dibentuk sesuai
keinginan. Seiring berjalannya waktu, kualitas plastik dari setiap
perusahaan pun dipertanyakan. Apakah proses produksi plastik
tersebut telah menghasilkan plastik dengan kualitas yang baik atau
tidak. Hal ini berkaitan dengan baik material plastik ataupun proses
produksinya. Salah satu proses produksi yang menggunakan bahan
baku plastik tersebut adalah injeksi plastik (injection Molding).
Pada tugas akhir ini dilakukan optimasi kekuatan tarik dan
impact pada proses injeksi di mesin injection molding HAITIAN MA
900/260e dengan mengubah parameter-parameter proses yang ada
pada mesin injeksi plastik tersebut Untuk mencari altenatif material
plastik yang dapat menghasilkan produk yang memiliki kualitas
yang optimal berdasarkan kekuatan tarik dan impact sebagai
batasannya. Penyelesaian tugas akhir ini memanfaatkan metode
Taguchi dan logika Fuzzy. Parameter proses injeksi plastik yang
dipilih adalah waktu tahan, waktu pedinginan dan temperatur.
Setiap parameter memiliki tiga level, yaitu untuk temperatur 2200C,
2250C, 2300C, untuk waktu tahan 5 , 10 dan 15 detik, dan untuk
waktu pendinginan 10 , 15 dan 20 detik.
Hasil yang didapat dari penelitian ini adalah kombinasi
parameter yang dapat menaksimalkan kekuatan spesimen tarik dan
impact secara serentak adalah temperatur nozzle sebesar 2250C,
waktu tahan sebesar 15 detik dan waktu pendinginan sebesar 20
detik. Waktu tahan tidak berpengaruh secara signifikan pada
multirespon dikarenakan nilai Fhitung-nya lebih kecil dari nilai Ftabel
pada tabel distribusi F. Persentase peningkatan kekuatan tarik dan
impact secara serentak yang didapatkan dari eksperimen dengan
metode Taguchi dan logika Fuzzy sebesar 40,34%.
=================================================================================================
Human needs and dependency for plastic nowadays is
huge.This material is not replaceable by other materials. Because it
is easy to get, easy to carry everywhere and easily to be formed.
Over time, the plastic quality of any company ever questioned.
Whether the plastic production process has produced plastic with
good quality or not. This relates to both plastic materials or the
production process. One of the production processes that uses
plastic raw materials is plastic injection (injection Molding).
To find alternative of plastic material which can produce
optimal quality products such as high tensile strength and impact in
this study optimization of tensile strength and impact on the process
of injection in the injection molding machine type HAITIAN MA
900/260e was performed by changing the process parameters in
injection Molding machine. The completion of this final project
applied method of Taguchi and Fuzzy logic. Plastic injection process
parameters such as holding time, cooling time and temperature are
chosen. Each parameter has three levels, i.e. temperature level were
2200C, 2250C, 2300C, holding time level were 5, 10 and 15
seconds, and the cooling time levels were 10, 15 and 20 seconds.
The results obtained from this study was the combination of
parameters that could be maximize tensile and impact strength of
specimen simultaneously i.e. the 2250C of temperature of the nozzle,
15 seconds of holding time and 20 seconds of cooling time .
holding time was no effect on the multirespon significantly due to its
Fhitung value is smaller than the value of Ftabel distribution in Table F.
The percentage of the increase in tensile strength and impact
strength simultaneously obtained from experiments using Taguchi
method and Fuzzy logic was 40,34 %.

Item Type: Thesis (Undergraduate)
Additional Information: RSM 668.412 Pri p
Uncontrolled Keywords: plastik, parameter proses injeksi, optimasi, Taguchi, logika Fuzzy, Tegangan Tarik dan Impact
Subjects: T Technology > TJ Mechanical engineering and machinery
Divisions: Faculty of Industrial Technology > Mechanical Engineering > 21201-(S1) Undergraduate Thesis
Depositing User: Yeni Anita Gonti
Date Deposited: 02 Mar 2020 04:08
Last Modified: 02 Mar 2020 04:08
URI: http://repository.its.ac.id/id/eprint/75252

Actions (login required)

View Item View Item