Pengaruh Komposisi TiO2 Terhadap Kemampuan Self Cleaning pada Kaca dengan Dispersant Polietilen Glikol (PEG) 4000

Akbar, Dahry Yuniar (2015) Pengaruh Komposisi TiO2 Terhadap Kemampuan Self Cleaning pada Kaca dengan Dispersant Polietilen Glikol (PEG) 4000. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
2411100107-Undergraduate_Thesis.pdf - Accepted Version

Download (4MB) | Preview

Abstract

Salah satu teknologi yang sedang dikembangkan untuk aplikasi self cleaning adalah dengan memanfaatkan fotokatalisis bahan TiO2 dimana fotokatalisis merupakan proses reaksi kimia yang dibantu oleh energi sinar ultraviolet. Efek fotokatalisis inilah yang dapat mendekomposisi pengotor berupa senyawa organik. TiO2 disintesis dengan menggunakan bahan dasar TiCl3. Hasil sintesis kemudian dicuci menggunakan aquades lalu dikalsinasi menggunakan furnace dengan suhu 300○C selama 4 jam untuk mendapatkan TiO2 struktur anatase. Larutan TiO2 yang dilapiskan pada sampel kaca dibuat dengan mencampurkan PEG 4000, kloroform, dan serbuk TiO2. Komposisi TiO2 dibuat bervariasi, yaitu 0 gram, 1 gram, 1,5 gram, 2 gram, 2,5 gram, dan 3 gram, dengan PEG dan kloroform tetap untuk semua variasi komposisi TiO2. Pelapisan dilakukan dengan teknik doctor blade. Pengujian self cleaning menggunakan dua jenis pengotor yaitu lumpur dan pewarna. Pengujian dilakukan dengan dua cara yaitu pengujian sifat hidrofilik dan pengujian sifat fotokatalisis. Hasil pengujian menunjukkan sifat self cleaning terbaik didapatkan pada sampel dengan komposisi TiO2 sebesar 3 gram dengan kemampuan menghilangkan pengotor hingga 96% pada penjemuran di bawah sinar matahari dan 74% pada penyinaran UV, serta memiliki selisih transmitansi hingga 58,8%. Sedangkan hasil pengujian sifat hidrofilik menunjukkan bahwa sifat hidrofilik sangat dipengaruhi oleh fotokatalisis. Adapun ketidaksamaan sifat hidrofilik sampel disebabkan oleh adanya penggumpalan serbuk TiO2 di permukaan lapisan. ==================================================================================================== One of the technologies that are being developed for selfcleaning applications is to utilize TiO2 photocatalytic material through a photocatalytic chemical reaction process assisted by the energy of ultraviolet rays. Photocatalytic effect decomposes the impurities in the form of organic compounds. TiO2 synthesized by using precursor of TiCl3. The synthesis uncorporates ammonia washing and calcination at 300○C for 4 hours to obtain TiO2 anatase. TiO2 solution was coated on the glass sample in the form of paste made by mixing PEG 4000, chloroform, and TiO2 powder. TiO2 composition was varied, i.e. 0 gram, 1 gram, 1.5 gram, 2 grams, 2.5 grams and 3 grams, while PEG and chloroform amounts fixed for all variations studied. Coatings were was under taken by the doctor blade technique. Self cleaning testing was using two types of impurities, namely mud and dyes. The test was done in two ways, namely hydrophilic and photocatalytic properties tests. The results showed that the best self-cleaning properties was obtained on the sample with a composition of TiO2 of 3 grams with the ability to eliminate impurities up to 96% under direct sun and 74% in UV radiation. It has a transmittance difference of up to 58.8% . The hydrophilic properties depend on photocatalytics. However, due to profuse agglomeration of TiO2 the hydrophilic properties decreases.

Item Type: Thesis (Undergraduate)
Additional Information: RSF 667.9 Akb p
Uncontrolled Keywords: anatase, PEG, self cleaning, TiO2
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA418.9.C57 Coatings
Divisions: Faculty of Industrial Technology > Physics Engineering > 30201-(S1) Undergraduate Thesis