Pembuatan komposit Gipsum Orthophedic Cast dari Limbah Organik ( Cangkang Kerang ) : Efek rasio air-serbuk dan serat-serbuk

Chasanah, Humairoh Nur (2015) Pembuatan komposit Gipsum Orthophedic Cast dari Limbah Organik ( Cangkang Kerang ) : Efek rasio air-serbuk dan serat-serbuk. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
2711100034-Undergraduate_Thesis.pdf - Accepted Version

Download (6MB) | Preview

Abstract

Cangkang kerang merupakan salah satu sumber kalsium (Ca) dengan kadar 34 – 46 % yang dapat diaplikasikan di bidang medis. Dengan melimpahnya limbah cangkang kerang di Indonesia sebagai Negara perairan, maka limbah cangkang kerang berpotensi untuk dimanfaatkan kandungan kalsium di dalamnya sebagai bahan baku produk gipsum komposit orthopedic cast menggunakan metode gelombang mikro dengan variasi daya, waktu dan massa. Hasil gypsum anhidrate yang dihasilkan di pergunakan dalam pembuatan produk gypsum cast berdasarkan hasil analisa kandungan gugus fungsi (SO42-). Penelitian ini bertujuan untuk menganalisa pengaruh rasio komposisi serbuk gipsum anhidrat dan serat bambu, serta air dan serbuk gipsum anhidrat terhadap sifat mekanik dan biologi pada proses iritasi pada kulit pasien pasca pemakain komposit gipsum cast. Dari beberapa parameter yang ada, didapatkan rasio serbuk 61: air 39: serat 0,25% serta rasio serbuk 63: air 37: serat 0,25% yang berpotensi untuk bisa diaplikasikan dibidang medis sebagai komposit gipsum cast.pembuatan produk gypsum cast. Gipsum anhidrat dihasilkan dari radiasi gelombang mikro daya 540 watt, 75 menit, massa 50 gram. Rasio serbuk, air serta serat memiliki efek yang signifikan pada kekuatan mekanik dan biologi. Water absorption paling baik adalah pada rasio serbuk 63: air 37: serat 0,25% dan serbuk 65: air 35: serat 0,5%. Untuk hasil kuat tekan terbaik adalah rasio serbuk 61: air 39 untuk serat 1% dan 0,25%. Serta serbuk 63: air 37: serat 0,25% . U ntuk uji iritasi tidak ada efek iritasi pada kulit pasien pasca pemakain komposit gipsum cast. Dari beberapa parameter yang ada, didapatkan rasio serbuk 61: air 39: serat 0,25% serta rasio serbuk 63: air 37: serat 0,25% yang berpotensi untuk bisa diaplikasikan dibidang medis sebagai komposit gipsum cast. ===================================================================================================== Sea shell is one of calcium (Ca) source with content of calcium 34-46% which can be applied in the medical field. With the abundance of waste sea shell in Indonesia as a country waters, the sea shell waste potentially useful calcium content it as a raw material composite orthopedic cast gypsum products using microwaves with variation of power, time and mass. Results anhidrate gypsum produced can use in the manufacture of cast gypsum products based on the analysis of the content from the functional group (SO4 2-). This study aimed to analyze the influence of the composition ratio of anhydrous gypsum powder and bamboo fiber, as well as water and gypsum powder anhydrous against mechanical and biological properties of the cast gypsum product manufacturing process. Anhydrous gypsum generated of microwave radiation power of 540 watts, 75 minutes, 50 g ram mass. Ratio powder, water and fiber have a significant effect on the mechanical strength and biology. Water absorption is the most excellent in powder ratio of 63: Water 37: 0.25% fiber and powder 65: Water 35: fiber 0.5%. For best results the compressive strength is the ratio of the powder 61: water 39 to the fiber 1% and 0.25%. As well as the powder 63: Water 37: fiber 0.25%. To test the irritation no i rritating effect on t he patient's skin after usage of the composite gypsum cast. From some of the parameters, obtained powder ratio 61: Water 39: 0.25% fiber and powder ratio 63: water 37: fiber 0,25% that potentially can be applied to the medical field as a composite gypsum cast.

Item Type: Thesis (Undergraduate)
Additional Information: RSMt 553.635 Cha p
Uncontrolled Keywords: cangkang kerang, gelombang mikro, gipsum anhidrat, gipsum komposit orthopedic cast, serat bambu.
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA418.9 Composite materials. Laminated materials.
T Technology > TP Chemical technology
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: Yeni Anita Gonti
Date Deposited: 26 Mar 2020 03:28
Last Modified: 26 Mar 2020 04:05
URI: http://repository.its.ac.id/id/eprint/75552

Actions (login required)

View Item View Item